Abstract
Newly developed Zr–45Ti–5Al–3V alloy were irradiated by 84MeV carbon ions with doses of 4*1015ions/cm2 and 12*1015ions/cm2, respectively. XRD, SEM, TEM, SAD and tensile tests were performed to study the microstructural evolution and mechanical properties modification upon high energy carbon ion irradiation. XRD patterns show no phase change while the diffraction peak position and intensity vary with irradiation doses. Tensile tests verify monotonic change of alloy strengths and elongations upon irradiation. Microstructure observations of the irradiated samples reveal the irradiation-induced precipitation of (Zr,Ti)3C2, which was believed contributing to the alloy hardening. Superlattice was discovered by the SAD patterns of original and irradiated samples and the high energy C-ions implantation was demonstrated to promote the disorder–order transition by introducing lattice defects.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.