Composite Resin Discs Research Articles

Effect of different bleaching protocols on the color and translucency parameters of a new monochromatic universal composite resin

Background. Considering the few studies on the effect of bleaching protocols on the color properties of a newly developed monochromatic universal composite resin, the present study evaluated the effect of different bleaching protocols on the color change and translucency of Omnichroma (OMN) composite resin. Methods. In this laboratory study, 45 cylindrical OMN composite resin disks with a diameter of 10 mm and a thickness of 2 mm were used. The samples were randomly divided into three groups (n=15) based on the bleaching protocols: group 1: 40% hydrogen peroxide (HP) for 20 minutes, twice a day for three sessions one week apart; group 2: 20% carbamide peroxide (CP) for 8 hours a day, for 14 consecutive days; group 3: 40% HP with Nd:YAG laser (HP+Nd:YAG laser) applied on the gel for 30 seconds twice. Baseline and post-bleaching measurements of color parameters were done using a Vita Easyshade spectrophotometer. Data was analyzed using paired-samples t-test, one-way ANOVA, and post hoc Tukey tests (P<0.05). Results. All the bleaching protocols significantly changed the color (P<0.001) and translucency (P<0.001) parameters. CP caused the most color changes (P<0.05) and translucency (P<0.05), which were significant, and color and translucency changes caused by HP and HP+Nd:YAG laser were not significant (P>0.05). Conclusion. Bleaching caused a noticeable change in the color and translucency of the OMN composite resin. The effect of the at-home bleaching protocol was greater than the in-office ones.

Evaluation of Surface Roughness and Microhardness of Bulk-fill and Nanohybrid Composite after Exposure to Different Beverages at Various Time Intervals - An In vitro Study.

The aim of the study was to compare the surface roughness and microhardness of bulk-fill composite and nanohybrid composite resin after exposure to three different beverages at different time intervals. In this study, 60 composite discs each for bulk fill and nanohybrid, of dimensions 10 mm × 2 mm were made. Both composites were randomly divided into four subgroups, i.e., 15 samples each for artificial saliva, tea, coffee, and soft drinks which were further subdivided into five samples for three time intervals. Composite resin discs were immersed in beverages for 4 min in 24 h for 7, 15, and 30 days. All samples were evaluated for surface roughness and microhardness before and after immersion. Both the composites showed a significant increase in surface roughness in all the beverages with maximum change in surface roughness observed in nanohybrid composite resin immersed in soft drinks. Furthermore, the microhardness of both the composites was decreased significantly in all beverages with maximum change in microhardness observed in nanohybrid composite resin immersed in soft drinks. Bulk-fill composite resin has better resistance to surface roughness and higher microhardness as compared to nanohybrid. Furthermore, acidic beverages highly affect the physical properties of both composite resins for longer periods.

Hydrated Calcium Silicate in Resin Composites for Prevention of Secondary Caries

Introduction and aimsThe gaps at the margins of restorative composite resin can increase as the carious process occurs underneath the materials, causing further demineralization along the tooth cavity wall. The aim of this study was to evaluate the effects of restorative resin composite containing hydrated calcium silicate (hCS) filler on enamel protection against demineralization by simulating microleakage between the test material and teeth in a cariogenic environment. MethodsThe experimental resin composites were composed of 70 wt.% filler, which was mixed with a glass filler and hCS in a weight ratio of 70.0% glass (hCS 0), 17.5% hCS + 52.5% glass (hCS 17.5), 35.0% hCS + 35.0% glass (hCS 35.0), and 52.5% hCS + 17.5% glass (hCS 52.5). A light-cured experimental resin composite disk was positioned over a polished bovine enamel disk, separated by a 30-µm gap, and immersed in artificial saliva with pH 4.0 for 15, 30, and 60 days. After the immersion period, the enamel disk was separated from the resin composite disk and evaluated using a microhardness tester, atomic force microscopy, and polarized light microscopy. The opposing sides of the enamel and resin composite disks were observed using scanning electron microscopy/energy dispersive X-ray spectrometry. ResultsThe enamel surface showed a significant increase in microhardness, decreased roughness, and remineralization layer as the proportion of hCS increased (P < .05). In the scanning electron microscopy image, the enamel surface with hCS 35.0 and 52.5 after all experimental immersion periods, showed a pattern similar to that of a sound tooth. ConclusionsThe results demonstrated that increasing the hCS filler level of restorative resin composites significantly decreased enamel demineralization. Clinical relevanceHydrated calcium silicate laced restorative resin composites may be a promising dental biomaterial for protecting teeth against demineralization and preventing secondary caries around restorations.

