Zone Of High-strength Low-alloy Steels Research Articles

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Effect of Ce Content on Microstructure-Toughness Relationship in the Simulated Coarse-Grained Heat-Affected Zone of High-Strength Low-Alloy Steels

The study aimed to identify a moderate degree of Ce addition to improve the toughness in the simulated coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steels, based on the effect of the Ce content on particle characteristics, microstructure and impact toughness. Three steels with 0.012 wt.%, 0.050 wt.% and 0.086 wt.% Ce content were subjected to 100 kJ/cm heat input in their thermal welding cycles. The particles and microstructures in the simulated CGHAZ of each steel were characterized and the impact-absorbance energy levels were measured at −20 °C. The results indicated that Ce2O2S inclusion compounds were gradually modified to CexSy-CeP and CeP with the increasing of the Ce content. A higher fraction of acicular ferrite was formed in the 0.012 wt.%-Ce-treated steel due to the lower mismatch between Ce2O2S and α-Fe. Furthermore, a lower fraction of M-A constituent was obtained in the 0.012 wt.%-Ce-treated steel. As a result, superior toughness and a typical amount of ductile fracture were detected in the simulated CGHAZ of the 0.012 wt.%-Ce-treated steel. Compared with the 0.012 wt.%-Ce-treated steel, a smaller prior austenite grain was observed in the 0.086 wt.%-Ce-treated steel because of the segregation of CeP at the grain boundary. However, the larger size and density of CeP led to poor toughness in the CGHAZ of the 0.086 wt.%-Ce-treated steel.

Impact of Mo content on the microstructure– toughness relationship in the coarse-grained heat-affected zone of high-strength low-alloy steels

Abstract The present study elucidates the influence of Mo content on the microstructure – toughness relationship in the coarsegrained heat-affected zone of high-strength low-alloy steels. The low-Mo and high-Mo steels were subjected to 100 kJ cm–1 heat input welding thermal cycling. The results indicated that (Ti,Mo)-carbonitrides were formed in high-Mo steel, whereas (Ti,Nb)-carbonitrides were formed in low-Mo steel. The finer and dispersed precipitates in high-Mo steel refined the prior austenite grain in the coarse-grained heat-affected zone based on the grain boundary pinning effect. However, the smaller prior austenite grain and excessive Mo content induced the formation of an entirely bainitic microstructure in high-Mo steel. Furthermore, a higher fraction of martensite –austenite constituents was observed in high-Mo steel. These results could be responsible for the deterioration of the toughness in the coarse-grained heat-affected zone of high-Mo steel.

The critical influence of La content on the microstructure-toughness relationship in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels

The present study was envisaged to investigate the role of La content on the particle, microstructure and toughness in the simulated coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steels. Three steels with La content of 0.016 wt.%, 0.046 wt.% and 0.093 wt.% were prepared and simulated in a 100 kJ/cm heat input welding thermal cycle. Subsequently, the particle and microstructure of selected specimens were characterized and the impact absorb energy was measured at −20 °C. The results indicated that the La2O2S inclusions in 0.016 wt.%-La steel were gradually modified to LaS-LaP in 0.046 wt.%-La steel and to LaP in 0.093 wt.%-La steel. A higher fraction of acicular ferrite was obtained in the simulated CGHAZ of 0.016 wt.%-La steel, since the inclusion of La2O2S was more powerful to induce the formation of acicular ferrite. Furthermore, the fraction of M-A constituents in the simulated CGHAZ increased with increasing La content. The impact toughness in the simulated CGHAZ of 0.016 wt.%-La steel was the highest, owing to the high fraction of the fine-grained acicular ferrite and low fraction of M-A constituent.

The significant impact of Ti content on microstructure–toughness relationship in the simulated coarse-grained heated-affected zone of high-strength low-alloy steels

ABSTRACTThis study aims to investigate the influence of Ti addition on microstructure and toughness in the simulated coarse-grained heated-affected zone (CGHAZ) of high-strength low-alloy steels. The steels with low and high Ti content respectively were subjected to 100 kJ/cm heat input welding thermal cycle. The results indicated that the second-phase particles were mainly oxide covered with MnS and fine (Ti,Nb)N precipitate in low-Ti steel, which were modified to the oxide surrounded by TiN and coarse (Ti,Nb)N precipitate in high-Ti steel. Compared with low-Ti steels, the coarser precipitates induced larger austenite grain in CGHAZ of high-Ti steel. Moreover, the wrapping of TiN decreases the ability of inclusion to promote the nucleation of acicular ferrite, resulting in lower fraction of acicular ferrite in CGHAZ of high-Ti steel. Content of martensite-austenite constituent increased in CGHAZ of high-Ti steel. They were all responsible for the degeneration in toughness in CGHAZ of high-Ti steel.

