Abstract

In order to develop new β-type Ti-based biochemical materials, a series of Ti-10Mo-1.25Si-xZr (x=4–13) alloys were designed and prepared using vacuum arc melting method. Phase analysis and microstructural observation showed that all the as cast samples consisted of equiaxed β-Ti phase. With the increase of Zr content, the structure of grain boundary changed from semi-continuous network to denser granular, and the microstructure was refined. The solid solution effect of the β-phase stabilization elements (i.e. Mo, Zr and Si) predominantly determined the mechanical properties. These β-type Ti-10Mo-1.25Si-xZr biomaterials exhibited a good combination of high compressive strength, high yield stress, good plasticity, as well as rather low Young's modulus (in the range of 23.086GPa–32.623GPa), which may offer potential advantages in the applications in hard tissue replacements (HTRs).