Abstract
Mg2SiO4:Sm3+ (1–11mol%) nanoparticles were prepared by a rapid low temperature solution combustion route. The powder X-ray diffraction (PXRD) patterns exhibit orthorhombic structure with α-phase. The average crystallite size estimated using Scherer’s method, W–H plot and strain–size plots were found to be in the range 25–50nm and the same was confirmed by Transmission Electron Microscopy (TEM). Scanning electron microscopy (SEM) pictures show porous structure and crystallites were agglomerated. The effect of Sm3+ cations on luminescence of Mg2SiO4 was well studied. Interestingly the samples could be effectively excited with 315nm and emitted light in the red region, which was suitable for the demands of high efficiency WLEDs. The emission spectra consists of four main peaks which can be assigned to the intra 4-f orbital transitions of Sm3+ ions 4G5/2→6H5/2 (576nm), 4G5/2→6H7/2 (611nm), 4G5/2→6H9/2 (656nm) and 4G5/2→6H11/2 (713nm). The optimal luminescence intensity was obtained for 5mol% Sm3+ ions. The CIE (Commission International de I’Eclairage) chromaticity co-ordinates were calculated from emission spectra, the values (0.588, 0.386) were close to the NTSC (National Television Standard Committee) standard value of red emission. Coordinated color temperature (CCT) was found to be 1756K. Therefore optimized Mg2SiO4:Sm3+ (5mol%) phosphor was quite useful for solid state lighting.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.