Effects of Small Ni Addition on the Microstructure and Toughness of Coarse-Grained Heat-Affected Zone of High-Strength Low-Alloy Steel

The objective of the present study is to investigate the effects of nickel (Ni) on the microstructure and impact toughness of coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steel. It was observed that the microstructure of CGHAZ predominantly consisted of bainite and a small proportion of martensite-austenite (M-A) constituents and acicular ferrite (AF). With increased Ni content, the percentage of M-A constituent decreased and AF increased; consequently, the impact toughness of CGHAZ increased. The study revealed that a small addition of nickel significantly affected the formation of M-A constituents and AF; however, no obvious influence was observed on the bainitic microstructure of high-strength low-alloy steel.

The role of Cu and Al addition on the microstructure and fracture characteristics in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels with superior toughness

ABSTRACTThe effects of Cu and Al addition on the microstructure and fracture in the coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steels with superior toughness were studied and compared with the X70 pipeline base steel counterpart. The microstructure in base steel was dominated by a small fraction of acicular ferrite and predominantly bainite. However, acicular ferrite microstructure was obtained in Cu-bearing steel, which nucleated on complex oxide with outer layer of MnS and CuS because of Cu addition. The microstructure in Al-bearing steel consisted of bainite with ultrafine martensite–austenite constituent, which was refined by Al addition. CGHAZ in Cu-bearing and Al-bearing steels had superior impact toughness and ductile fracture, which were attributed to acicular ferrite and ultrafine martensite–austenite constituent, respectively.

Toughness improvement by Zr addition in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels

ABSTRACTThe effect of Zr addition on the microstructure and impact toughness in the coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steels subjected to 100 kJ cm-1 heat input was investigated. The second- phase particles were mainly Al–Ti complex oxides and (Ti,Nb)N precipitates in Zr-free steel, whereas lots of finer Zr–Al–Ti complex oxides and (Al,Ti,Nb)N precipitates were formed in Zr-bearing steel because of Zr addition. These finer oxides and precipitates effectively restricted the austenite grain growth by pinning effect during welding thermal cycle, and smaller and more uniform prior austenite grains were obtained in CGHAZ of Zr-bearing steel. Furthermore, more acicular ferrite grains nucleated on Zr–Al–Ti complex oxides, inducing formation of fine-grained microstructure in CGHAZ of Zr-bearing steel. The toughness improvement in CGHAZ of Zr-bearing steel with dimple fracture surface was attributed to the grain refinement by pinning effect and acicular ferrite formation.

In situ observation and electron backscattered diffraction analysis of granular bainite in simulated heat-affected zone of high-strength low-alloy steel

ABSTRACTIn this study, the formation of granular bainite (GB) which may form in the heat-affected zone of double-sided double arc welding joint was in situ observed. The crystallographic characteristics of GB were also compared with those of microstructure mainly comprising lath bainite (LB). The results show that bainite packets exist at the initial stage of GB transformation and can be distinguished by the distribution of retained austenite and martensite–austenite constituents. The bainite blocks of GB are larger than those of LB which makes both the length and fraction of high-angle grain boundaries in GB less than those of LB which partly lead to the brittleness of granular bainite.

In-situ microscopy study of grain refinement in the simulated heat-affected zone of high-strength low-alloy steel by TiN particle

ABSTRACTHigh-strength low-alloy steels subjected to high heat input welding are susceptible to failure due to low toughness caused by grain coarsening. The effect of TiN on grain refinement in the simulated heat-affected zone (HAZ) was investigated. Because of small amount of Ti addition, abundant dispersed nanoscale TiN precipitates were formed. The TiN precipitates tended to be stable at high temperature and effectively retarded the austenite grain growth by refining the grain size during thermal cycle. Furthermore, the TiN also covered on the surface of Al–Ti complex oxide with MnS and caused low interface energy with ferrite. The acicular ferrite grains nucleated on complex inclusion in austenite grains at intermediate temperature and induced the austenite grain transform to the fine-grained mixed microstructure of acicular ferrite and bainite. The crystallographic grain size became small in the simulated HAZ due to the effective pinning effect and acicular ferrite formation.

