6H and 4H-SiC Avalanche Photodiodes

Abstract

We report on the fabrication and testing of SiC p-i-n avalanche photodiodes. APDs of 0.25 mm2 area on a-plane (1120) 6H-SiC as well as off-axis Si face 6H and 4H-SiC were successfully fabricated. A beveled mesa was used as edge termination. Recessed windows were formed using reactive ion etching to enhance low-wavelength UV performance. We performed current-voltage tests with and without UV illumination to determine dark current, photocurrent, and gain on selected devices. Dark current was less than 1 pA at 0.5Vbr on multiple devices. Quantum efficiency of 40% or greater was observed for all orientations and polytypes.