Microtensile Bond Strength Values Research Articles

Microtensile Bond Strength and Failure Mode of Different Universal Adhesives on Human Dentin

AimThe aim of this study was to compare the microtensile bond strength (µTBS) and failure mode of 4 different universal adhesive systems (UAs) on human dentin. Materials and methodsThe study sectioned the occlusal thirds of 32 human third molars and divided them into 4 groups based on the adhesive system used. Group A: Palfique Universal Bond, Group B: Single Bond Universal, Group C: All-Bond Universal, and Group D: One Coat 7 Universal. The specimens underwent a 10,000-cycle thermocycling ageing process prior to testing (n = 32). Afterwards, 8 beams were obtained per group and subjected to µTBS testing using a digital universal testing machine at a speed of 1 mm/min. The microtensile bond strength values were analysed in Megapascals (MPa), and the failure mode was evaluated using a stereomicroscope. Welch's parametric ANOVA with robust variance and the Games-Howell post hoc test were used for µTBS comparisons, and Fisher's exact test was used to determine the association between adhesive type and failure mode. The significance level was set at P < .05. ResultsGroup D showed a significantly higher µTBS than groups A (P < .001) and B (P < .001), but no significant difference was observed with group C (P= .075). Furthermore, groups B and C showed significantly higher µTBS than group A (P< .001 and P < .001, respectively), but there was no significant difference between groups B and C (P = .132). Additionally, group A exhibited a significant association with an adhesive failure mode (P < .05), whereas groups B, C, and D were significantly associated with a mixed failure mode (P < .05). ConclusionThe One Coat 7 Universal adhesive system showed higher microtensile bond strength values and higher chemical interaction with dentin compared to Palfique Universal Bond and Single Bond Universal. However, no significant differences were observed compared to All-Bond Universal.

Preheating and "snow-plow" composite application technique affect double bond conversion but not bond strength to dentine.

To measure degree of conversion (DC) of a flowable composite, microtensile bond strength (MTBS) to dentine in the snow-plow technique with/without preheating and temperature in the preheated composite. For DC, snow-plow specimens of Filtek Ultimate Flowable (Flow) and Filtek Bulk Fill (Bulk) (3M) were prepared by light-curing composites simultaneously in standardized molds while in control groups light-curing was separate. DC of Flow was measured using micro-Raman spectroscopy. For MTBS, specimens were prepared on dentine of human extracted molars by simultaneous (snow-plow) or separate (control) light-curing. MTBS was measured using a universal testing machine after 24 h and 6 months. Data were analyzed using ANOVA with Tukey's post hoc (α = 0.05). Increased curing time significantly increased DC in snow-plow from 13.4% ± 11.6% (10 s) to 31.8% ± 4.4% (40 s) albeit significantly lower than controls (p < 0.05). Preheated Bulk improved conversion in snow-plow (44.3% ± 1.7%) and control (50.5% ± 2.6%) (p < 0.05). No significant differences occurred in MTBS between groups (p > 0.05). MTBS values ranged between 66.7 ± 8.4 MPa (snow-plow group_21°C_baseline) and 54.1 ± 15.8 MPa (control_21°C_long-term). Temperature in the preheated Bulk dropped to ~38°C after 30 s. Snow-plow technique, irrespective of preheating, resulted in lower DC of Flow than separate light-curing of composite increments. Snow-plow, irrespective of preheating, resulted in similar initial and long-term MTBS to dentine. Clinicians with preference for flowable composite liners in Class II restorations should be aware that the snow-plow technique of simultaneous light-curing of flowable and bulk-fill composite increments affects monomer-to-polymer conversion, albeit no effect on immediate, and long-term bonding to dentine was detected. Preheating sculptable bulk-fill composite improves conversion of the flowable liner in the snow-plow technique but has no detectable effect on bond strength to dentine.

