Abstract
Fe-based bulk metallic glasses (BMGs) with high boron content have potential application as a coating material used in the framework for storing spent nuclear fuels to support their safe long-term disposal. The high glass forming ability (GFA) and large supercooled liquid region are therefore required for such Fe-based BMGs in either the glassy powder fabrication or the subsequent coating spraying. In order to meet these requirements, the influence of Nb content on the GFA of Fe57Cr10Zr8B18Mo7−xNbx (x=1–5, at.%) alloys was investigated, as Nb has positive roles in GFA and thermal stability of BMGs. The results indicate that a fully amorphous phase in the as-cast samples with 3 mm in diameter is obtained for both the Fe57Cr10Zr8B18Mo5Nb2 and Fe57Cr10Zr8B18Mo4Nb3 alloys. The corresponding supercooled liquid regions of the two BMGs are 78 K and 71 K, respectively. The mechanism for improving their GFA was analyzed based on the principle of metal solidification, the parameters for glass formation and thermal properties of the alloys. The compression strength and Vicker’s hardness of the two BMGs are 1,950 MPa and 1,310 HV, 2,062 MPa and 1,180 HV, respectively. The developed BMGs with high B content, good GFA, and very high hardness can be used as coating materials to the framework for spent nuclear fuels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.