The Effect of Mechanical Alteration on Repair Bond Strength of S-PRG-Filler-Based Resin Composite Materials.

This study investigates the impact of mechanical alteration on resin composite surfaces and its subsequent effect on repair bond strength. A total of 100 resin composite disks were prepared and were allocated for 24 h or 1 year of artificial aging. Specimens were embedded in epoxy resin, and the composite surfaces were mechanically altered using either diamond burs or air abrasion with aluminum oxide or glass beads. A universal bonding material was applied and a 2 mm circular and 3 mm high repair composite cylinder were prepared using a Teflon mold. Then, the specimens were tested for their shear bond strength, and the de-bonded specimens were observed under a scanning electron microscope to determine the failure pattern. SPSS 26.0 statistical software was used to analyze the data. Two-way ANOVA showed a statistically significant effect of mechanical alteration and aging on the shear bond strength of S-PRG-filler-based resin composite (p < 0.05). Surface modification with a fine diamond bur showed a significantly higher bond strength in both 24-h- and 1-year-aged specimens. Surface modification with alumina significantly increased the bond strength of 1-year-aged specimens; however, it was statistically insignificant for 24 h-aged specimens. Mechanical alteration with a fine diamond bur and 50-micron alumina can improve the repair bond strength of the composite.

Comparative bonding performance of coronal dentin disks and CAD/CAM resin composite disks for biological restoration: The impact of resin-coating technique.

This study evaluated the bonding performance of coronal dentin disks, designed for biological restoration, and CAD/CAM resin composite disks when bonded to flat dentin surfaces using dual-cure resin cements, with and without a resin-coating (RC) technique. Three distinct groups were established within the non-RC group, each using one of the two types of resin cements in a self-adhesive mode: one-step self-etch adhesive (1-SEA) without light-cure, 1-SEA with light-cure, and a separate group using an alternate cement. Within the RC group, a subgroup was established for each cement. The microtensile bond strength (μTBS) of the disk-dentin beam was tested after 0 and 10,000 thermocycles in a 5°C/55°C. No significant μTBS difference was observed among the non-RC groups. However, when using RC, the μTBSs of coronal dentin disks significantly exceeded those of CAD/CAM resin composite disks. Thermocycle aging did not affect μTBS in any of the bonding methods, except in self-adhesive mode.

The optical behavior of nano filled resin composite loaded with graphene oxide nanoparticles

ObjectivesAssessment of the effect of incorporation of graphene oxide nanoparticles (GONPs), different concentrations into resin composite with different thicknesses on its color modulation.Materials and methodsGONPs were prepared using the chemical reduction method and characterized using a transmission electron microscope and X-ray diffraction. The minimum concentrations of GONPs that provided the most effective antibacterial action (0.05 wt% and 0.2 wt%.) were prepared to be the concentration added to the tested resin composite. Calculations were done to find the required volume of the GONPs solution needed according to the mass of the resin composite. 70 nano-filled resin composite discs were prepared with 10 mm diameter × 3 mm height. 10 resin composite discs were prepared without GONPs incorporation and served as a control (G0). The other 60 resin composite specimens were divided into 2 equal groups (G1& G2) according to the concentration of the loaded nanoparticles in the specimens. Each group was divided into 3 equal subgroups according to the thickness of the resin composite containing GONPs; [T1: GONPs dispersed in the bottom 1 mm of the disc, while the top 2 mm of the disc was of resin composite only. T2: GONPs dispersed only in the bottom 2 mm of the disc and T3: GONPs dispersed in the total thickness of the disc (3 mm)]. ∆E values were calculated using a Vita Easy shade Spectrophotometer.ResultsIncorporation of GONPs into resin composite induced significant color change and among all the 6 experimental groups, G1T1 group (of 0.05 wt% concentration GONPs dispersed only in the bottom 1 mm of the disc) showed a non-significant color change.ConclusionDispersion of GONPs has a detectable effect on the color change of resin composite. Meanwhile, dispersion in low concentration for only the bottom 1 mm thickness of resin composite has an undetectable effect on its color.