Dentin remineralization using a stimuli-responsive engineered small molecule GSK3 antagonists-functionalized adhesive

ObjectivesTideglusib has shown great performance in terms of dentin regenerative properties. This study aims to evaluate bonding ability, of demineralized dentin infiltrated with polymeric nanoparticles (NPs) doped with tideglusib (TG) (TG-NPs). MethodsDentin conditioned surfaces were infiltrated with NPs and TG-NPs. Bonded interfaces were created and stored for 24 h and then submitted to mechanical, chemical and thermal challenging. The resin-dentin interface was evaluated through a doubled dye fluorescent technique and a calcium chelator fluorophore under a confocal laser scanning microscopy, and by field emission scanning electron microscopy. ResultsDentin surfaces treated with TG-NPs and load cycled produced higher bond strength than the rest of the groups. Immersion of dentin specimens treated with undoped-NPs in collagenase solution attained the lowest microtensile bond strength (MTBS) values. Both porosity and nanoleakage decreased when dentin was infiltrated with TG-NPs, that revealed strong signals of xylenol orange stain at both hybrid layer and dentinal tubules. The presence of NPs, in general, inducted the presence of mineralized interfaces after mechanical loading and thermocycling. ConclusionsNanoparticles doped with tideglusib promoted the highest dentin bonding efficacy among groups, as they facilitated the maximum bond strength values with creation of mineral deposits at the hybrid layer and dentinal walls. Tideglusib enabled scarce porosity, nanoleakage and advanced sealing among dentin groups. SignificanceDoping hydrophilic polymeric NPs with tideglusib, infiltrated in etched dentin represents a reproducible technique to create reparative dentin at the resin-dentin interface, by inducing therapeutic bioactivity.

MICROTENSILE BOND STRENGTH OF UNIVERSAL ADHESIVE TO DENTIN AFTER ER: YAG LASER PRETREATMENT WITH DIFFERENT CONDITIONING MODES - AN IN VITRO STUDY

Adhesion to dentin remains challenging due to its complex nature that prevents complete infiltration of hydrophobic monomer to hydrophilic dentinal substrate. Recently, Er:YAG laser has been used in dentin pretreatment to enhance the bond strength. A deficient hybrid layer is formed following laser etching as it causes thermal damage and collagen denaturation of dentinal substrate. As the results are controversial, attempts are made to modify laser etching technique with respect to energy density, pulse duration and water spray. Thus, the present study aimed to evaluate the influence of Er:YAG laser conditioning of dentin by activation of Chlorhexidine collagen stabilising agent on the bond strength. Samples included 60 freshly extracted premolar which were divided into three groups (n=20) based on the protocol of dentin pretreatment done: Group 1 (Control) - Phosphoric acid etching followed by universal adhesive; Group 2 (Experimental) - Conventional Er:YAG laser dentioning; Group3 (Experimental) - Er:YAG laser dentin conditioning with coronal reservoir of 0.12% Chlorhexidine. Occlusal class 1 cavity was prepared on the samples followed by which dentin conditioning protocol was carried out for the respective groups. Universal adhesive was applied followed by Composite resin restoration. 1000 cycles of Thermocycling was done and the samples were sectioned to obtain microsections. Microtensile bond strength values were obtained by subjecting the specimens to Universal testing machine.Highest microtensile bond strength value was obtained for group 1 followed by group 3 with least value obtained for Group2 with statistically significant values between the groups. (p&lt;0.0001). Within the limitations of the present invitro study, it can be concluded that preetching with phosphoric acid increases the bond strength of universal adhesive to dentin. Laser conditioning of dentin through activation of chlorhexidine provided better bond strength value of universal adhesive when compared to conventional laser dentin conditioning.

In vitro effect of different cleaning procedures of ah plus on microtensile bond strength of immediate or delayed restoration

Aims: Although immediate restoration is recommended after endodontic treatment, delayed restoration is still required in some cases. Also, the presence of the residual endodontic sealer in the pulp chamber may interfere with the adhesive materials and jeopardize the sealability. The purpose of the study was to determine the effect of different sealer residue cleaning methods on dentin bond strength of immediate or delayed endodontic composite restoration. Methods: The occlusal surface of seven freshly extracted human molar teeth without caries were prepared to expose the flat dentin surface. Teeth were randomly divided into six experimental groups according to the cleaning method and restoration timing. Control group was not contaminated with the endodontic sealer and immediately restored (n=10). Cleaning protocols were cotton pellet soaked in saline (CPS) or cotton pellet soaked in 95% ethanol (CPE) or microbrush soaked in 95% ethanol (MBE). After removing of the sealer, a self-etching adhesive system was applied immediately (i) or delayed (d). The microtensile test applied and data were analyzed by Levene's, two way ANOVA and Tukey HSD statistical tests. Results There was no significant difference between the control group and the MBEd and CPSd groups (p&gt;0.05). The bond strength of the CPSi, CPEi, CPEd, MBEi groups was statistically different from control (p&lt;0.05) and there was no significant difference between these groups (p&gt;0.05). Conclusion: CPSd and the MBEd groups showed better microtensile bond strength values than other experimental groups.

