Abstract
Manufactured graphite is a preferred material for in-core components of molten salt reactors and fluoride salt-cooled high-temperature reactors, which are in permanent contact with liquid salts. However, owing to the porous nature of nuclear graphite, under certain conditions, molten salts may intrude graphite's pores and affect graphite's properties and functionality. Therefore, a better understanding of molten salt intrusion (distribution across sample cross section and penetration depth) is needed to assess its effects. In this work, we have demonstrated the use of neutron imaging (computed tomography) in the evaluation of salt penetration and distribution of a wide range of graphite grades with diverse microstructures that have been subjected to FLiNaK (LiF–NaF–KF) intrusion at 750 °C and 5 bar pressure for 12 h. Because of the great neutron attenuation contrast from scattering and adsorption between Li (from FLiNaK) and the graphite matrix, we have obtained direct visualization of FLiNaK salt distribution in the salt-impregnated graphites for the first time. Three-dimensional reconstructed images and cross-sectional concentration profiles demonstrate that salt penetration and density distribution are greatly dependent on the microstructural properties of the graphite grade.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.