Preparation Of Cobalt Nanoparticles Research Articles

Hydrazine metal complexes as a single source in the mechanochemical preparation of metallic magnetic nanoparticles and investigation of their magnetic hyperthermia properties

Ferromagnetic metallic cobalt and nickel nanoparticles were synthesized by intramolecular metal-hydrazine ligand oxidation reduction reaction in basic media and the solid state. Nickel nanoparticles Ni1 and Ni2 are obtained from two complexes, Ni(N2H4)2(C2O4) and Ni(N2H4)2(HCO2)2, respectively. X-ray powder diffraction (XRD) and energy-dispersive X-ray (EDX) data show pure fcc crystal structures of nanoparticles. Scanning electron microscopy (SEM) images revealed both Ni1 and Ni2 nanoparticles have agglomerated sphere morphologies. The crystallite size estimated by using the Scherer method for Ni1 and Ni2 were 18.7 and 6.2 nm. Vibrating sample magnetometer (VSM) data show the coercivity of metallic nickel samples Ni1 and Ni2 are 50 and 153 Oe, respectively. Both nanoparticles cause an increase in the temperature of water under applied alternative magnetic field and showed specific loss power (SLP) of 70 W/g and 104.8 W/g, respectively. The same method is used in preparation of cobalt nanoparticles from two complexes, Co(N2H4)2(C2O4) and Co(N2H4)2(HCO2)2. XRD analysis data show both nanoparticles have hcp crystal structure. SEM images show nanosheet structure with sheet thickness of 10 to 30 nm. Coercivity of Co1 and Co2 nanoparticles obtained by VSM and Hc are 182 and 171 Oe, respectively. In spite of high coercivity in both Co1 and Co2 nanoparticles, the magnetic hyperthermia heating effects are not observed in practice and specific loss power (SLP) is zero.

Preparation of Cobalt Nanoparticles

AbstractThe development of modern chemistry is currently proceeding in several priority areas including investigations focused on the synthesis, stabilisation, and application of transition metal nanoparticles (NPs), which are widely used in physical, chemical, engineering, and biomedical processes. A special place among known transition metal NPs is occupied by cobalt nanoparticles, since they are used for highly important targets, such as creation of new catalysts, magnetic devices, composites, or carriers for drug delivery. The selective preparation of NPs is a difficult task that requires special conditions and has some limitations. In this minireview, we summarise the most successful and most efficient methods for obtaining Co NPs, including chemical and physical aspects of their preparation.

Preparation of cobalt nanoparticles from polymorphic bacterial templates: A novel platform for biocatalysis

Nanoparticles have gathered significant research attention as materials for enzyme immobilization due to their advantageous properties such as low diffusion rates, ease of manipulation, and large surface areas. Here, polymorphic cobalt nanoparticles of varied sizes and shapes were prepared using Micrococcus lylae, Bacillus subtilis, Escherichia coli, Paracoccus sp., and Haloarcula vallismortis as bacterial templates. Furthermore, nine lipases/carboxylesterases were successfully immobilized on these cobalt nanoparticles. Especially, immobilized forms of Est-Y29, LmH, and Sm23 were characterized in more detail for potential industrial applications. Immobilization of enzymes onto cobalt oxide nanoparticles prepared from polymorphic bacterial templates may have potential for efficient hydrolysis on an industrial-scale, with several advantages such as high retention of enzymatic activity, increased stability, and strong reusability.

Mechanochemical Preparation of Cobalt Nanoparticles through a Novel Intramolecular Reaction in Cobalt(II) Complexes

A novel solid state reaction involving a series of cobalt(II) hydrazine-azides has been used to prepare metallic cobalt nanoparticles. The reactions of [Co(N2H4)(N3)2], [Co(N2H4)2(N3)2], and [Co(N2H4)(N3)Cl]·H2O via NaOH, KOH as reactants were carried out in the solid state. These complexes undergo an intramolecular two-electron oxidation-reduction reaction at room temperature, producing metallic cobalt nanoparticles (Co1–Co6). The aforementioned complexes contain cobalt(II) that is an oxidizing agent and also hydrazine ligand as a reducing agent. Other products produced include sodium azide and ammonia gas. The cobalt metal nanoparticles were characterized using X-ray powder diffraction (XRD), scanning electron microscopy (SEM), and vibrating sample magnetometer (VSM). The synthesized cobalt nanoparticles have similar morphologies; however, their particle size distributions are different.