Comparison of the Effect of Various Surface Treatments on the Microtensile Bond Strength of Lithium Disilicate Ceramic with Dentin- An In-vitro Study

AIM AND OBJECTIVE: The aim of this study was to evaluate and compare the effect of various surface treatments on the microtensile bond strength of Lithium disilicate ceramic with dentin.&#x0D; MATERIALS AND METHODS: A total of 45 human extracted premolars were obtained for the study. The samples were mounted in dental stone blocks having two “V” shaped notch on mesial and distal side of the mounted tooth. The samples were divided into three groups with 15 samples in each. The GROUP-A Control (without any surface treatment), GROUP-B (air abrasion with Al2O3 particles for 15 seconds) and GROUP-C (laser treatment for 5 seconds). Standardize tooth preparation was done on samples and lithium disilicate crowns were fabricated with a loop on occlusal surface. After surface treatment crowns were luted with self adhesive resin cement and pull out load test was performed in universal testing machine. The data was analysed using one way ANOVA TEST for multiple group comparison followed by Tusky HSD post hoc test. Level of significance was considered at 5% (p-value&lt;0.05).&#x0D; RESULTS: The surface treatment considerably increased the retention of lithium disilicate crowns. The air abrasion group showed the highest microtensile bond strength values. There was significant difference between air abrasion and laser treatment groups.&#x0D; CONCLUSION: It was evident that microtensile bond strength was adequately increased after both the surface treatments (air abrasion with Al2O3 particles and laser treatment) and there was significant increase in bond strength with air abrasion with Al2O3 particles group when compared to laser treatment group.

Sodium carboxymethyl cellulose-based extrafibrillar demineralization to optimize dentin bonding durability.

To investigate the effects of a sodium carboxymethyl cellulose (SCMC)-based extrafibrillar demineralization conditioner on dentin bonding durability and explore the possible mechanisms. The SCMC-based extrafibrillar demineralization conditioner was facilely developed by dissolving SCMC into deionized water at an appropriate concentration. A single layer collagen mineralization/demineralization model was designed to visualize extrafibrillar demineralization in detail. Dentin surfaces of human third molars were conditioned with 3 % SCMC or 37 % phosphoric acid (PA). The morphology, composition, and mechanical properties of conditioned dentin from each group were characterized. To evaluate dentin bonding performance, SCMC- and PA- conditioned dentin were applied with adhesive restoration using the dry-bonding technique. The microtensile bond strength (MTBS), interface nanoleakage, and in situ zymography were measured after 24h of water storage, 10,000 thermocycles, or one month of collagenase aging. The inhibitory effect of SCMC on recombinant human matrix metalloproteinase-2 (rhMMP-2) and cell toxicity were also investigated. After SCMC conditioning, both demineralization of extrafibrillar minerals and retention of intrafibrillar minerals were observed in the single layer collagen model and the dentin ultrastructure. The mechanical properties of SCMC-conditioned dentin were largely preserved. Compared with PA, SCMC conditioning produced greater MTBS values and less nanoleakage expression after aging. Endogenous gelatinolytic activity was suppressed in SCMC-conditioned dentin. In addition to being nontoxic, the inhibition of rhMMP-2 by SCMC was confirmed to be dose-dependent. From the perspective of minimal intervention, the SCMC-based extrafibrillar demineralization conditioner could improve dentin bonding durability, suggesting a promising strategy to extend the service life of adhesive restorations.

Does the Application of Additional Hydrophobic Resin to Universal Adhesives Increase Bonding Longevity of Eroded Dentin?

