Monodisperse Superparamagnetic Nanoparticles Research Articles

Monodisperse superparamagnetic nanoparticles by thermolysis of Fe(III) oleate and mandelate complexes

Monodisperse superparamagnetic iron oxide nanoparticles of controlled size were synthesized by thermal decomposition of organic iron compounds in different high-boiling solvents in the presence of oleic acid and/or oleylamine. The compounds included Fe(III) oleate and mandelate, formed from FeCl3 and the respective acids. The size of the nanoparticles was easily tuned to 8–27 nm by varying the experimental conditions. The nanoparticles were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and magnetization measurements. The hydrophobic coating of the particles was analyzed by thermogravimetric analysis (TGA) and atomic absorption spectroscopy (AAS). To make the particles biocompatible and water dispersible, nontoxic hydrophilic poly(ethylene glycol) derivatives were synthesized and used for phase transfer of hydrophobic particles into water using a ligand-exchange procedure.

The Influence of CuFe2O4 Nanoparticles on Superconductivity of MgB2

Abstract The influence of CuFe2O4 nanoparticle doping on superconducting properties of Fe-sheated MgB2 wires has been studied. The wires containing 0, 3 and 7.5 wt.% of monodisperse superparamagnetic nanoparticles (∼7 nm) were sintered at 650°C or 750°C for 1 hour in the pure argon atmosphere. X-ray diffraction patterns of doped samples showed very small maxima corresponding to iron boride and an increase in the fraction of MgO phase indicating some interaction of nanoparticles with Mg and B. Both magnetic and transport measurements (performed in the temperature range 2–42 K and magnetic field up to 16 T) showed strong deterioration of the superconducting properties upon doping with CuFe2O4. The transition temperatures, Tc, of doped samples decreased for about 1.4 K per wt.% of CuFe2O4. Also, the irreversibility fields Birr(T) decreased progressively with increasing doping. Accordingly, also the suppression of Jc with magnetic field became stronger. The observed strong deterioration of superconducting properties of MgB2 wires is at variance with reported enhancement of critical currents at higher temperatures (determined from magnetization) in bulk MgB2 samples doped with Fe3O4 nanoparticles. The probable reason for this discrepancy is briefly discussed