Influencia de diferentes opacidades y la técnica de estratificación de resinas compuestas de nanotecnología en la longitud de onda e intensidad de fluorescencia: estudio in vitro

Objective: To evaluate the influence of opacity and the layering technique on the fluorescence of different composite resins. Materials and Methods: Two opacities (enamel and dentin) and the layering technique (enamel + dentin) of the composite resins: Filtek® Z350 and Palfique LX5 were evaluated in vitro. Composite resin discs were fabricated using a preformed matrix of 10 mm diameter and 0.5 mm thick for the single opacity groups and 10 mm thick for the layering technique groups, using 2 layers of 0.5 mm thickness of each opacity (n = 5). Specimens were analyzed using the Raman spectroscopy method. Data were analyzed using the Kruskall-wallis and Mann-Whitney U tests. Results: When evaluating the intensity of fluorescence, no statistically significant difference was found when comparing the layering technique and enamel opacity (p2&gt; 0.05) and an increase in the dentin opacity value for both brands of composite resin. Regarding wavelength, no statistically significant difference was found when comparing the layering technique with enamel opacity and dentin opacity for both Filtek® Z350 and Palfique LX5® composite resins (p2 &gt; 0.05). Conclusions: The fluorescence intensity of the layering technique is similar to enamel opacity for both composite resins. Likewise, the wavelength of the layering technique is similar to the enamel opacity and dentin opacity for both brands.

Effect of various irrigation protocols and antioxidant application on bonding performance of two adhesive systems to coronal dentin.

The aim was to evaluate the effect of different irrigation protocols and antioxidants application on the shear bond strength (SBS) of two different adhesive systems to deep coronal dentin at different temperature. One hundred and twenty human premolar teeth were cut longitudinally in two halves, then the prepared specimens were allocated into four main groups according to the irrigation protocols; Distilled water (control), Sodium hypochlorite (NaOCl) + Ethylenediamine Tetra-acetic Acid (EDTA), and NaOCl + Editronate (HEDP), two subgroups according to irrigation solutions temperature; 4°C and 37°C, two divisions according to grape seed extract (GSE) application (with and without), and two subdivisions according to the applied adhesive systems; OptiBond-All-In-One (OPT) and ScotchBond Universal (SBU). Adhesives were applied in self-etch (SE) mode and resin composite material discs were built. Specimens were kept in distilled water for 24-h at 37°C before SBS testing. Four-way ANOVA and Tukey HSD tests were used for data analysis (α=0.05). 4°C irrigants solution temperature showed the least significant SBS values, distilled water group showed significantly higher SBS values compared to NaOCl + EDTA and NaOCl + HEDP groups respectively. GSE application improved dentin bond strength significantly within each adhesive. Increasing the temperature of the irrigation solutions has significantly enhanced the SBS of coronal dentin. Antioxidants application following different irrigation protocols has improved the SBS. Key words:Irrigation protocols, temperature, bond strength, coronal dentin, antioxidant, adhesive systems.