This paper evaluates the effect of an additional hydrophobic resin coat (extra HL) associated with universal adhesives on sound and eroded dentin and evaluated immediately or after 2 years of water storage to improve the microtensile bond strength (μTBS) and nanoleakage (NL) when compared to the use of universal adhesives only. Sixty-four molars were assigned to eight groups using the following combinations: 1. dentin substrate, including sound and eroded dentin; 2. treatment, including the control and extra HL and storage time (immediately and after two-years of storage). Two universal adhesives (Prime & Bond Active or Scotchbond Universal) were evaluated. Before restoration, half of the teeth were subjected to soft-drink erosion. Composite buildups were bonded; specimens were stored (37 °C/24 h), sectioned into resin–dentin bonded sticks and tested for microtensile bond strength and nanoleakage using SEM (immediately and after two-years of storage). Three-way ANOVA and Tukey’s test (α = 0.05%) were used. In the immediate testing, the application of extra HL did not increase microtensile bond strength values compared with the control group in either substrate (p > 0.05). However, extra HL significantly decreased nanoleakage values when applied to eroded and sound dentin (p = 0.0001). After two years, the application of extra HL produced significantly higher microtensile bond strength and lower nanoleakage values than the control group for both adhesives (p = 0.0001). In all cases, sound dentin showed higher microtensile bond strength and lower nanoleakage values than eroded dentin (p = 0.000001). An extra HL increased the bond strength and reduced nanoleakage in eroded dentin after two-years of storage.

Effects of different universal adhesives and surface treatments on repair bond strength between resin composites.

This study aimed to evaluate the effects of different universal adhesives and surface treatments on the repair bond strength between resin composites. A total of 220 composite samples were divided into three groups according to the adhesive resin to be applied: 1) Scotchbond Universal, 2) G-Premio Bond, and 3) Peak Universal Bond. They were then divided into seven subgroups according to surface treatments (n=10): A) air abrasion, B) air abrasion+silane, C) hydrofluoric acid, D) hydrofluoric acid+silane, E) air abrasion+hydrofluoric acid+silane, F) silane, and G) no surface treatment (negative control). After surface treatment, a repair composite was applied. Samples aged in the thermocycle were subjected to micro-tensile bond strength testing. Cohesive strength values of 10 non-aged composite blocks were used as a positive control. Kruskal-Wallis and one-way ANOVA tests were used for statistical evaluation. Fractured surfaces were evaluated using a scanning electron microscope. In Scotchbond Universal and G-Premio Bond, the mean micro-tensile bond strength value of the no surface treatment subgroup was significantly lower than that of the positive control. All subgroups of Peak Universal Bond showed similar values to the positive control. While Scotchbond Universal and G-Premio Bond required mechanical roughening before adhesive application, Peak Universal Bond did not require any surface treatment. Different universal adhesives may show different repair bonding strengths with different surface treatments. Since achieving a standard in this regard can be associated with many independent factors, clinicians should determine how to apply the adhesive they use most effectively with the most appropriate surface treatment based on their own clinical experience.

Removal of Different Thicknesses Influences the Repair Bond Strength of Dental Resin Composites

This study investigates the repair bond strength of aged resin composites after removing different thicknesses, determine the repair performance using the same or different resin composites and describe the treated surfaces after ageing. Seventy simulated class I cavities were prepared in extracted human third molars were randomly divided into two groups and restored with a nanofilled (Filtek Z350) or a microhybrid (Clearfil APX) composite. Five specimens without ageing in each group acted as a positive control for microtensile bond strength (MTBS) test. After thermocycling, each group was randomly divided into two subgroups: Group RT1, 1 mm removed and Group RT3, 3 mm removed, followed by roughening. Ten specimens in each subgroup were repaired with the same or different composites, and MTBS tests were conducted. The surface roughness (Sa), and water contact angle of the remaining five specimens in each subgroup were measured. In every combination group, Group RT3 showed significantly higher MTBS values than Group RT1, and identical composite was not compulsory for higher repair bond strength. Removal thickness had no significant effect on the Sa in same composite group. In both the Z350 and APX groups, the water contact angle decreased with increasing removal thickness.

