Abstract
Introduction: in present scenario, light and high strength aluminium metal matrix composite are extensively used due to its high mechanical and tribological properties. Aluminium metal matrix composite reinforced with ceramic and industrial waste can customize its mechanical-chemical behavior. The purpose of the work: to create an aluminum matrix composite material using ceramic (primary) and industrial (secondary) waste represented by red mud and coconut shell ash, respectively. The mass fraction of the strengthening phase varied from 5 to 12.5 wt. % respectively with the residual mass percentage of the aluminum alloy. Method of investigation: nine specimens of composite materials were prepared by stir casting. Stirring was carried out at a speed of 50 to 100 rpm for 20 minutes at a temperature of 800 °C. Result and Discussion: the hardness behavior of the aluminum metal matrix composite was studied at an indentation load of 10, 15 and 20 kN. Taguchi method with L27 orthogonal array was selected to conduct analysis of variance (ANOVA) and regression analysis by selecting the mass percentage of red mud and mass percentage of coconut shell ash. The indentation load was used as an input parameter, and the hardness behavior was taken as an output parameter. The signal-to-noise ratio, response rank table, contour plot, and normal probability plot are investigated and it is found that hardness values improve with the addition of both reinforcing components and indenter load. The results show that the hardness value varies from 33.34 HB to 53.44 HB, and the effect of red mud mass percentage is more significant than the indenter load and coconut shell ash mass percentage.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.