Abstract
An enormous attention has been paid to cobalt aluminate (CoAl2O4) blue pigments owing to their significant hue of blue colour. Nevertheless, several serious disadvantages, such as high cost due to the high cobalt consumption and poor solar reflectance, are associated with this pigment. Therefore, the development of cost effective and sustainable blue pigments with reduced Co content and improved solar reflectivity is a major focused area in pigment research. Herein, a new series of multifunctional blue coloured inorganic pigments with low cobalt content were prepared via the solid-state method. The structural and spectroscopic evaluations were indicated that the strong blue colour could be generated because of the distorted tetrahedrally organized cobalt chromophore. This structural distortion of the chromophore geometry was linked to the covalency and electron affinity factors. Colour (b* = −59.21) and solar reflectance (R* = 64%) measurements of the optimized composition (NaZn0.9Co0.1PO4) was observed to be superior than the commercially available CoAl2O4 blue pigment. Meanwhile, the optimized pigment loaded epoxy coated steel substrate in marine medium exhibited impressive corrosion resistance properties. The anticorrosive mechanism, further established through the XPS results, validated that the phosphatized inhibitive film served as the barrier for corrosion. The estimated Co content in NaZn0.9Co0.1PO4 was found to be around 10 times lower than the CoAl2O4 blue pigment indicating the cost-effective nature. The optimized pigment was able to retain its optical properties in the prepared acrylic coatings on Al sheet and concrete block. Further, the temperature shielding studies ensured a reduction of ~4 °C in comparison with CoAl2O4 coatings. Therefore, the developed multifunctional blue pigment could be employed for the economic production of blue exterior paint for anticorrosive cool roof coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.