Abstract
The anodic behavior of CrSi2 electrode in 0,5 M H2SO4, 0,5 M HClO4, 0,5 M HNO3 and 0,5 M HCl solutions has been studied by the methods of polarization, capacitance, and impedance measurements. It has been concluded that in the process of anodic oxidation at potentials from corrosion E to transpassivation E inclusive, an oxide film is formed on the surface of chromium disilicide in the studied media, which is close in composition to SiO2 (with a small content of chromium oxides). The presence of this film on the silicide surface determines its high chemical resistance in the studied solutions. The thickness of the oxide film on CrSi2 has been calculated depending on the potential and composition of the electrolyte. The growth constant of the oxide film has been determined.
Highlights
The anodic behavior of CrSi2 electrode in 0,5 M H2SO4, 0,5 M HClO4, 0,5 M HNO3 and 0,5 M HCl solutions has been studied by the methods of polarization, capacitance, and impedance measurements
It has been concluded that in the process of anodic oxidation at potentials from corrosion E to transpassivation E inclusive, an oxide film is formed on the surface of chromium disilicide in the studied media, which is close in composition to SiO2
4. Yuan L., Wang H.M. Corrosion behaviors of a γ-toughened Cr13Ni5Si2/Cr3Ni5Si2 multi-phase ternary metal silicide alloy in NaCl solution // Electrochimica Acta
Summary
Емкостных и импедансных измерений изучено анодное поведение CrSi2-электрода в растворах 0,5 M H2SO4, 0,5 M HClO4, 0,5 M HNO3 и 0,5 M HCl. Сделан вывод, что в процессе анодного окисления при потенциалах от E коррозии до E перепассивации включительно на поверхности дисилицида хрома в исследованных средах формируется оксидная пленка, близкая по составу к SiO2 (с небольшим содержанием оксидов хрома). Присутствие на поверхности силицида данной пленки обусловливает его высокое химическое сопротивление в изученных растворах. Рассчитана толщина оксидной пленки на CrSi2 в зависимости от потенциала и состава электролита. Ключевые слова: дисилицид хрома CrSi2; анодное окисление; пассивация; кислый электролит; импеданс. Поступила в редакцию 18.08.2021; после доработки 01.09.2021; принята к публикации 06.09.2021. B. Shein Perm State University, Perm, Russia
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Вестник Пермского университета. Серия «Химия» = Bulletin of Perm University. CHEMISTRY
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.