Comparative Evaluation of Surface Roughness and Colour Stability of Four Different Composite Resins after Application of Desensitising Agents: An In-vitro Study

Introduction: Dentinal Hypersensitivity (DH) is a common clinical condition usually associated with exposed dentinal surfaces. Desensitising agents are regularly used by patients experiencing hypersensitivity, which can affect the physical properties of the existing restorative material. Aim: To evaluate the surface roughness and colour stability of four different types of composite resin restorations after exposure to a desensitising agent. Materials and Methods: The in-vitro study was conducted in the Department of Conservative Dentistry and Endodontics at Ranjeet Deshmukh Dental College and Research Centre, Nagpur, Maharashtra, India from January 2024 to March 2024. Total 56 standardised composite resin discs of size 8×2 mm thickness were prepared using four different types of composites: microhybrid, nanofilled, nanohybrid, and flowable. They were further divided into control and experimental groups based on the application of a desensitising agent, with seven samples in each subgroup. The desensitising agent was applied twice a day for three minutes for one month. Surface roughness was evaluated using a surface profilometer, and colour stability was assessed using a spectrophotometer with the Commision on Ilumination (CIE) L*a*b* formula. The data were analysed using Student’s t-test for pair-wise comparison and One-way Analysis of Variance (ANOVA), with Tukey post-hoc tests for intergroup comparison. Results: The application of a desensitising agent on the samples resulted in a significantly greater effect on the surface roughness of the experimental subgroup than their control counterparts (p≤0.05). Among all groups, the nanofilled group exhibited the lowest surface roughness (0.418±0.047), and the colour change (1.87±0.00) was clinically acceptable. However, the flowable group had the maximum colour change amongst all the other groups (3.16±0.00). Conclusion: Within the limitations of the study, nanofilled composite resin restorative material has minimal surface roughness and colour change after exposure to the desensitising agent. It can be considered the material of choice for restoration in patients with DH.

PEEK surface treatment on surface roughness and bond integrity to composite resin utilizing Er: YAG, Rosebengal activated by PDT, and aluminum trioxide particles

AimsTo evaluate the impact of conditioning protocols, aluminum trioxide (Al2O3), Er:YAG laser (EYL), and Rosebengal (RB), on the surface roughness (Ra) and shear bond strength (SBS) of polyetheretherketone (PEEK) attached to composite restorations. MethodEighty PEEK discs in total were produced and then divided into four groups (n = 20). Group1:Sulfuric acid (SA), Group 2: PDT (RB), Group 3: Al2O3, Group 4 EYL, respectively. The Ra of PEEK discs was evaluated using the surface profilometer. After being luted, the discs were attached to composite resin discs. After that, samples were put to SBS testing on a Universal testing apparatus. A stereo microscope was also used to evaluate the type of breakdown. The data were analyzed using Tukey's test and one-way analysis of variance. ResultsThe SA treated group exhibited the highest Ra. Nevertheless, the RB specimens activated by PDT treatment had the lowest mean Ra score. The group that received the treatment of SA exhibited the highest average score of SBS. In contrast, specimens treated with PDT and activated by RB exhibited the lowest levels of bond fidelity. Cohesive failure emerges as the prevailing kind of fracture within the various groups subjected to testing. ConclusionThe utilization of Al2O3, RB activated by PDT, and EYL shows promise as a viable substitute for Sulfuric acid in enhancing the bond integrity of composite cement and surface roughness in PEEK materials

PEEK Surface Treatment Using Nd: YAG, Riboflavin Activated by PDT, and Alumina Particles on Surface Roughness, Bond Failure, and Bond Integrity to Composite Resin

