Abstract
The glass forming ability of the [(Fe 12/13Y 1/13) 100- x B x ] 96Nb 2Zr 2 ( x=9–26) system was investigated using a series of cluster lines. Three types of clusters, an icosahedron (Fe 12Y), a capped Archimedes anti-prism (Fe 8B 3) and a capped trigonal prism (Fe 9B), as well as a binary eutectic (Fe 83B 17) were considered. Bulk glassy alloy rods of 3 mm in diameter were synthesized using a copper mold suction-casting method. The glass transition temperature was observed for all samples in the boron range of 15.9at%-25.7at%, with the alloy at 15.9at% of boron having the best thermal properties. The ferrous-based bulk metallic glasses (BMG) obtained have high reduced glass transition temperatures with the maximum reaching 0.63 and large supercooled liquid regions with the maximum reaching 111 K. Magnetic testing revealed a large value of coercive force and remanent magnetization, being 11 kA/m and 0.1 T, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of University of Science and Technology Beijing, Mineral, Metallurgy, Material
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.