Abstract

The application of ionic liquids (IL) in polymer electrolytes represents a safer alternative to the currently used organic solvents in lithium batteries due to their nonflammability and thermal stability. However, as a plasticizer, it is generally agreed that the introduction of ionic liquid usually leads to a trade-off between ion transport and mechanical properties of polymer electrolyte. Here we report the synthesis of an IL-embedded polymer electrolyte with both high ionic conductivity (2.77 × 10−4 S cm−1 at room temperature) and excellent mechanical properties (high tensile strength up to 11.4 MPa and excellent stretchability of 387% elongation at break) achieved by strong ion–dipole interactions between polymer electrolyte components, which was unveiled by the DFT calculation. Moreover, this polymer electrolyte also exhibits nonflammability, good thermal stability and the ability to recover reversibly from applied stress, i.e., excellent elasticity. This highly viscoelastic polymer electrolyte enables tight interfacial contact and good adaptability with electrodes for stable lithium stripping/plating for 2000 h under a current density of 0.1 mA cm−2. By coupling with this polymer electrolyte, the LiFePO4/Li cells exhibit outstanding cycling stability at room temperature as well as the reliability under extreme environmental temperature or being abused.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.