Aims: Conditioning protocols, Airborne Particles of Alumina (ABP), Neodymium-Doped Yttrium Aluminium Garnet (Nd: YAG) laser, and Riboflavin (RF), were tested on PEEK disc bonded to composite restorations for surface roughness (Ra) and shear bond strength (SBS). Method and Material: Random sampling was used to divide 80 PEEK discs into four groups for surface conditioning. (n = 20). Group 1: Sulfuric acid (SA); Group 2: PDT (RF); Group 3: Alumina particle ABP; Group 4: NYL. Pretreated PEEK discs were measured for Ra using a surface profilometer. They were luted and bonded to composite resin discs. On Universal testing equipment, SBS was tested. Stereomicroscopes analyzed failure type. Data was analyzed using one-way ANOVA and Tukey’s test. Results: The SA-treated group had the highest Ra (1.411 ±0.043 μm). However, PDT (RF) treated tissues had the lowest mean Ra score (1.299 ± 0.019 μm). Regarding SBS, the SA-treated group (11.83±0.82 MPa) had the highest mean score. PDT (RF) (10.23±0.64 MPa) treated specimens showed the lowest bond integrity values. The most common fracture type in all investigated groups is cohesive failure. Conclusion: Airborne alumina, riboflavin, and Nd: YAG laser could replace PEEK sulfuric acid to improve composite cement bond integrity and surface roughness.

Modulation of implants PEEK to composite resin shear bond strength and surface roughness on pre-treatment with contemporary air abrasion techniques vs photodynamic therapy vs conventional diamond grit bur

AimThe chief aim of the study was to determine/equate the surface roughness (SRa) and shear bond strength (BS) of pretreated PEEK discs with contemporary air abrasion techniques, photodynamic (PD) therapy by curcumin photosensitizer (PS) and conventional diamond grit straight fissure bur adhered to the composite resin discs. Material and methodTwo hundred discs of PEEK were prepared of 6 mm × 2 mm × 10 mm dimension. The discs were randomly divided into five groups (n = 40) for treatment, Group I: treatment with deionized distilled water (control group); Group II: PD therapy using curcumin PS; Group III: discs treated and abraded with air-borne particles (ABP) silica (30 μm particle size) modified alumina (Al); Group IV: ABP of alumina (110 μm particle size); and Group V: The PEEK were finished with 600-μm grit size straight diamond cutting bur installed in high speed hand-piece. The surface profilometer was used to evaluate the values of surface roughness (SRa) of pretreated PEEK discs. The discs were luted and bonded to discs of composite resin. The bonded PEEK samples were placed in Universal testing machine to evaluate shear BS. The type of BS failure for PEEK discs pre-treated with five regimes respectively was evaluated under stereo-microscope. The data was statistically analyzed using one-way ANOVA and the comparisons between mean values of shear BS were evaluated by Tukey's test (ρ≤0.05). ResultsThe PEEK samples pre-treated with diamond cutting straight fissure burs displayed statistically significant highest value of SRa values (3.258± 0.785 µm). Similarly, the shear BS was observed to be higher for the PEEK discs pre-treated with straight fissure bur (22.37±0.78 MPa). A comparable difference but not statistically significant difference was observed between PEEK discs pre-treated by curcumin PS and ABP-silica modified alumina (ρ ≥ 0.05). ConclusionPEEK discs pre-treated with diamond grit straight fissure bur displayed highest values of SRa and shear BS. It was trailed by ABP-Al pre-treated discs; whereas the SRa and shear BS values for the discs pre-treated with ABP-silica modified Al and curcumin PS did not show competitive difference.

The impact of the diode laser 940 nm photoactivated bleaching on color change of different composite resin restorations.

The study's main objective was to evaluate as well as compare the impact of diode laser 940 nm and conventional in-office bleaching technique on the color change of different composite resin restorations. A total of ninety composite resin discs (CRDs) were made from Filtek™ Bulk Fill, nanohybrid composite resin Filtek™ Z550 XT Universal Restorative, and flowable composite resin restoration Filtek™ Z350xt Flowable Composite. Group A: (30) CRD for Filtek™ Bulk Fill, group B: (30) CRD for Filtek™ Z550 XT Universal Restorative, and group C: (30) CRD for Filtek™ Z350xt Flowable Composite. A1, B1, and C1: (10 CRD in each group): Control group without bleaching. A2, B2, and C2: 10 CRD in each group bleached with Laser White20 without laser activation. A3, B3, and C3: 10 CRD in each group bleached with Laser White20 and activated by diode laser 940 nm. The color was evaluated using a dental spectrophotometer. One-way ANOVA was utilized for the comparison of the color stability of the CRD. P < 0.05 is regarded as statically significant. Both conventional and diode laser in-office vital tooth bleaching protocols affected the color stability of composite resin restorations. The result demonstrated that bleaching without laser activation produced color change (mean [8.30], standard deviation [SD] (1.95) P [< 0.001]), whereas the bleaching and activation by diode laser produced color change (mean [8.11], SD [1.99], P [< 0.001]). Both types of bleaching protocol affected composite resin restorations' color stability. In all tested materials, color changes after the bleaching protocol were clinically perceptible. The restorations following the bleaching procedure are required to be replaced by clinicians.

