Abstract
A new quaternary Li0.19Al2.72O3.64N0.36 transparent ceramic with the Vickers hardness of 17.91 ± 0.2 GPa at a load of 9.8 N and the in-line transmittance of 83.4% at 3.5 µm was prepared by hot isostatic press sintering (HIP) after pressureless sintering. The 7Li and 27Al magic-angle spinning (MAS) NMR spectra combined with the XRD Rietveld refinement was adopted to analyze the crystal structure. It is revealed that all the lithium ions are located in octahedra and the cation vacancies are mainly concentrated in tetrahedra. Based on the bond valance models, the complicated relationship among composition, crystal structure and intrinsic hardness of the spinel-type transparent ceramic were disclosed. Compared with the γ-AlON, the higher hardness of Li0.19Al2.72O3.64N0.36 transparent ceramic is attributed to the coupling effect of enhanced hardness of bonds in octahedra and the slightly weakened hardness of bonds in tetrahedra.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.