PH-dependent delivery of chlorhexidine from PGA grafted mesoporous silica nanoparticles at resin-dentin interface

BackgroundA low pH environment is created due to the production of acids by oral biofilms that further leads to the dissolution of hydroxyapatite crystal in the tooth structure significantly altering the equilibrium. Although the overall bacterial counts may not be eradicated from the oral cavity, however, synthesis of engineered anti-bacterial materials are warranted to reduce the pathogenic impact of the oral biofilms. The purpose of this study was to synthesize and characterize chlorhexidine (CHX)-loaded mesoporous silica nanoparticles (MSN) grafted with poly-L-glycolic acid (PGA) and to test the in vitro drug release in various pH environments, cytotoxicity, and antimicrobial capacity. In addition, this study aimed to investigate the delivery of CHX-loaded/MSN-PGA nanoparticles through demineralized dentin tubules and how these nanoparticles interact with tooth dentin after mixing with commercial dentin adhesive for potential clinical application.ResultsCharacterization using SEM/TEM and EDX confirmed the synthesis of CHX-loaded/MSN-PGA. An increase in the percentage of drug encapsulation efficiency from 81 to 85% in CHX loaded/MSN and 92–95% in CHX loaded/MSN-PGA proportionately increased with increasing the amount of CHX during the fabrication of nanoparticles. For both time-periods (24 h or 30 days), the relative microbial viability significantly decreased by increasing the CHX content (P < 0.001). Generally, the cell viability percentage of DPSCs exposed to MSN-PGA/Blank, CHX-loaded/MSN, and CHX-loaded/MSN-PGA, respectively was > 80% indicating low cytotoxicity profiles of experimental nanoparticles. After 9 months in artificial saliva (pH 7.4), the significantly highest micro-tensile bond strength value was recorded for 25:50 CHX/MSN and 25:50:50 CHX/MSN-PGA. A homogenous and widely distributed 50:50:50 CHX-loaded/MSN-PGA nanoparticles exhibited excellent bonding with the application of commercially available dentin adhesive.ConclusionsA pH-sensitive CHX release response was noted when loaded in MSN grafted PGA nanoparticles. The formulated drug-loaded nanocarrier demonstrated excellent physicochemical, spectral, and biological characteristics. Showing considerable capacity to penetrate effectively inside dentinal tubules and having high antibacterial efficacy, this system could be potentially used in adhesive and restorative dentistry.

Effect of remineralizing agents on resin-dentin bond durability of adhesive restorations: An in vitro study

Aim: To prolong the clinical success and durability of bonded restorations, hybrid layer stabilization is crucial for better adhesion between the resin and tooth substrate. The aim of this in vitro study was to assess the ability of self-assembling peptide (curodont protect) and a remineralizing agent (MI paste plus) in promoting biomimetic remineralization for stabilization of the hybrid layer to improve the resin-dentin bond durability. Materials and Methods: Standardized mesio-occlusal (MO) and disto-occlusal (DO) cavities were prepared on 60 mandibular molars. Teeth were randomly allocated to different groups and after acid etching, half of the MO cavities (n = 30) of dentin were treated with curodont protect and another half (n = 30) with MI paste plus. Half of the DO cavities (n = 30) were pretreated with chlorhexidine, whereas the other half did not receive any dentin pretreatment before placing adhesive restoration. Half of the samples from each group (n = 15) were subjected to thermomechanical load cycles. Immediate and after aging bond strengths were estimated using a universal testing machine, and the type of bond failure was assessed under a scanning electron microscope. Data obtained in megapascals were analyzed by one-way analysis of variance and Tukey’s multiple post hoc test with the significance level set as P ≤ 0.05. Results: Immediate bond strength values were significantly high for the control group and low for the MI paste plus group (P = 0.002). Significant differences were not observed between the curodont protect and chlorhexidine (P = 0.0514) treated groups. In all groups, bond strength values were decreased significantly after thermomechanical cyclic (TMC) loading (P = 0.0001). Adhesive type fractures were reported more in failure mode analysis. Conclusion: All groups exhibited reduced microtensile bond strength values after aging. The dentin treated with chlorhexidine, curodont protect, and MI paste plus produced more durable bonding than the control group.

Bonding Performance of a Hydrophilic Amide Monomer Containing Adhesive to Occlusal and Cervical Dentin.

