ПІДВИЩЕННЯ ВОГНЕЗАХИСНОЇ ЕФЕКТИВНОСТІ ІНТУМЕСЦЕНТНИХ ЕПОКСИДНИХ ПОКРИТТІВ СПОЛУКАМИ ІНТЕРКАЛЬОВАНОГО ГРАФІТУ

Abstract

Investigation of the effect of nitrate oxide graphite on the parameters of char layer, obtained from the system of ammonium polyphosphate / melamine / pentaerythritol / epoxy resin under the influence of temperatures of 200–800 °С. Methodology. A fire retardant mixture was chosen as a model intumescent system ammonium polyphosphate / melamine / pentaerythritol. As a polymer component was used bisphenols A / F epoxy resin together with a polyamidoamine hardener. Nitrate oxide graphite was obtained by oxidation of natural scaly graphite with fuming nitrogen acid. The effect of impurities of nitrate oxide graphite was determined by thermogravimetry on the intumescence coefficient of intumescent compositions and the mass of the char residue intumescent compositions in temperature range of 200–800 °С. Findings. The influence of nitrate oxide graphite on the characteristics was studied of char layer of epoxy intumescent system ammonium polyphosphate / melamine / pentaerythritol / epoxy resin. The study of thermal oxidative degradation was carried out intumescent compositions in the temperature range 200–800 °С. It was shown that intercalated graphite compounds increase the thermal stability of the formed char layer at temperatures > 600 °С. Determined intumescence coefficients and thermogravimetric analysis of modified intumescent systems was performed nitrate oxide graphite with different degrees of intercalation, in the conditions of 200–800 °С. It was established that the optimal parameters of the char layer are in terms of volume intumescence coefficient and mass of the char residue are provided by graphites, which contain 15–25% of intercalant in its composition. But the results obtained allow us to determine nitrate oxide graphite as a promising modifier of epoxy intumescent systems to increase its fire protection efficiency. Originality. The influence of degree of intercalation of nitrate oxide graphite was studied on the characteristics of char layer of epoxy intumescent system for the first time. Practical value. The optimal content of intercalant in nitrate oxide graphite was established for the development of formulations of intumescent epoxy coatings with increased fire retardant properties.