Abstract
This work reports the synthesis of copper- and cobalt-based coupled and mixed metal oxides (CuO-Co3O4 and CuCo2O4, respectively) utilizing a simple hydrothermal and calcination approach. CuO-Co3O4, CuCo2O4, and the control samples were characterized by powder X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray, and X-ray photoelectron spectroscopy. TEM and FE-SEM analyses of CuO-Co3O4 reveal the presence of two distinct morphologies: rod- and sphere-shaped particles (CuO and Co3O4, respectively). Further, CuO-Co3O4 was efficiently utilized as an electrocatalyst for the selective oxidation of hydrazine (Hyz). CuO-Co3O4 shows a high redox response compared to CuO, Co3O4, CuCo2O4, and the physical mixture of CuO and Co3O4 (CuO/Co3O4). This enhanced performance is attributed to the synergistic interaction between the metal ions caused by their close proximity and the increased exposure of surface active sites. CuO-Co3O4 shows a broad linear range (1–3500 µM), a low detection limit (0.29 µM), and high sensitivity (0.5756 µA µM-1 cm-2) for the Hyz determination. Kinetic parameters, for instance the diffusion coefficient and catalytic rate constant for Hyz oxidation were obtained using chronoamperometry. Additionally, CuO-Co3O4 was effectively utilized to analyze Hyz in real samples with acceptable recovery rates.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call