Oxygen-deficient iron oxide thin films, which have recently been shown to be highly active for photoelectrochemical water oxidation, were surface-functionalized with a monolayer of a molecular iridium water oxidation cocatalyst. The iridium catalyst was found to dramatically improve the kinetics of the water oxidation reaction at both stoichiometric and nonstoichiometric α-Fe2O3-x surfaces. This was found to be the case in both the dark and in the light as evidenced by cyclic voltammetry, Tafel analysis, and electrochemical impedance spectroscopy (EIS). Oxygen evolution measurements under working conditions confirmed high Faradaic efficiencies of 69–100% and good stability over 22 h of operation for the functionalized electrodes. The resulting ∼200–300 mV shift in onset potential for the iridium-functionalized sample was attributed to improved interfacial charge transfer and oxygen evolution kinetics. Mott–Schottky plots revealed that there was no shift in flat-band potential or change in donor density fo...