High Isostatic Pressure Research Articles

Layered composite magnetic refrigerants for hydrogen liquefaction

Many exciting effects resulting from the coupling of magnetic sublattice with a magnetic field, may be exposed by changing the field. One such phenomenon is the magnetocaloric effect, which is characterized by the absorption or emission of heat in response to changes in the external magnetic field. Magnetic refrigeration based on the magnetocaloric effect has emerged as an attractive alternative to conventional cooling technology that relies on gas compression and expansion. It is not only more efficient and environmentally friendly, but it can also be implemented across a broad temperature range, from ultra-low to a few hundred Kelvin temperatures. One of the areas where magnetic cooling can have a significant impact is hydrogen liquefaction. Hydrogen is one of the most promising candidates for clean energy sources, but it must be liquefied to facilitate storage and transportation, which requires cooling it down to ∼20 K. The ideal magnetic refrigerant should exhibit consistent magnetocaloric properties across the entire operating temperature range of a cooler. This paper presents novel three-layer composite magnetic refrigerants that provide a uniform magnetocaloric response over a 30 K temperature range. The selected initial HoNi2, DyNi2, and TbNi2 magnetic intermetallic compounds with a Laves phase structure exhibit large magnetocaloric properties in the temperature range of 13–37 K. The composite composition of 23.56 wt% HoNi2 + 18.21 wt% DyNi2 + 58.23 wt% TbNi2 optimized for 2 T magnetic field change, was determined through numerical approach. The composites are manufactured using spark plasma sintering (SPS) and innovative high-isostatic-pressure (HIP) synthesis. The results of isothermal entropy change derived from magnetization data for a 2 T magnetic field change indicated 4.7 J/kgK (47.2 mJ/cm3K) and 4.4 J/kgK (44.2 mJ/cm3K) in the temperature range of approx. 13–42 K for composites after SPS and SPS + HIP processes, respectively. Despite the sample subjected to HIP showing slightly lower results, the entropy change is nearly uniform over the 30 K temperature range due to enhanced atomic diffusion between neighboring compounds, as confirmed by microscopic studies. Such a uniform magnetocaloric response in ∼30-K temperature range has never been observed before in layered refrigerants. By utilizing the innovative high-isostatic-pressure synthesis technique, we have paved the way to high-performing magnetic composite materials that can be used in cryogenic magnetic coolers operating over a broad temperature span, expanding the possibilities of what can be achieved and laying the foundation for cost-effective, clean hydrogen energy.

Investigation of Layered Structure Formation in MgB2 Wires Produced by the Internal Mg Coating Process under Low and High Isostatic Pressures.

Currently, MgB2 wires made by the powder-in-tube (PIT) method are most often used in the construction and design of superconducting devices. In this work, we investigated the impact of heat treatment under both low and high isostatic pressures on the formation of a layered structure in PIT MgB2 wires manufactured using the Mg coating method. The microstructure, chemical composition, and density of the obtained superconductive wires were investigated using scanning electron microscopy (SEM) with an energy-dispersive X-ray spectroscopy (EDS) analyzer and optical microscopy with Kameram CMOS software (version 2.11.5.6). Transport measurements of critical parameters were made by using the Physical Property Measurement System (PPMS) for 100 mA and 19 Hz in a perpendicular magnetic field. We observed that the Mg coating method can significantly reduce the reactions of B with the Fe sheath. Moreover, the shape, uniformity, and continuity of the layered structure (cracks, gaps) depend on the homogeneity of the B layer before the synthesis reaction. Additionally, the formation of a layered structure depends on the annealing temperature (for Mg in the liquid or solid-state), isostatic pressure, type of boron, and density of layer B before the synthesis reaction.

The effect of boron on the structure and lattice parameters of diamond single crystals

Boron doped diamonds (BDD) with boron concentration above 1019 at./cm3, grown under conditions of high isostatic pressure by the temperature gradient method, were studied by Transmission Electron Microscopy methods, EELS analysis and X-ray diffraction analysis. It was shown that boron is distributed unevenly in the grown crystal. It was found that in places of maximum boron content, interplanar distances d111 increase from 0.206 to approximately 0.2065 nm. Parallel bands were discovered, the boundaries of which are fragments of the intermediate carbon phase (ICP-phase). Numerous twins along the {111} plane, as well as fragments of rhombohedral 9R phase, were discovered.

