Abstract

Conventional and nanocrystalline MCrAlY coatings were applied by the high-velocity oxy-fuel (HVOF) deposition process. The ball-milling method was used to prepare the nanocrystalline MCrAlY powder feedstock. The microstructure examinations of the conventional and nanocrystalline powders and coatings were performed using X-ray diffraction (XRD), high-resolution field emission scanning electron microscope (FESEM) equipped with energy-dispersive X-ray spectroscopy (EDX), transmission electron microscope (TEM), and X-ray photoelectron spectroscopy (XPS). Williamson–Hall analyzing method was also used for estimation of the crystalline size and lattice strain of the as-milled powders and sprayed coatings. Owing to the investigation of the oxidation behavior, the freestanding coatings were subjected to isothermal and cyclic oxidation testing at 1000 and 1100 °C under static air. The results showed that the conventional as-sprayed MCrAlY coating had a parabolic behavior in the early stage and prolonged oxidation process. On the contrary, in the case of the nanocrystalline MCrAlY coating, the long-term oxidation behavior has deviated from parabolic to sub-parabolic rate law. Moreover, the results also exemplified that the nanocrystalline MCrAlY coating had a greater oxidation resistance following the creation of a continuous and slow-growing Al2O3 scale with a fine-grained structure. The nucleation and growth mechanisms of the oxides formed on the nanocrystalline coating have also been discussed in detail.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call