A calorimetric study of the glass transition kinetics in polyisoprene

Abstract

The connection between the dielectric and calorimetric relaxation behaviours of synthetic polyisoprene Cariflex IR 305 is studied. A similar comparison of dielectric and dilatometric results was described in [1]. The heat capacity was measured during heating of samples prepared with different thermal history. Experimental results were compared with the heat capacity curves calculated for a model based on the multiparameter theory of Kovacs et al. [4]. The model considers the relaxation system as being composed of a set of subsystems characterized by different relaxation times. The distribution of relaxation times and their temperature dependence were taken from the diclectric measurement. The relaxation time of a subsystem from posed to depend, not only on the actual, temperature of the sample, but also on the deviation of this subsystem from equilibrium, or alternatively, on the deviation of the system as a whole. The comparison between the measured and modeled curves shows that both influences must be taken into account in order to explain the experimental results.