Dental and composite resin discoloration induced by different hydraulic calcium silicate-based cements: two-year in vitro assessment.

Few long-term studies assess the discoloration induced by hydraulic calcium silicate-based cement on dental structures. In addition, as far as we know, no long-term study has assessed the discoloration induced by these cement on composite resin. This in vitro study aimed to assess, during a period of two years, the discoloration potential of different hydraulic calcium silicate-based cements (hCSCs) on the enamel/dentin structure and composite resin restoration. A total of 40 enamel/dentin discs were obtained from bovine incisors, and 40 composite resin discs (10 mm in diameter × 2 mm thick) were fabricated. A 0.8 mm-deep cavity was made in the center of each disc and filled with the following hCSCs (n=10): Original MTA (Angelus); MTA Repair HP (Angelus); NeoMTA Plus (Avalon); and Biodentine (Septodont). An initial color measurement was performed (T0 - baseline). After 7, 15, 30, 45, 90, 300 days, and two years, new color measurements were performed to determine the color (ΔE00), lightness (ΔL'), chroma (ΔC'), hue differences (ΔH'), and whiteness index (WID). For enamel/dentin, the ΔE00 was significant among groups and periods (p<0.05). NeoMTA Plus had the greatest ΔE00. The NeoMTA Plus group had the greatest ΔE00 after two years for composite resin. Significant reduction in lightness was observed for all groups after two years (p<0.05). The most significant WID values were observed after 30 days for Biodentine (enamel/dentin) and MTA Repair HP groups (composite resin) (p<0.05). The hCSCs changed the colorimetric behavior of both substrates, leading to greater darkening over time. The Bi2O3 in the Original MTA seems relevant in the short periods of color change assessment.

Pre-Heating of Low-Shrinkage Composite Resins: Effects on Color Stability and Surface Roughness.

Objectives: The present study aimed to investigate the effect of preheating on the color stability and surface roughness of a silorane-based composite resin. Materials and Methods: A total of 44 Filtek P90 composite resin disks, (10mm×1mm), were fabricated using plastic molds and were divided into two groups. In group 2, the composite resin syringes were placed in a thermostatically controlled water bath at 55‒60°C before preparing the disks. After polishing the samples with silicon carbide papers, they were stored in distilled water for 48 hours. Roughness and color parameters were then measured in two stages: immediately after retrieval from distilled water and after 40 days of storage in tea solution. Finally, the differences in roughness and color parameters were recorded. Independent samplet-test and regression analysis were used at a significance level of P<0.05. Results: Based on the findings of the present study, there was no significant difference among the mean ∆E values (P=0.4); however, a significant difference in mean surface roughness (P=0.01) was found between the two groups. Regression analysis showed a significant relationship between the study groups in terms of surface roughness and ΔE values​ (preheated: r2 = 0.73; non-preheated: r2= 0.76). Conclusion: Filtek P90 silorane-base composite showed ΔE>3.3 and surface roughness above 0.2µ under preheated and non-preheated conditions and discoloration increased following preheating.