Effect of Cu addition on microstructure and impact toughness in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels

The effects of Cu content on microstructure and impact toughness in the simulated coarse-grained heat-affected zone (CGHAZ) of high-strength low-alloy steels were investigated. It has been observed that the microstructure in the simulated CGHAZ of Cu-free steel is dominated by a small proportion of acicular ferrite and predominantly bainite with martensite–austenite constituent. Whereas, in the 0.45 and 1.01% Cu-containing steels, the acicular ferrite increased significantly due to the effective nucleation on intragranular inclusions with outer layer of MnS and CuS. The formation of acicular ferrite is attributed to superior high heat-affected zone impact toughness in the 0.45% Cu-containing steel. Furthermore, the increasing martensite–austenite constituent and ε-Cu precipitates in the simulated CGHAZ of 1.01% Cu-containing steel caused degradation in impact toughness.

Effect of Cr Content on Microstructure and Impact Toughness in the Simulated Coarse-Grained Heat-Affected Zone of High-Strength Low-Alloy Steels

The relationship of Cr content to microstructure and impact toughness in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels subjected to varying heat input welding thermal cycles is investigated. Results show that the microstructures of the simulated coarse-grain heat-affected zone in steels with different Cr contents and welding heat inputs consist of predominantly bainite, a small proportion of acicular ferrite, and martensite–austenite constituents. With the Cr content increasing from 0.33 to 0.65% and 1.02%, the fraction of acicular ferrite is decreased and martensite–austenite constituents are increased. Meanwhile, when the heat input increased from 20 to 100 and 200 kJ cm−1, martensite–austenite constituents increase in amount and coarsen remarkably. The impact toughness of simulated coarse-grain heat-affected zone at −20 °C decreases obviously with increasing Cr content, especially subjected to high-heat input welding.

Toughness improvement by Cu addition in the simulated coarse-grained heat-affected zone of high-strength low-alloy steels

The effect of microstructure and Cu addition in a simulated coarse-grained heat-affected zone (CGHAZ) of a high-strength low-alloy (HSLA) steel subjected to 100 kJ cm−1 heat input welding was studied. It has been observed that the primary microstructure in Cu-free HSLA steels is dominated by bainite, whereas, in Cu-bearing HSLA steels, the predominant microstructure is acicular ferrite. The acicular ferrite nucleated at intragranular complex inclusions consisting of Al and Ti oxides, covered with layer of MnS and CuS. The presence of high intensity of acicular ferrite and hard impingements between acicular ferrite laths or plates has contributed to the fine-grained and interlocked microstructure. The enhanced toughness in CGHAZ of Cu-bearing HSLA steel is attributed to the fine-grained interlocked microstructure of acicular ferrite.

In-situ observation of grain refinement in the simulated heat-affected zone of high-strength low-alloy steel by Zr-Ti combined deoxidation

The effect of Zr-Ti combined deoxidation on the grain refinement in the simulated coarse-grained heat-affected zone of a high-strength low-alloy steel was investigated by means of analytical characterization techniques such as in-situ microscopy, transmission electron microscopy, and electron backscattered diffraction analysis. Owing to the Zr-Ti combined deoxidation, a large amount of fine Zr-Ti oxide particles were formed in the steel and retarded the austenite grain growth during simulated welding thermal cycle. The austenite grains were small and uniform. The Mn can diffuse spontaneously from austenite to Zr-Ti oxide inclusion and MnS precipitated on ZrO2, which can form Mn depleted zone in the vicinity of inclusion. The acicular ferrite grains nucleated on intragranular Zr-Ti oxide inclusions in austenite grains grew in different directions and effectively divided the austenite grain into several finer and separate regions at intermediate temperature. The crystallographic grain size became small in the simulated coarse-grained heat-affected zone of Zr-Ti-killed steel due to the effective pinning effect by Zr-Ti oxide particles and acicular ferrite formation.

In-situ Observations of Acicular Ferrite Growth Behavior in the Simulated Coarse-grained Heat-affected Zone of High-strength Low-alloy Steels

In-situ Observations of Acicular Ferrite Growth Behavior in the Simulated Coarse-grained Heat-affected Zone of High-strength Low-alloy Steels

Correlation of modified crack tip opening distance with heat input to the heat affected zone of high-strength low-alloy steels

Investigated is the dependency of the crack tip opening displacement (CTOD) on the local microstructure of the heat affected zone in high-strength low-alloy (HSLA) microalloyed steel. Since the initiation of the crack tip location could not be controlled in fatigue, any possible correlation between heat iput in welding and fracture toughness could be smeared. Modified CTOD data are defined; they show that the fracture resistance of the weld joint decreased as the heat input increased.