Effect of pretreatments on the graphene coated bipolar plate of proton exchange membrane fuel cell(PEMFC) was investigated in simulated environments for PEMFC by using electrochemical measurement techniques. Interfacial contact resistance(ICR) between the graphene coated bipolar plate and the gas diffusion layer(GDL) was measured. The value of ICR decreased with an increase in compaction stress(). ICR of graphene coated bipolar plate was higher than that of bare 316L stainless steel. However, Potentiodynamic measurement results showed that the corrosion resistance of graphene coated bipolar plate was higher than that of bare 316L stainless steel. acid pretreatment was the most effective among various pretreatments. The lowest ICR and the corrosion current density were obtained when using solution pretreatment.