Abstract
The (1 1 2) surfaces of Bridgman-grown p- and n-type CuInSe2 single crystals were prepared using different polishing, etching and annealing regimes. The surfaces were subsequently studied using Rutherford backscattering-channelling (2 MeV He+ ions) and Raman techniques. A layer of damage below the polished surface was produced after polishing with 3 Μm and 1 Μm diamond pastes and fine 0.05 Μm alumina slurry. The thickness of the damaged layer depends on the polishing grade and was found to be 30 nm after 0.05 Μm grade polishing. Subsequent etching in a 1% Br-methanol solution removed the damaged layer after 30s. However, the etching process produced what appeared to be an Se excess in a layer close to the surface. This excess can be dissipated by annealing; also, heat treatment of unetched samples at 400 ‡C was found to repair polish-induced damage.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.