Abstract
A preliminary study of deformation behavior of friction stir welded (FSW) Ti-6Al-4V was performed using two different tools with cylindrical and stepped spiral pin design for the welding process. The nugget regions experienced temperature above β transus and the matrix transformed to fine acicular α during cooling of the nugget. By using stepped spiral pin design, a local region with much refined grain structure and significant tool debris particles were observed. Room temperature tensile test showed increased strength and decreased ductility in the material from this region. Fractographic analysis revealed that tool debris particles served as void nucleation sites. Tensile tests of FSW material were carried out at 625 °C in the strain rates of 3 × 10−4 and 1 × 10−3 s−1. The strength was higher as compared to the as-received material. Microstructural evolution during tensile test was also investigated. Results showed that dynamic globularization occurred during the high temperature tensile test.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.