The influence of the HIP process on the microstructure, critical temperature and critical current density of double-doped (with Dy2O3 + C, and Tb2O3 + C) MgB2 bulk compounds

ABSTRACT We present the results of the irreversibility field (B irr ), critical temperature (T c), and magnetic critical current density (J cm) for cylindrical samples encapsulated in carbon and doped with 1-3 at% dysprosium and terbium oxides. All samples were analyzed microstructurally by using a scanning electron microscope (SEM) and X-ray diffraction (XRD). The influence of annealing temperature and time and high isostatic pressure on J cm was investigated. Our results show that double-doped (C + Tb2O3 and C + Dy2O3) and low isostatic pressure heat treatment (0.1 MPa) decrease the T c by about 0.5 K compared to the undoped MgB2 (0.1 MPa). The magnetic measurements show that double-doped and heat treatment under high isostatic pressure (HIP - 1 GPa) leads to a decrease in T c of about 2.5 K compared to the undoped MgB2 sample after the HIP process. Our results show that the HIP process slightly increases J cm at 4.2 K and 20 K, and improves J cm at 30 K in undoped MgB2 samples. Furthermore, our results show that the HIP process and double-doped significantly increase J cm at 4.2K and decrease J cm at 30K. Our results indicate that the HIP process can produce high field and low-temperature pinning centers in doubly doped MgB2 materials.

Impact of rare earth oxides metal (Dy, Tb, Er, Eu, Sm) admixtures on the structure, morphology, pinning centers and critical parameters of MgB2 materials manufactured by ambient pressure sintering and hot isostatic pressure processes

In our paper, we present the results of the structural, morphological and critical parameters of MgB2 cylindrical materials doped with Dy2O3, Tb2O3, Er2O3, Eu2O3 and Sm2O3. The materials were annealed under low and high isostatic pressures at 800 °C for 1 h in an argon atmosphere. Our results show that the HIP process significantly increases the density of MgB2 materials modified by the RE2O3 additive from 1.05 to 2.4 g/cm3. Scanning electron microscope (SEM) images indicate that the HIP process removes voids from the MgB2 material. The results indicate that the HIP process slightly affects the formation of REB4 and REB6 and does not affect the process of RE substitution for Mg. Further SEM results show that the morphologies of samples annealed at low isostatic pressure with Dy2O3, Tb2O3 and Er2O3 doping are completely different from those of samples with Eu2O3 and Sm2O3 doping. The magnetic measurements indicate that RE2O3 doping and annealing under low isostatic pressure slightly increases the critical temperature (Tc) and decreases the irreversible magnetic field (Birr). On the other hand, thermal treatment under high isostatic pressure with an admixture of RE2O3 lead to a greater increase in Tc and a decrease in Birr. Further magnetic measurements show that RE2O3 doping and annealing under low isostatic pressure mainly increase the magnetic critical current density (Jmc) at 4.2 K–30 K in low magnetic fields. Additional results indicate that high isostatic-pressure annealing of the RE2O3-doped MgB2 material significantly increases Jmc in low magnetic fields and decreases Jmc in high magnetic fields. Our results indicate that the Eu2O3 admixture most effectively increases Tc and Jmc and creates the large amount of the REB6 phase. It is as the only admixture that increases Birr after the HIP process and yields the smallest MgB2 grains.

Influence of bending and heat treatment under high isostatic pressure on synthesis reaction and transport critical current density in isotopic IMD Mg11B2 'wind and react' coils

We show for the first time the results for small coils, which were wound with unreacted magnesium diboride (MgB2) wires with nano-amorphous isotopic boron (11B) by using combined internal magnesium (Mg) diffusion (IMD) and hot isostatic pressing (HIP) techniques. The small coils with a diameter of 20 mm or 10 mm were annealed under low (0.1 MPa) and high (1.1 GPa) isostatic pressure. The 10 mm coils annealed under high isostatic pressure of 1.1 GPa had significantly increased critical temperature (Tc), irreversible magnetic field (Birr) and transport critical current density (Jtc), with significantly accelerated Mg diffusion and improved homogeneity of the Mg11B2 material. Moreover, our findings show for the first time that the bending of the unreacted IMD Mg11B2 wires significantly affects the synthesis reaction under the low and high isostatic pressure. Our findings also show for the first time that diffusion of Mg during heat treatment under high isostatic pressure is completely different than during heating under low isostatic pressure. Mg diffusion under low isostatic pressure annealing is mainly dependent on the heat treatment temperature, bending diameter and 11B layer density. This Mg diffusion is related to the simultaneous formation of the superconducting phase. However, the diffusion of Mg under high isostatic pressure heat treatment is mainly dependent on the isostatic pressure, 11B layer density and Mg state (liquid or solid). Our results indicate that liquid Mg is first pushed into the 11B layer by high isostatic pressure and then a superconducting phase is formed.