Adhesion of auto-mixed and manual-mixed self-adhesive resin cements to dentin on exposure to long-term high-altitude pressure

PurposeThe purpose of this study is to test the shear-bond-strengths of auto-mixed and manual-mixed self-adhesive resin cement to dentin on long-term high-altitude pressure.Design/methodology/approachHuman molars were embedded in acrylic resin. Sixty composite resin discs were obtained. The composite resin discs were bonded to dentin using hand-mixed and auto-mixed self-adhesive resin cement. After cementation, the samples were stored in artificial saliva and divided into two subgroups (n = 30), hypobaric pressure and the atmospheric pressure group. The specimen underwent three pressure cycles per day for 100 days. The failure types were evaluated after debonding with scanning electron microscopy. The shear bond strength was tested with Universal Testing Machine. Analysis of variances/Tukey post hoc tests were used for statistical analysis. Groups were also evaluated by the Weibull modulus.FindingsRegardless of hypobaric pressure changes, the highest bond strength was examined in auto-mixed Panavia SA samples. A significant difference was found in both auto-mixed MaxCem EC and hand-mixed RelyX U200 group after exposure to hypobaric pressure compared to the control group.Originality/valueThe luting cement-type, mixing methods of cements and environmental pressure changes significantly influence the bond strengths. Dentists can use auto-mixed self-adhesive resins in patients likely to be exposed to hypobaric pressure.

Assessment of Color Difference of Translucent Zirconia Substructure Veneered Using a Layering Technique with Two Different Veneering Thicknesses: An in-vitro study

Background and objectives. The introduction of zirconia to the dental field created a path for development of new designs and applications, but still, a minimum framework thickness of 0.5 mm with the remaining thickness of the restoration used for building the ceramic veneer was always recommended. This might have possibly affected the final shade of the restoration due to the whitish color of Y-TZP. This in vitro study was designed to assess the color difference of translucent zirconia substructure veneered using a traditional layering technique with two different veneering thicknesses. Methods. A total of twenty translucent Ice zirconia disc samples with standardized dimensions 12 mm in a diameter, 0.5mm in thickness were designed and constructed using zirkonzahn system. The samples were classified into two groups: Group I: (n = 10) veneered by 0.5 mm thickness layering technique using IPS emax Ceram dentin shade A2. Group II (n = 10) veneered by 1 mm thickness layering technique using IPS emax Ceram dentin shade A2. Twenty composite resin discs 12mm in diameter and 5mm in thickness in A3 shade, were fabricated to be bonded to ceramic specimens using Dual-curing translucent rely X Unicem automix Self-Adhesive Resin luting cement. Spectrophotometer was used to measure color parameters L*, a*, b* for all samples. ΔE values were measured to determine color differences between the specimens and the A2 VITA classical shade (target shade). ΔE values were compared with an acceptability threshold (ΔE=3.7). Independent t-test was used to analyze data (P&lt;0.05) in this study and was analyzed using (SPSS) software, version 22. Results. The results showed that veneering thicknesses had a significant effect on the mean (ΔE) Values at P ≤ 0.001. The 0.5 mm veneer thickness showed the higher significant mean color difference (∆E) than the 1.0 mm veneering thickness where the recorded mean (ΔE) Values were (4.15±1.31) (2.65±1.39) respectively at p ≤ 0.001. Conclusions. This study concluded that 1.0 mm veneer thickness was the optimum thickness regarding color matching.

Microhardness Evaluation of Microhybrid Versus Nanofilled Resin Composite After Exposure to Acidic Drinks.

