Abstract
LixNi1/3Mn2/3O2 (x > 2/3) compounds have been synthesized from P3 type Na2/3Ni1/3Mn2/3O2 precursor through a new reduction-ion exchange method. The XRD patterns of LixNi1/3Mn2/3O2 show superlattice peak around 2θ = 20°, which is similar to that of the lithium-excess manganese based cathode materials. In contrast to sample obtained from traditional ion exchange method, the LixNi1/3Mn2/3O2 compound delivers LiNi1/2Mn1/2O2–Li2MnO3 solid solution type potential profiles and higher capacity than that of Li2/3Ni1/3Mn2/3O2, especially for the capacity delivered in high potential region. Moreover, it exhibits extremely small irreversible capacity at the initial cycle and small capacity loss during cycling in the voltage range 4.7–2.5 V. The structure and electrochemical properties of metallic elements substituted LixNi2/9M1/9Mn2/3O2 (M = Al, Co, Fe, Mg) were also studied. XRD and Raman spectra results suggest that small amount substitution of Ni with other metal ions does not affect the main structure of LixNi2/9M1/9Mn2/3O2 compounds. For Mg substituted compound, LixNi2/9Mg1/9Mn2/3O2, it exhibits improved cycleability compared with the other samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.