This study aimed to evaluate the bonding performance of a new one-step self-etching adhesive system containing a novel hydrophilic amide monomer. Clearfil Universal Bond Quick (CUB) and Clearfil Megabond 2 (CMB) were used as the one-step and two-step adhesive systems, respectively. Flat dentin surfaces of human premolars were exposed using #600 SiC (silicon carbide) and bonded with the respective adhesives of each system. The teeth were sectioned to obtain beams (1 mm × 1 mm) after 24 h of water storage. The mean bond strength and standard deviations (MPa) on an occlusal surface were as follows: CUB: 45.9 ± 19.7 and CMB: 67.9 ± 25.3. The values for cervical ones were CUB: 56.0 ± 20.3 and CMB: 67.6 ± 16.0, respectively. In both conditions, the microtensile bond strength (μTBS) value was lower than that of CMB. As seen during the microscopic observation, no adhesive failure was observed after μTBS testing because CUB formed a firm and tight adhesive interface.

Effects of Zn-Doped Mesoporous Bioactive Glass Nanoparticles in Etch-and-Rinse Adhesive on the Microtensile Bond Strength.

The purpose of this study was to assess the effects in the dentin bond strength of dental adhesives (DAs) and biological effects using zinc (Zn)-doped mesoporous bioactive glass nanoparticles (MBN-Zn). Synthesized MBN and MBN-Zn were characterized by scanning electron microscopy (SEM), X-ray diffraction and the Brunauer, Emmett and Teller (BET) method. The matrix metalloproteinases (MMP) inhibition effects of DA-MBN and DA-MBN-Zn were analyzed. The microtensile bond strength (MTBS) test was conducted before and after thermocycling to investigate the effects of MBN and MBN-Zn on the MTBS of DAs. The biological properties of DA-MBN and DA-MBN-Zn were analyzed with human dental pulp stem cells (hDPSCs). Compared with the DA, only the DA-1.0% MBN and DA-1.0% MBN-Zn exhibited a statistically significant decrease in MMP activity. The MTBS values after thermocycling were significantly increased in DA-1.0% MBN and DA-1.0% MBN-Zn compared with the DA (p < 0.05). It was confirmed via the MTT assay that there was no cytotoxicity for hDPSCs at 50% extract. In addition, significant increases in the alkaline phosphatase activity and Alizarin Red S staining were observed only in DA-1.0%MBN-Zn. These data suggest the 1.0% MBN and 1.0% MBN-Zn enhance the remineralization capability of DAs and stabilize the long-term MTBS of DAs by inhibiting MMPs.

Microtensile Bond Strength Between Self-Adhesive Resin Cements and Resin Based Ceramic CAD/CAM Block

Purpose: The objective of this study is to evaluate and compare the microtensile bond strength (μTBS) of four different self-adhesive resin cements to a resin-based ceramic CAD/CAM block, at the baseline, and after subjecting them to 5,000 thermo-cycles.Materials and Methods: Four self-adhesive dual-cured resin cements; G-CEM LinkAce (GC EUROPE, Leuven, Belgium), RelyX U200 (3M ESPE, Seefeld, Germany), Maxcem Elite (Kerr, CA, USA), TheraCem (Bisco, Schaumburg, USA) were applied to Cerasmart CAD/CAM blocks (GC EUROPE, Leuven, Belgium). CAD/CAM blocks were sectioned into sticks and subjected to µTBS tests at 24 hours, and the other half were subjected to tests after 5000 thermo-cycles. The data were tested by one-way variance analysis (p&lt;0.05). Results: The highest bond strength values were observed in TheraCem, followed by G-CEM LinkAce and RelyX U200, respectively (p&lt;0.05). At the baseline, G-CEM LinkAce, RelyX U200, and Maxcem Elite showed statistically similar results. After 5,000 thermal-cycles, a significant decrease was observed in the bond strength values of G-CEM LinkAce (p&lt;0.05). Conclusion: Between the adhesive cements used in the study, TheraCem showed the highest micro-tensile bond strength values both in the baseline (24h) results, and after the 5,000 thermal-cycle aging procedures.