ABSTRACTObjective:To investigate the effect of two acidic agents on microhardness of nanofilled and microhybrid resin composite materials.Materials and Methods:70 resin composite discs (10 mm diameter and 2 mm thick) were prepared from 2 resin composites (35 from each type), nanofilled (Z350XT) and microhybrid (Z250), 3M/ESPE. Ten discs (5 from each group) were used as control (tested at 1 h before immersion). Each group was divided into 3 subgroups (n = 10) according to the storage media: distilled water (control), box-type cola and orange juice. Each subgroup was further subdivided into 2 divisions (n = 5) according to microhardness testing at 24 h and 7days after immersions. Digital Vickers Microhardness Tester (FM-7, Future Tech, Tokyo, Japan) was used to measure surface microhardness with a Vickers diamond indenter. The surface of the specimens received a load of 200 g for 10 seconds. Three indentations not less than 1 mm from each other were placed on the surface of all specimens. Vickers hardness number (VHN) was calculated for each indentation Data were statistically analyzed using one- way ANOVA followed by Newman-keuls tests (P ≤ 0.05).Results:Orange juice showed statistically significantly the lowest VHN mean value (92.7) followed by the Cola group (95.15) then the water group (104.02) compared to the control group (117.4). Microhybrid composite groups showed statistically significant higher VHN mean value (108.1) than the nanofilled composite (100.2). The 7days groups showed statistically significant lower VHN mean value (97.3) than 24h groups (106.6).Conclusions:All storage media reduced hardness of resin composites with orange juice showing the highest reduction in hardness values. Microhybrid is more resistant to degradation than nanofilled composite. Over time, microhardness of resin composites decreased progressively.

The effect of environmental pressure changes on the bond strength between zirconia ceramic and adhesive resin cement

PurposeThe purpose of this study was to investigate the effect of the environmental pressure changes on the bond strength between zirconia ceramics and adhesive resin cement.Design/methodology/approachIn total, 40 rectangular-shaped zirconium-oxide ceramic specimens were prepared. For surface modification, all zirconia specimens were sandblasted with 50 μm alumina particles. The composite resin discs were bonded to modified zirconia surfaces with resin cement. The specimens were divided into four groups; hyperbaric, hypobaric, hyperbaric + hypobaric and control group. The specimen underwent pressure cycles for 30 days. The shear bond strength test was performed by using the universal testing machine, and failures of the debonded samples were examined with scanning electron microscopy and light microscope.FindingsNo significant difference in bond strength was found between the hyperbaric, hypobaric and control groups after 30 days (p > 0.05). However, there was a significant difference in the hyperbaric + hypobaric group compared to the control group (p = 0.022). Also, the Weibull modulus was highest in control group and lowest in the hyperbaric + hypobaric group.Originality/valueBarometric changes due to flying followed by diving may have an adverse effect on the retention of zirconia ceramics. Care should be taken in the selection of materials for dental treatment of people who are exposed to environmental pressure changes.

Effect of Preheating and Vibration on Microhardness and Microleakage of Microhybrid Resin Composite (In Vitro Study)

BACKGROUND: Preheating and sonic vibration are two methods for the treatment of microhybrid resin composites that may effect on their mechanical and physical properties. AIM: This study was conducted to assess the effect of using preheating and sonic vibration on microhardness and microleakage of microhybrid resin composite METHODS AND MATERIALS: For microhardness test, a total of 30 samples of resin composite discs were prepared. Samples were divided into three groups according to the method of treatment of resin composite, controlled group (T0), preheated group (T1), and sonic vibration group (T2). Surface microhardness values were evaluated at baseline and after thermocycling. For microleakage test, a total of 30 Class-V cavities were prepared on the labial surfaces of extracted human anterior teeth. The cavities were then divided into three groups according to the method of resin composite treatment as mentioned before in the microhardness test. All samples were sectioned; then two-dimensional cross-sectional images from each sample. Each cross-sectional image was analyzed using Image J software to quantify interfacial microleakage at the cavity floor. STATISTICAL ANALYSIS USED: Two-way ANOVA analysis was used to test the effects of thermocycling on three groups of each test. One-way ANOVA was used to compare between three different methods of resin composite treatment. RESULTS: For microhardness at baseline revealed that the highest mean value was recorded for the control group, followed by the sonic vibration group meanwhile, the lowest mean value was recorded for the sonic vibration group, followed by preheated group at microleakage test. CONCLUSION: Preheating and sonic vibration of microhybrid resin composite does not improve its microhardness; however, sonic vibration provides better marginal adaptation than the preheating and the conventional methods.