Abstract
본 연구에서는 polyester polyol을 사용한 수성 폴리우레탄의 내수성을 향상시키기 위해 polyester polyol, poly(propylene carbonate) (PPC), 4,4-dicyclohexylmethane diisocyanate (<TEX>$H_{12}MDI$</TEX>), dimethylol propionic acid (DMPA)를 사용하여 수성 폴리우레탄을 합성하였다. PPC를 사용하여 합성된 수성 폴리우레탄의 물성은 FT-IR, GPC, DSC 및 UTM 등을 통해 평가하였다. PPC의 함량이 증가함에 따라 합성된 수성 폴리우레탄의 기계적 물성은 증가하였으며 polyester polyol과 PPC의 비가 9 : 1일 때 가장 높은 값의 내수성을 나타내었다. In this study, waterborne polyurethane was synthesized with polyester polyol, poly(propylene carbonate) (PPC), 4,4-dicyclohexylmethane diisocyanate (<TEX>$H_{12}MDI$</TEX>) and dimethylol propionic acid (DMPA) to improve the water resistance. The properties of the synthesized waterborne polyurethane using poly(propylene carbonate) (WPUP) was evaluated through FT-IR, GPC, DSC and UTM. The mechanical properties were increased with the increase in the amount of PPC. When the ratio of polyester polyol to poly(propylene carbonate) is 9:1, the highest water resistance was showed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.