Modified Microtensile Bond Strength of Glass Ionomer to Composite Resin Using Universal Adhesive in Self-etch and Total-etch Modes

Background: Glass Ionomer Cements (GICs) are frequently used as base or liner before the application of restorative materials. The success of this approach depends on the bond strength of GICs to composite resin. Objectives: This study to assess the modified microtensile bond strength of glass ionomer to composite resin using universal adhesive in self-etch and total-etch modes. Methods: Samples were fabricated of resin-modified GIC (RMGIC) and conventional GIC(CGIC) (6 x 1 x 1 mm), and were randomly divided into 8 groups. Clearfil SE Bond and G-Premio universal adhesive in self-etch and total-etch modes were used according to the manufacturers’ instructions. Z250 composite was applied over the GIC (12 x 1 x 1 mm), and light-cured. The microtensile bond strength was measured using a universal testing machine. The samples in each group were evaluated under an electron microscope to determine the mode of failure. Data were analyzed using one-way ANOVA and Tukey’s test. Results: The microtensile bond strength of RMGI used with Clearfil SE Bond was significantly higher than that of other groups (6.57±1.15 MPa) (P&lt;0.05). The maximum and minimum microtensile bond strength values of CGIC after applying the bonding agents were recorded after using G-Premio total-etch mode (1.34±0.77 MPa) and SE Bond in total-etch mode(1.18±79 MPa), respectively. Conclusion: Application of of G-Premio in both modes did not show any significant different bond strength in both glass ionomers. The bond strength of RMGIC was higher than that of CGIC, and the maximum bond strength of RMGI was achieved by the use of SE Bond.

The effects of 45S5 bioactive glass and Er:YAG Laser on the microtensile bond strength of fluorosed teeth.

This vitro study aimed to evaluate the effects of 45S5 bioactive glass (BAG) and Er:YAG laser as desensitization treatments on the microtensile bond strength (MTBS) of fluorosed teeth. The 120 noncarious fluorosis were to obtain superficial dentin, being classified into four groups according to the Thylstrup and Fejerskov Index (TFI). Specimens from each group were randomly divided into five subgroups. After fluorosed teeth hypersensitivity models were established, the following pretreatments were applied on dentine surface: Subgroup 1: deionized water (Control); Subgroup 2: BAG; Subgroup 3: Er:YAG laser; Subgroup 4: BAG + Er:YAG laser, and Subgroup 5: Er:YAG laser + BAG. One sample was randomly selected from each subgroup for scanning electron microscope (SEM). The remaining samples were bonded with composite resin by Adper Single Bond 2 adhesive. Then water bath at 37°C for 24 hr. After 5,000 thermocycling, MTBS was tested and fracture mode was analyzed. The difference of MTBS between BAG group and Control group was found statistically significant (p < .05) in fluorosis. The Er:YAG laser + BAG group showed lowest MTBS values in fluorosis. In conclusion, the pretreatment of BAG might be beneficial to the adhesive of fluorosed teeth. Er:YAG laser desensitization alone or using BAG first and then Er:YAG laser desensitization might not affect the adhesive of fluorosed teeth, while Er:YAG laser desensitization followed by the pretreatment of BAG would be not conducive to the adhesive of fluorosed teeth.

Polyphenol-enriched extract of Arrabidaea chica used as a dentin pretreatment or incorporated into a total-etching adhesive system: Effects on bonding stability and physical characterization.

The aim of this paper was to evaluate the physical properties and the long-term bond strength of a 2.5% polyphenol-enriched extract of Arrabidaea chica (AC) incorporated into both the phosphoric acid and the primer of a three-step total-etch adhesive, or into an aqueous solution as a dentin pretreatment. Fifty dentin surfaces received the treatments (n=10): CON (control) - application of the three-step adhesive system (Adper Scotchbond Multipurpose, 3M ESPE); WAT - distilled water used as a pretreatment after dentin etching and before application of the adhesive system; ACPA - AC incorporated into the phosphoric acid; ACW - dentin pre-treatment with AC incorporated into an aqueous solution after etching; ACP - AC incorporated into the primer. Microtensile bond strength tests were performed after 24h, 6 and 12months of storage. Slices from the resin-dentin interface were obtained for scanning electron microscopy analysis of the hybrid layer. Degree of conversion of AC incorporated into the primer was evaluated. The particle size, polydispersity index and zeta potential of all the solutions prepared by incorporating AC (phosphoric acid, primer and distilled water) were measured by dynamic light scattering, which brought about changes after incorporation. Degree of conversion of the primer was not affected after incorporating AC. ACP showed lower microtensile bond strength values than the other groups. Bond strength decreased after 6months of storage, stabilizing at the 12-month evaluation. Therefore, use of AC incorporated into the primer led to lower bond strength values, since AC modified the physical properties (particle size, polydispersity index and zeta potential) of the primer, but did not change the degree of conversion. Application of AC as a dentin pretreatment did not affect bond strength or the micromorphological characteristics of the hybrid layer.

