Ge-alloying of Cu2ZnSnS4 is a promising strategy for producing wide-bandgap absorber materials suitable for use in tandem structures or indoor solar cell applications. Incorporating Ge can suppress Sn-related defects while maintaining the kesterite structure and p-type conductivity throughout the entire range of composition. In this study, Cu2Zn(Sn1−xGex)S4 monograins were synthesized in molten salt by the synthesis-growth method, where value x was varied from 0 to 1, with a step of 0.2. The inclusion of Ge into the crystals was confirmed by energy-dispersive X-ray spectroscopy, Raman spectroscopy, and X-ray diffraction analysis. The bandgaps of Cu2Zn(Sn1−xGex)S4 solid solutions were determined as Eg = 1.50–2.25 eV by external quantum efficiency measurement. A detailed study of temperature and laser power-dependent photoluminescence (PL) for powder crystals with x = 0, x = 0.2 and x = 0.4 revealed that the dominant recombination mechanisms originate from defect clusters involving a shallow acceptor and deep donor defect. Ge-alloying helped to suppress the harmful SnZn donor defects, but at the same time shifted the defects' energy levels deeper into the bandgap. The obtained activation energies indicate that the acceptor defect becomes shallower with the inclusion of Ge. At the mid-temperature range (T = 60–200 K), the presence of two different recombinations was revealed in the system, originating from very closely located PL emission bands.