Extraction of bioactive compounds from Peruvian purple corn cob by high isostatic pressure

The purple corn cob is an agro-industrial by-product that contains high-value bioactive compounds, which makes its use attractive for the development of extraction processes. The aim of this research was to extract the bioactive compounds from the purple corn cob by high isostatic pressure at different processing temperatures. Pressures of 0.01 MPa, 250 MPa, 450 MPa and 650 MPa for 3 minutes and at temperatures of 25 °C, 45 °C and 65 °C were used. High pressure extraction was compared with conventional extraction (2.5 h at 25°C). The purple corn cob extract obtained by isostatic processing at 650 MPa and 65 °C presented high antioxidant activity and content of bioactive compounds, unlike the conventional extraction of 2.5 h and 65 °C (p < 0.05). However, it did not show a significant difference with the extract obtained at 450 MPa and 45 °C (p > 0.05). Seven different anthocyanins were identified by liquid chromatography in the extracts obtained by high isostatic pressure (650 MPa at 65 °C) and hydroalcoholic maceration (2.5 h at 65 °C), mainly cyanidin-3-glucoside, pelargonidin-3-glucoside and peonidin-3-glucoside, and their respective malonyl derivatives. The high isostatic pressure increased the extraction of bioactive compounds by more than 50% and obtained them in shorter times, thus appearing as a new alternative, and eco-friendly method for the extraction of bioactive compounds from plant tissues.

Influence of Sintering Conditions and Nanosilicon Carbide Concentration on the Mechanical and Thermal Properties of Si3N4-Based Materials.

In the work, silicon nitride ceramics (Si3N4) and silicon nitride reinforced by nano silicon carbide particles (Si3N4-nSiC) in amounts of 1-10 wt.% were investigated. The materials were obtained using two sintering regimes: under conditions of ambient and high isostatic pressure. The influence of the sintering conditions and the concentration of nanosilicon carbide particles on the thermal and mechanical properties was studied. The presence of highly conductive silicon carbide particles caused an increase in thermal conductivity only in the case of the composites containing 1 wt.% of the carbide phase (15.6 W·m-1·K-1) in comparison with silicon nitride ceramics (11.4 W·m-1·K-1) obtained under the same conditions. With the increase in the carbide phase, a decrease in the densification efficiency during sintering was observed, which caused a decrease in thermal and mechanical performance. The sintering performed using a hot isostatic press (HIP) proved to be beneficial in terms of mechanical properties. The one-step high-pressure assisted sintering process in the HIP minimizes the formation of defects at the sample surface.

Пористость консолидированных методом газовой экструзии компактов из никелевых нанопорошков

The method of hot gas extrusion differs from other methods of metal pressure treatment in that the processed material is subjected to intense plastic deformation by extrusion under conditions of high isostatic pressure of inert gas and heating in the area of plastic deformation. The method makes it possible to process powder materials, while inevitably there is a need to control mechanical properties by controlling porosity and pressure inside the pores. The paper presents a method for calculating the pressure inside the pores from the minimum size of the closed pore. The pore pressure was evaluated on materials obtained by the consolidation of nickel nanopowders by hot gas extrusion. Quantitative processing of the material cross-section view images obtained by scanning electron microscopy showed that the minimum pore size is 220 nm. The formula for calculating the pore pressure is derived from the formula for calculating the critical pore radius. It takes into account the external impact pressure (the gas pressure during the extrusion process was equal to 400 MPa), the surface tension coefficient and the yield strength of nickel (at the extrusion start temperature of 910 °С), as well as the minimum pore radius. The proposed method for calculating the pressure inside a closed pore will allow us to evaluate the mechanical properties of materials obtained by various methods of powder metallurgy.