Preparation of cobalt nanoparticles by direct current arc plasma evaporation method

In order to prepare cemented carbides with excellent mechanical properties, the cobalt nanoparticles were prepared by direct current (DC) arc plasma evaporation method for the first time and the effect of three adjustable parameters (current, filling pressure and the pressure ratio of hydrogen to argon (PH2/PAr)) was investigated on the average diameter and the productivity through L16(43) orthogonal experiment in this paper. The crystalline structure, chemical composition, morphology, and particle size distribution of the samples were characterized by transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray fluorescence analysis (XRF) and selected area electron diffraction (SAED), respectively. The results indicated that the cobalt nanoparticles achieved a high purity of 99.933wt.% with a spherical shape, and the cobalt nanoparticles had a cubic crystal structure with a slight shrinkage in the lattice parameters. Both the average diameter and the productivity were increased with the increase of the three parameters, but the average diameter decreased when the value of PH2/PAr varied from 2/3 to 1. Under different technical parameters, the average diameter varied from 28nm to 70nm and the productivity varied from 43g/h to 324g/h.

Sacrificial seed mediated synthesis of copper nanopots by a modified polyol process

A novel modified polyol process has been developed for the synthesis of hollow copper nanopots. Cobalt hydrazine complex was employed for the preparation of cobalt nanoparticles (NPs), which in turn acted as sacrificial seeds for the production of Cu nanopots and nanocups. The reduction of Cu2+ to Cu0 was observed by the colour change from bluish green to dark brownish red. The reaction was followed with the help of a UV–Vis spectrometer. A surface plasmon band at 558 nm indicated the formation of Cu NPs. Chemical characterisation was carried out using inductively coupled plasma optical emission spectrometer and Leco gas analysers, CS-444 and TC-600. Crystal structure was obtained by carrying out X-ray diffraction studies and it showed a face centred cubic structure. Particle size and morphology were obtained from scanning electron microscope. On average, copper nanopots of size 72 nm could be obtained using this method.

Preparation of cobalt nanoparticles from [bis(salicylidene)cobalt(II)]–oleylamine complex by thermal decomposition

[Bis(salicylidene)cobalt(II)] was used as a precursor to prepare cobalt nanoparticles of average diameter 25–35 nm by thermal decomposition. The different combinations of triphenylphosphine and oleylamine were added as surfactants to control the particle size. The resultant samples are characterized by X-ray diffractometer (XRD) and transmission electron microscope (TEM) to depict the phase and morphology. The hysteresis loops of the obtained samples reveal the soft magnet behaviors the enhanced coercivity ( H c) and decreased saturation magnetization ( M s) in contrast to their respective bulk materials.

Preparation of cobalt nanoparticles by hydrogen reduction of cobalt chloride in the gas phase

Cobalt nanoparticles were produced by the hydrogen reduction of cobalt chloride vapor in a multistage tubular aerosol flow reactor. Reaction zone temperature, preheating temperature, mole fractions of CoCl 2 and H 2, and residence time were considered as key process variables for the control of particle size and size distribution. Ranging from 50 to 78 nm in average diameter, cobalt nanoparticles with narrow size distributions were synthesized throughout our experiments. All of the considered process variables affected the particle size and size distribution in the synthesis of cobalt nanoparticles. As the reaction zone temperature and the CoCl 2 mole fraction increased, the average particle diameter increased. But the average particle diameter decreased as the residence time of reactants increased.