Adhesion procedures for CAD/CAM indirect resin composite block: A new resin primer versus a conventional silanizing agent

PurposeThe purpose of this study was to evaluate the effectiveness of both a resin primer containing methyl methacrylate (MMA) and a silanizing agent on bonding to indirect resin composite blocks, using two types of build-up hybrid resin composites. MethodsSHOFU BLOCK HC (Shofu) specimens were blasted with alumina, after which one of two surface treatments was applied: CERA RESIN BOND (Shofu, the Silane group) or HC primer (Shofu, the MMA group). Resin composites made using either Solidex Hardura (SDH, Shofu) or Ceramage Duo (CMD, Shofu) were built up and micro-tensile bond strength (μTBS) values were measured after storage in water for either 24h or 6 months (n=24 per group). The fracture surfaces after μTBS measurements and the resin block/build-up resin interfaces were observed by scanning electron microscopy (SEM). ResultsThe bond strength of the Silane/SDH group significantly decreased after 6 months (p<0.001), whereas in the MMA group there was no significant loss after 24h or 6 months (p=0.99). In the CMD group, the bond strength after 6 months was significantly lowered in both the Silane group (p<0.001) and the MMA group (p<0.001), but the latter still showed greater adhesion. SEM images demonstrated that the matrix resin was partially destroyed at the fracture surfaces of the MMA group and fracture surface unevenness was observed. ConclusionsA primer containing MMA produced stronger bonding to CAD/CAM resin even after long-term aging compared to a silane treatment.

Influence of different surface treatments and universal adhesives on the repair of CAD-CAM composite resins: An in vitro study

Statement of problemThe repairability of computer-aided design and computer-aided manufacturing (CAD-CAM) composite resins might be adversely affected by the high degree of matrix polymerization that occurs during their manufacturing process. However, information on their repairability is lacking. PurposeThe purpose of this in vitro study was to evaluate the microtensile bond strength of CAD-CAM composite resins subjected to simulated repair procedures by using varying surface treatments and universal adhesives. Material and methodsFour different CAD-CAM blocks (Brilliant Crios, Lava Ultimate, Shofu Block HC, and Vita Enamic) were thermocycled (5000 times, 5/55 °C) and divided into 4 groups according to the surface treatment: control, 9% hydrofluoric acid etching, aluminum oxide airborne-particle abrasion, and tribochemical silica airborne-particle abrasion. After surface treatments, the surface roughness was measured with a nanoindenter and further examined with scanning electron microscopy. After the application of 3 different universal adhesives (Clearfil Universal Bond, Prime&Bond Universal, and Single Bond Universal), the specimens were subjected to a simulated repair process with composite resin. Bonded specimens were cut into 1 mm2 beams, and microtensile bond strength values were determined until failure at a crosshead speed of 0.5 mm/min. The bond strength data were analyzed with 3-way analysis of variance, and surface roughness data were analyzed with 2-way analysis of variance tests. Pairwise analyses were performed with the Tukey test (α=.05). ResultsAll surface treatments effectively improved repair microtensile bond strength values compared with the control (P<.05). Aluminum oxide airborne-particle abrasion had similar mean bond strength values compared with tribochemical silica airborne-particle abrasion (P>.05). Among the CAD-CAM blocks treated with hydrofluoric acid etching, Vita Enamic had the highest mean bond strength values. The highest mean microtensile bond strength repair values with the highest cohesive failure rates were found with the silane-containing universal adhesive (Single Bond Universal). ConclusionsSurface treatment with aluminum oxide airborne-particle abrasion and tribochemical silica airborne-particle abrasion produced successful repair results for aged resin nanoceramics, whereas hydrofluoric acid etching can be used for aged hybrid ceramic repair. Silane-containing universal adhesive reported increased bond strength. Application of universal adhesive after surface treatment is recommended to increase repair strength.