Two-body wear resistance and fatigue survival of new Y-TZP and ATZ ceramics made with a new slip-casting method

BackgroundDental zirconium oxide restorations are milled from pre-sintered blocks or disks which are produced either with high isostatic pressure (HIP) or, simpler, a slurry technique. The objective was to perform a fatigue test and an in vitro wear simulation of two ceramics, yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP) ceramic and a hybrid zirconium oxide-aluminum oxide ceramic, (ATZ) both produced either the classical way using high isostatic pressure (HIP, control) or with a slurry technique. Materials and methodsTen discs/group were subjected to a cyclic biaxial fatigue test using a staircase approach under water at 37 °C in a dynamic universal testing machine. The 2-body wear test was performed on eight lapped 12 mm thick cylindrical samples subjected to spherical (ø 6 mm) leucite ceramic antagonists in a CS-4 chewing simulator at 49 N force and 0.7 mm lateral movement for 600 k cycles and 4167 thermal cycles (5–55 °C). Volumetric wear was calculated based on laser-scanned surfaces. Selected samples of both tests were viewed in SEM. ResultsAll the ceramic specimens produced using the HIP method survived up to 1.2 M cycles with the maximum load of the equipment (1000 N) loading the specimens up to 1527 MPa. The fatigue limit stress at 1.2 M cycles for the Slurry ATZ samples was 946 MPa. For the Slurry Y-TZP samples the fatigue limit stress at 1.2 M cycles was 658 MPa. At 600 k cycles, all zirconium oxide ceramics showed no measurable wear and had a highly polished appearance. The leucite ceramic antagonists wear developed in a linear way. There was no difference between the materials produced with the slurry and the HIP process. ATZ ceramic produced significantly more wear than 3Y- TZP ceramic. ConclusionsThe HIP method provided higher fatigue strength than the Slurry manufacturing method. All HIP ceramics surpassed the limit threshold (1527 MPa) of the testing machine. The tested ceramics did not show any measurable wear but had worn the leucite reinforced glass ceramic antagonists for a considerable amount.

High Critical Current Density in the Textured Nanofiber Structure in Multifilament MgB2 Wires Made by the Powder-In-Tube (PIT) Technique.

We show that the structure of multifilament MgB2 wires made by the powder-in-tube (PIT) method can be texturized by annealing the structure under high isostatic pressure. Our results show that we obtained continuous fibers with a uniform diameter of 250 nm in all 36 filaments, a small grain size of approximately 50 nm and a high density of the superconducting material. These results contribute to a significant improvement in the critical current density in high magnetic fields, e.g., 100 A/mm2 at 14 T and 4.2 K.

Design and Application of a Rock Porosity Measurement Apparatus under High Isostatic Pressure

Rock porosity is a key physical parameter at room temperature and pressure that plays an important role in evaluating reserves of oil and natural gas. Research on rock porosity spans over a hundred years. However, in situ porosity under a high isostatic pressure has not been adequately explored, and the experimental conditions for measuring porosity remain unclear. To investigate the feasibility of porosity measurement under a high isostatic pressure and the optimal choice of experimental conditions for this, we design an experimental apparatus that can achieve isostatic pressure up to 200 MPa to fit the relationship between the void volume of a given sample and the drop in gas pressure in an empty standard chamber. The effect of experimental parameters, such as the initial gas pressure at the inlet, the time needed for the gas to reach equilibrium, and the time needed for vacuuming, on the porosity experiment was examined. A series of porosity experiments under different isostatic pressures of up to 200 MPa were carried out with this apparatus. The results quantitatively verify the degree to which porosity is related to isostatic pressure.

Effect of Heat Treatments under High Isostatic Pressure on the Transport Critical Current Density at 4.2 K and 20 K in Doped and Undoped MgB2 Wires.

Annealing undoped MgB2 wires under high isostatic pressure (HIP) increases transport critical current density (Jtc) by 10% at 4.2 K in range magnetic fields from 4 T to 12 T and significantly increases Jtc by 25% in range magnetic fields from 2 T to 4 T and does not increase Jtc above 4 T at 20 K. Further research shows that a large amount of 10% SiC admixture and thermal treatment under a high isostatic pressure of 1 GPa significantly increases the Jtc by 40% at 4.2 K in magnetic fields above 6 T and reduces Jtc by one order at 20 K in MgB2 wires. Additionally, our research showed that heat treatment under high isostatic pressure is more evident in wires with smaller diameters, as it greatly increases the density of MgB2 material and the number of connections between grains compared to MgB2 wires with larger diameters, but only during the Mg solid-state reaction. In addition, our study indicates that smaller wire diameters and high isostatic pressure do not lead to a higher density of MgB2 material and more connections between grains during the liquid-state Mg reaction.

