Abstract
This work addresses a two-parameter description of crack-tip fields in bend and tensile fracture specimens incorporating the evolution of near-tip stresses following stable crack growth with increased values of the crack driving force as characterized by J. The primary objective of this study is twofold. First, the present investigation broadens current understanding on the role of constraint and test conditions in defect assessment procedures for pipeline girth welds using SE(T) and SE(B) specimens. Second, the work addresses the potential coupled effects of geometry and ductile tearing on crack-tip constraint as characterized by the J−Q theory which enables more accurate correlations of crack growth resistance behavior in conventional fracture specimens. Plane-strain and 3-D finite element computations including stationary and growth analyses are conducted for 3P SE(B) and clamped SE(T) specimens having different notch depth (a) to specimen width (W) ratio in the range 0.1 ≤ a/W ≤ 0.5. Additional 3-D finite element analyses are also performed for circumferentially cracked pipes with a surface flaw having different crack depth (a) over pipe wall thickness (t) ratios and fixed crack length. A computational cell methodology to model Mode I crack extension in ductile materials is utilized to describe the evolution of J with the accompanying evolving near-tip opening stresses. Laboratory testing of an API 5L X70 steel at room temperature using standard, deeply cracked C(T) specimens is used to measure the crack growth resistance curve for the material and to calibrate the key cell parameter defined by the initial void fraction, f0. A key result emerging from this study is that shallow crack SE(B) specimens can accurately and conservately produce crack growth resistance curves that describe well the measuring toughness capacity of circumferentially cracked pipes under remote bending. The present results provide additional understanding of the effects of constraint on crack growth which contributes to further evaluation of crack growth resistance properties in pipeline steels using SE(T) and SE(B) specimens while, at the same time, eliminating some restrictions against the use of shallow cracked bend specimens in defect assessment procedures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Pressure Vessels and Piping
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.