Abstract
TiC-TiO2 composite powders were prepared by in-flight oxidation of titanium carbide powder in RF induction thermal plasmas. Original titanium carbide powder of 20-38μm in particle size was axially injected into the center of argon-oxygen plasma. The powders were partially spheroidized and evaporated through the plasma treatment. X-ray diffraction of plasma-treated powders showed the formation of titanium dioxides, both rutile and anatase phases. The phase content of the plasma-prepared powders strongly depended on the plasma conditions, such as the plasma generating pressure and the oxygen flow rate in plasma generating gas. Especially, the increase of oxygen flow rate in plasma gas gave rise to the increase of heat transfer from plasma to powder particles, exothermic heat of oxidation reaction and cooling rate of plasma, giving the increase of spheroidization ratio, formation ratio of titanium dioxides, and content of anatase phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of the Japan Society of Powder and Powder Metallurgy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.