The significant influence of packing density of unreacted Mg+2B mixture and heat treatment conditions on some of critical parameters for MgB2/Fe wires

Our research show that the higher packing density of the unreacted material (Mg +2B) by 8%, especially for Mg in the solid state, allows to eliminate the large number of large voids (20 µm), improves the homogeneity and density of the MgB2 superconducting material, allows to obtain a greater number and longer lengths of connections between MgB2 grains, eliminates the formation of the intermetallic phase (iron borides), allows to obtain MgB2 grains of a uniform size and shape, increase irreversible magnetic field (Birr), critical temperature (Tc) and upper magnetic field (Bc2). Research show that spherical grains significantly reduce the number of inter-grain connections in the material with low and high density of unreacted material and allows to obtain the more superconducting phase. Research shows that MgB2 grains with a plate-like and rectangular shape allow to obtain more connections between the grains. Studies show that thermal treatment under high isostatic pressure does not allow to obtain the large amount of superconducting phase for the unreacted material of low density. Moreover, studies show that the high packing density of unreacted material and thermal treatment under high isostatic pressures (0.8 GPa and 1.1 GPa) allow to obtain a large amount of superconducting phase even for Mg in the solid state. Additionally, studies points that heat treatment under medium isostatic pressure (0.3 GPa) significantly reduce Birr and Bc2. Our results are important for long superconducting wires made by using the powder-in-tube (PIT) technique. Because they indicate that the higher packing density of the unreacted material (Mg +2B) will allow to obtain a the superconducting material with greater homogeneity and density, and improve the critical parameters e.g. coils.

Influence of Amorphous Boron Grain Size, High Isostatic Pressure, Annealing Temperature, and Filling Density of Unreacted Material on Structure, Critical Parameters, N-Value, and Engineering Critical Current Density in Mgb2 Wires.

Our results show that a lower density of unreacted Mg + B material during an Mg solid-state synthesis reaction leads to a significant reduction in the quantity of the superconducting phase and lowers the homogeneity of the superconducting material. It also significantly reduces the irreversible magnetic field (Birr), critical temperature (Tc), upper magnetic field (Bc2), engineered critical current density (Jec), and n-value, despite high isostatic pressure (HIP) treatment and the use of nanoboron in the sample. Our measurements show that samples with large boron grains with an 8% higher density of unreacted Mg + B material allow better critical parameters to be achieved. Studies have shown that the density of unreacted material has little effect on Birr, Tc, Bc2, Jec, and the n-value for an Mg liquid-state synthesis reaction. The results show that the critical parameters during an Mg liquid-state synthesis reaction depend mainly on grain size. Nanoboron grains allow for the highest Birr, Tc, Bc2, Jec, and n-values. Scanning electron microscopy (SEM) images taken from the longitudinal sections of the wires show that the samples annealed under low isostatic pressure have a highly heterogeneous structure. High isostatic pressure heat treatment greatly improves the homogeneity of MgB2.

Bacillus spore germination at moderate high pressure: A review on underlying mechanisms, influencing factors, and its comparison with nutrient germination.

Spore-forming bacteria are resistant to stress conditions owing to their ability to form highly resistant dormant spores. These spores can survive adverse environmental conditions in nature, as well as decontamination processes in the food and related industries. Bacterial spores may return to their vegetative state through a process called germination. As spore germination is critical for the loss of resistance, outgrowth, and development of pathogenicity and spoilage potential, the germination pathway has piqued the interest of the scientific community. The inhibition and induction of germination have critical applications in the food industry. Targeted germination can aid in decreasing the resistance of spores and allow the application of milder inactivation procedures. This germination-inactivation strategy allows better maintenance of important food quality attributes. Different stimuli are reported to trigger germination. Among those, isostatic high pressure (HP) has gained increasing attention due to its potential applications in industrial processes. However, pressure-mediated spore germination is extremely heterogeneous as some spores germinate rapidly, while others exhibit slow germination or do not undergo germination at all. The successful and safe implementation of the germination-inactivation strategy, however, depends on the germination of all spores. Therefore, there is a need to elucidate the mechanisms of HP-mediated germination. This work aimed to critically review the current state of knowledge on Bacillus spore germination at a moderate HP of 50-300 MPa. In this review, the germination mechanism, heterogeneity, and influencing factors have been outlined along with knowledge gaps.

