Abstract
Ti-6Al-4V alloy was forging in different temperatures processed, different forging ratio, after 450~550℃ heat treatment, by X ray diffraction (XRD) and scanning electron microscopy (SEM) and Transmission electron microscopy (TEM) observation. In accordance with the experimental result, alloy from 800℃ forging, Low forging ratio and high forging ratio, the microstructure is fine-grained + + α+ β-phase. By XRD (0002) diffraction peak is the maximum. Alloy from 950℃ forging, Low forging ratio, the microstructure is equiaxed + lath + acicular martensite α' + α + β-phase. High forging ratio, non-thermal reaction ω-phase precipitation. By XRD (0002) and (01-11) diffraction peak is the quite.Alloy from 1050℃ forging the microstructure is α' + α' + α + β-phase. By XRD (01-11) diffraction peak is the maximum. Microstructure is Hexagonal-Closed-Packed (H.C.P) microstructure of α-phase, acicular martensitic structure of α'-phase, ω-phase and the orthorhombic α-phase. Body-Centered-Cubic (B.C.C) structure of the β-phase, The lattice parameter of is a=0.295nm、c=0.466nm，c/a ratio of 1.579; α'-phase with a = 0.291nm, c = 0.465nm, c/a ratio of 1.597; α-phase with a = 0.303nm, b = 0.492nm, c = 0.466nm; ω-phase with a = 0.468nm, c = 0.293nm; β-phase with a = 0.327nm. Key words: Titanium alloy, Forging, Texture.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.