Properties Of Vertebral Cancellous Bone Research Articles

Material properties of human vertebral trabecular bone under compression can be predicted based on quantitative computed tomography

BackgroundThe prediction of the stability of bones is becoming increasingly important. Especially osteoporotic vertebral body fractures are a growing problem and an increasing burden on the health system. Therefore, the aim of this study was to provide the best possible description of the relationship between the material properties of human vertebral trabecular bone measured under the most physiological conditions possible and the bone mineral density (BMD) determined by clinical quantitative computed tomography (QCT).MethodsForty eight cylindric cancellous bone samples with a diameter of 7.2 mm obtained from 13 human fresh-frozen lumbar vertebrae from 5 donors (3 men, 2 women) have been used for this study. After the specimens were temporarily reinserted into the vertebral body, the QCT was performed. For mechanical testing, the samples were embedded in a load-free manner using polymethylmetacrylate (PMMA). The surrounding test chamber was filled with phosphate buffered saline (PBS) and heated to 37 °C during the test. After 10 preconditioning load cycles, destructive testing was performed under axial compression. After determining the fracture site, BMD has been evaluated in this region only. Regression analyses have been performed.ResultsFracture site had an average length of 2.4 (±1.4) mm and a position of 43.9 (±10.9) percent of the measurement length from the cranial end. No fracture reached the embedding. The average BMD at the fracture site was 80.2 (±28.7 | min. 14.5 | max. 137.8) mgCaHA/ml.In summary the results of the regression analyses showed for all three parameters a very good quality of fit by a power regression.ConclusionThe results of this study show that QCT-based bone density measurements have a good predictive power for the material properties of the vertebral cancellous bone measured under near to physiological conditions. The mechanical bone properties of vertebral cancellous bone could be modelled with high accuracy in the investigated bone density range.

Subject-specific mechanical properties of vertebral cancellous bone assessed using a low-dose X-ray device

Objectives According to the inter-individual variability of bone mechanical properties, subject-specific evaluation of the cancellous bone Young's modulus is needed to build finite-element models predicting vertebral strength with accuracy. Relationships based on the density assessed by quantitative computed tomography were proposed. However, quantitative computed tomography is not always suited for the analysis of the whole spine for patients’ follow-up because of the high radiation dose. Hence, this study aims at evaluating the mechanical properties of the vertebral cancellous bone using a low-dose X-ray device. Material and methods Nineteen vertebrae were considered. Biplanar radiographs were made using the low-dose EOS ® system with a dual-energy modality to evaluate antero-posterior and lateral areal bone mineral densities. A cylindrical sample was extracted from each vertebral body and tested until failure to assess the Young's modulus and the ultimate stress of the vertebral cancellous bone. Results and discussion Mechanical properties were significantly related to the EOS ® areal densities. On one hand, the relationships remained less predictive than those based on quantitative computed tomography, but on the other hand, they better predict mechanical properties than previous studies using dual X-ray absorptiometry (clinical gold standard system for density assessment). Conclusion The study shows the feasibility to predict the Young's modulus of the vertebral cancellous bone from the whole vertebral areal bone mineral density (BMD). It gives promising prospects to build finite-element models, including both subject-specific geometry and subject-specific mechanical properties by using a low-dose X-ray device for regions where high radiation doses would limit tomography assessment possibilities.

A method for patient-specific evaluation of vertebral cancellous bone strength: In vitro validation

In the context of osteoporosis, important determinants of the fracture risk are the apparent strength and stiffness of cancellous bone, as well as its brittleness and energy absorption capacity. Standard medical imaging, however, cannot measure these mechanical properties directly. Consequently, an estimation of the risk for fracture is made by correlating relative density or mineral density at a skeletal site with statistics of fracture occurrence, which provides limited and partial indications on fracture risks. A better method for evaluating the patient-specific mechanical properties of cancellous bone is therefore required. In order to asses the mechanical properties of vertebral cancellous bone, we developed a finite element parametric model of lattice trabecular architecture that, in the future, will be suitable for use with bone imaging modalities. The model inputs are apparent morphological parameters (trabecular thickness and trabecular separation) and the bone mineral density. We conducted uniaxial compression tests on 36 canine vertebral cancellous bone specimens (C7 and L1) to validate model predictions of strength and stiffness in vitro. Predictions of strength and stiffness matched the experimental results within relative absolute errors of 17.7% and 12.8%, respectively (average of differences between model-predicted and measured values, divided by the average of measured values). We also employed the model for evaluation of strength and stiffness of human L1 and L5 vertebrae and found mean strength of 1.67 MPa (confidence interval 0.42 MPa) and mean elastic modulus of 190 MPa (confidence interval 50 MPa), which are well within the range of previously reported apparent strength and stiffness properties. The present model can be used to improve medical imaging-based evaluation of the spine in osteoporotic individuals by providing more specific information on the individual bone's susceptibility to fracture once clinical bone scans will be able to provide more reliable measures of trabecular thickness and separation.