Электронномикроскопический анализ высокого разрешения конусных углеродных нанотрубок, формируемых в аппарате высокого изостатического давления

Carbon nanotubes with “herringbone” layers structure synthesized in high isostatic pressure apparatus were studied by High Resolution Transmission Electron Microscopy (HRTEM) methods. Seven different values of semi-apex angles of graphene layers were observed in different nanotubes. It is shown that semi-apex angles approximately equal to 5, 15, 25 и 35 can be regarded only to the scroll structure of the nanotubes, while 10, 20 and 30 can be regarded to both scroll either nested graphene layers curved to cones due to the embedding of the pentagon’s to them. Thus, the observation of all (seven) of these values of semi-apex angles testifies presence of scroll nanotubes in the sample under study, though it does not exclude presence of nested-cone nanotubes.

Superior engineering critical current density obtained via hot isostatic pressing of MgB2 wires manufactured using nano-amorphous isotopic boron

The effects of heat treatment temperature, time and isostatic pressure on the grain connectivity and superconducting properties of Mg11B2 wires prepared using nano-amorphous isotopic boron powder (11B) have been investigated. The article presents detailed studies of the Mg11B2 material structure of the wires using scanning electron microscope (SEM). Heat treatment at low and high temperature for different annealing time and isostatic pressure does not create an internal macro-defect that disrupts connectivity in the Mg11B2 superconducting wires. Our study shows that dense longitudinal superconducting layers are formed at high annealing temperature of 800 °C for 60 min. Formation of dense longitudinal superconducting layers under high isostatic pressure (HIP) allow improved grain connectivity and high density of pinning centers and as a result, high engineering critical current density, Jec, at 4.2 K has been achieved. Also, high upper critical field (Bc2) and high irreversible magnetic field (Birr) were obtained using HIP process while superconducting transition temperature (Tc) was not significantly affected. Better grain connectivity obtained using high annealing temperature and long annealing time under low isotopic pressure leads to Jec enhancement at high magnetic fields at 20 K. Our results show that the annealing temperature of 800 °C for 60 min under isostatic pressure of 1 GPa yields the required Jec of 25 A/mm2 and 50 A/mm2 for ITER applications in magnetic fields of 8 T and 7 T, respectively. The promising results obtained in this work could pave the way for designing low activation superconducting Mg11B2 wires to be considered for next generation fusion magnets.

High transport critical current density in high magnetic fields at Mg11B2 wires made with nano 11B

In this work, we show the transport current results and structural analysis for Mg11B2 wires for the first time made with high purity, nano-size and amorphous boron 11 (11B). Irradiation has a weak effect on the MgB2 material made of 11B. Therefore, it is important for future applications to fusion reactors. This type of reactor will produce clean and cheap energy. We report for first time that high-fields pinning centers and dense layered structure lead to high transport critical current density (Jtc) in high magnetic fields. This allows to obtain highest Jtc value in the world (100 A/mm2 at 4.2 K and 8.5 T). We show that lack of dense layered structure and high-fields pinning centers lead to lower Jtc in high magnetic fields. Our research shows that high isostatic pressure (HIP) promotes high-field pinning centers.

Influence of high isostatic pressure and thermal pasteurization on chemical composition, color, antioxidant properties and sensory evaluation of jabuticaba juice

Jabuticaba (Plinia jaboticaba) is a Brazilian fruit rich in phenolic compounds, but its seasonality and high perishability hampers widespread consumption, which opens up the opportunity to develop technological processes and innovative products that meet the demands of the consumer. In this study, we evaluated the influence of high isostatic pressure (HIP; 600 MPa/25 °C/5 min) compared to thermal pasteurization (TP; 82 °C/2 min) on color parameters, chemical composition, sensory evaluation, and antioxidant properties of jabuticaba juice during 30 days of cold storage. HIP and TP increased total color difference and sensory acceptance decreased during cold storage. Both treatments were effective in ensuring microbiological stability during 30 days of cold storage. HIP was responsible for an increase in phenolics (35%), monomeric anthocyanins (103%), antioxidant capacity (99%), and the relative intensity by a heatmap analysis of compounds of biological interest in relation to untreated jabuticaba juice. Finally, HIP and TP's application showed to be promising processing technologies to develop stable jabuticaba juices with high-added value.