Internal Stress Corrosion Cracking Research Articles

Imidazoline behavior as corrosion inhibitor in the electrochemical characterization of SCC behavior of an API X70 steel exposed to brine solution

Abstract The effect of concentration of an organic imidazoline as inhibitor on internal stress corrosion cracking (SCC) behavior of an API X70 pipeline steel exposed to a brine solution was studied. The SCC process using simultaneously the slow strain rate stress test (SSRT) and electrochemical measurements was performed. Fracture surface analysis and secondary cracking were observed through a scanning electron microscopy (SEM). According to SEM fractography and SSRT results, the steel showed high SCC susceptibility with a brittle fracture and several secondary cracks without addition of inhibitor, whereas the addition of inhibitor to brine solution was effective to increase the SCC resistance of steel at concentrations of inhibitor of 50 and 100 ppm. A further addition of concentration of inhibitor had a negative effect on the mechanical properties of the steel. Electrochemical measurements results are in accordance with the SCC susceptibility, indicating that corrosion inhibitor film suppressed the anodic and cathodic reactions increasing the resistance to SCC until concentration of 100 ppm. Further addition of inhibitor aggravated the localized corrosion due to local desorption of inhibitor molecules. The Hilbert–Huang transform (HHT) analysis revealed the contribution of different corrosion process contained in the electrochemical current noise (ECN) signals at several inhibitor concentrations.

Analysis of the Physicochemical, Mechanical, and Electrochemical Parameters and Their Impact on the Internal and External SCC of Carbon Steel Pipelines.

The review presented herein is regarding the stress corrosion cracking (SCC) phenomena of carbon steel pipelines affected by the corrosive electrolytes that comes from external (E) and internal (I) environments, as well as the susceptibility and tensile stress on the SCC. Some useful tools are presented including essential aspects for determining and describing the E-SCC and I-SCC in oil and gas pipelines. Therefore, this study aims to present a comprehensive and critical review of a brief experimental summary, and a comparison of physicochemical, mechanical, and electrochemical data affecting external and internal SCC in carbon steel pipelines exposed to corrosive media have been conducted. The SCC, hydrogen-induced cracking (HIC), hydrogen embrittlement, and sulfide stress cracking (SSC) are attributed to the pH, and to hydrogen becoming more corrosive by combining external and internal sources promoting cracking, such as sulfide compounds, acidic soils, acidic atmospheric compounds, hydrochloric acid, sulfuric acid, sodium hydroxide, organic acids (acetic acid, mainly), bacteria induced corrosion, cathodic polarization, among others. SCC growth is a reaction between the microstructural, chemical, and mechanical effects and it depends on the external and internal environmental sources promoting unpredictable cracks and fractures. In some cases, E-SCC could be initiated by hydrogen that comes from the over-voltage during the cathodic protection processes. I-SCC could be activated by over-operating pressure and temperature at flowing media during the production, gathering, storage and transportation of wet hydrocarbons through pipelines. The mechanical properties related to I-SCC were higher in comparison with those reviewed by E-SCC, suggesting that pipelines suffer more susceptibility to I-SCC. When a pipeline is designed, the internal fluid being transported (changes of environments) and the external environment concerning SCC should be considered. This review offers a good starting point for newcomers into the field, it is written as a tutorial, and covers a large number of basic standards in the area.

Effect of non-conventional heat treatment of API X60 pipeline steel on corrosion resistance and stress corrosion cracking susceptibility

PurposeThe purpose of this paper is to study the effect of heat treatment (HT) applied to an API X60 steel in corrosion resistance and stress corrosion cracking (SCC) susceptibility through slow strain rate tests (SSRT) in NS4 solution and congenital water (CW) to assess external and internal SCC, respectively.Design/methodology/approachAPI X60 steel was heat treated at a temperature of 1,200°C for 30 min followed by water quenching. Specimens from this steel were machined according to NACE TM 198. SSRT were performed in a constant extension rate tests (CERT) machine at room temperature at a strain rate of 1 × 10–6s–1. For this purpose, a glass cell was used. Corrosion behavior was evaluated through polarization curves (PCs).FindingsThe SCC index obtained from SSRT indicates that the steel heat treated could be susceptible to SCC in CW and NS4 solution; the mechanism of SCC was hydrogen embrittlement. Thus, CW may promote the SCC phenomenon in pipelines. HT improves the steel corrosion resistance. Higher corrosion rate (CR) was observed when the steel is exposed to CW. The corrosion process in X60 steel shows that the oxidation reaction in the anodic branch corresponds to an activation process, and the cathode branches reveal a diffusion process.Originality/valueThe purpose of the heat treatment applied to X60 steel was to generate a microstructure of acicular ferrite to improve the corrosion resistance and SCC behavior.