In order to clarify the possibility of sintering reactor powders of ultra-high molecular weight polyethylene under pressure at a temperature higher than its equilibrium melting point at atmospheric pressure (T0m) without catastrophic changes in the internal structure of particles, a comparative WAXS analysis was carried out of the samples sintered below (T <T0m) and above (T> T0m) this temperature and cooled under different conditions. A multifunctional structural analysis of the X-ray scattering curves recorded in the Bragg-Brentano mode on a 2D Phaser Bruker diffractometer from UHMWPE reactor powders sintered under different conditions was carried out, and the crystallite sizes were calculated. It was found that an increase in the sintering temperature above T0m does not significantly change the crystal structure of the polymer, and the precursors produced can be used for further orientational hardening.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.