Electromagnetic Wave Absorption Performance Research Articles

Preparation and electromagnetic wave absorption of compressible graphene aerogels

In this study, a developed easy-operation method was adopted to generate ultralight and compressible graphene aerogels by using graphene oxide and ammonia. By changing the process parameters, such as reduction temperature, reducing agent content and ammonia concentration, the variation laws of the density and pore size of aerogels were obtained, which aided in realizing the controllable preparation of aerogel structures. The prepared graphene aerogel has good compressive performance, and its density can reach 5.26 mg/cm3. Although it was repeatedly compressed 200 times under a load that was 4000 times as large as its own weight, it maintained its structural integrity and mechanical properties. An ideal model of three-dimensional graphene aerogel was constructed, and the electromagnetic wave absorption performance was simulated using the Computer Simulation Technology (CST) Microwave Studio software. The results showed that when the thickness, pore size and height of the sheet were 1.4, 5 and 14 mm, respectively, an optimal electromagnetic wave absorption effect of −31.08 dB could be obtained. Furthermore, the effects of thickness, pore size and height of the sheet on the electromagnetic wave absorption performance are revealed, which provide a reference for the structural design of aerogels with both compressibility and electromagnetic wave absorption performance.

Bridging microscopic phase and defect manipulation with macroscopic core-sheath-shell structure for polarization-dominated electromagnetic wave absorption

Manipulating phases and defects brings boundless vitality to the design of electromagnetic wave (EMW) absorption (EMA) materials. However, current manipulations often prioritize the improvement in the overall EMA performance without distinguishing the effects of individual polarizations. Therefore, the design of EMA materials is result-oriented and limited by reliance on semi-empirical rules. Herein, we synthesized carbon cloth (CC)@MoS2@carbon nanotubes (CNTs) (CMSC) by self-assembly of MoS2 on CC, followed by in-situ growth of CNTs through high-temperature annealing. This synthesis process not only created a hierarchical core-sheath-shell structure consisting of an MoS2 intermediate sheath and a CNT outer shell but also introduced tunable vacancy defects and phases (2 H and 1 T). Density Functional Theory calculations revealed an enhanced carrier influx from the CNTs into the 2 H/1 T MoS2 due to the substantial difference in work function between the 1 T and 2 H phases, which promoted charge redistribution and subsequent polarization at defect sites and interfaces in CMSC. Therefore, defect-induced and interfacial polarizations dominated the EMW-attenuation mechanisms for CMSC, distinguishing it from CC@MoO2@CNTs, where conduction loss predominated. Owing to these enhanced polarizations and core-sheath-shell structure, CMSC exhibited a minimum reflection loss of −43.9 dB at 2.1 mm, even with a filler ratio of 3 wt%. This study highlights the potential for designing and tailoring polarization-dominated EMA materials through the manipulation of defects and phases.

Doped Porous Carbon Spheres with Controllable Vesicle Structure: Preparation and the Effects of Pore Size on Electromagnetic Wave Absorption Properties.

This work reports on the preparation of uniform vesicle-structural carbon spheres doped with heteroatoms of N, P, and S, with the pore sizes strictly controlled by the hard templates of monodisperse submicron SiO2 spheres. The uniformly doped vesicular carbon microspheres are obtained in three steps: Stöber hydrolysis for the SiO2; in situ polymerization for the immobilization; and alkaline etching after carbonization. The size of the vesicles can be easily adjusted by regulating the particle size of the submicron SiO2 spheres, which has a significant effect on its electromagnetic wave (EMW) absorption performance. Compared with microspheres with pore sizes of 180 and 480nm, when the vesicle aperture is 327nm, with only 5.5wt.% filling load and 1.9mm thickness, the material shows the best EMW absorption behavior with the effective absorption bandwidth (EAB) covers the entire Ku band (6.32GHz) and the minimum reflection loss (RLmin) of -36.10dB, suggesting the optimized pore size of the microspheres can significantly improve the overall impedance matching of the material and achieve broadband wave absorption. This work paves the way for the enhancement of EMW absorption properties of porous material by optimizing the pore size of uniform apertures while maintaining their composition.

Rice straw-inspired tunable multi-hollow channel parallel carbon fibers for enhanced electromagnetic wave absorption

The pure carbon materials are constrained in practical applications due to their inability to meet the requirements of broadband and strong absorption. To address this challenge, inspired by the parallel connection structure of hollow straw, this study successfully fabricated a multi-hollow channel parallel carbon fibers (MHCFs) structure by electrospinning and carbonization template methods. Compared with the traditional non-porous carbon fibers (CFs) structure (MHCFs-0), MHCFs-0.2 exhibit more excellent electromagnetic wave (EMW) absorption performance. It exhibits an impressive 5.59 GHz effective absorption bandwidth (EAB) at 1.8 mm. The reflection loss (RL) of MHCFs-1 reaches −52.64 dB. This remarkable enhancement in performance can be attributed to the channel structure, which can effectively introduce air, optimize impedance matching, and greatly promote polarization effects (including interface polarization and dipole polarization). It is worth noting that the integration of computer simulation technology (CST) with material structure design in this study opens up new ideas for the preparation of absorbing materials and the design of micro-nano structures, holding significant practical implications.

Molecular Intercalation‐Induced Two‐Phase Evolution Engineering of 1T and 2H‐MS2 (M = Mo, V, W) for Interface‐Polarization‐Enhanced Electromagnetic Absorbers

AbstractPolarization at interfaces is an important loss mechanism for electromagnetic wave (EMW) attenuation, though the motion behavior of carriers in interfaces composed of different types of conductors has yet to be investigated. Tuning the phase structure of transition metal dichalcogenides (TMDs) MS2 (M = Mo, V, W) by organics small molecule intercalation to achieve the modulation of interfacial types is an effective strategy, where 1T‐MS2 exhibits metallic properties and 2H‐MS2 has semiconducting properties. To exclude the contribution of the intrinsic properties of TMDs materials, three TMDs (MoS2, VS2, and WS2), which also possess phase transitions, are investigated. Among them, the 1T‐MS2 composite exhibits excellent EMW absorption performance under the synergistic effect of interfacial polarization and conduction loss. 1T‐MoS2/MOF‐A exhibits the best EMW absorption performance with an RLmin of −61.07 dB at a thickness of 3.0 mm and an EAB of 7.2 GHz at 2.3 mm. The effectiveness of the modulation of the interfacial polarization using 1T‐phase and 2H‐phase MS2 is demonstrated, which is important for the analysis of the carrier motion behavior during the interfacial loss.

Cross‐Scale Synergistic Manipulation of Dielectric Genes in Polymetallic Sulfides from Micropolarization to Macroconductance Toward Wide‐Band Microwave Absorption

AbstractRecently, the design and development of efficient microwave absorbents by facile engineering approaches have attracted much attention. Particularly, some unique structures caused by cross‐scale design are promising in enhancing the absorbing capability toward microwave irradiation. Herein, the cross‐scale design strategy is implemented to enhance the electromagnetic wave absorption performance of polymetallic sulfides (PMS). In PMS, the dipole polarization unit is optimized, and the distribution of electronic states is improved by doping Ti atoms; Meanwhile, the MS/M3S4 homogeneous hetero‐phases interfaces is constructed in PMS using a phase separation strategy; and the conductivity of PMS is modulated by the addition of acetylene black (ACET). The cross‐scale synergy of microwave absorption leads to a significant enhancement of the microwave absorption (MA) performance of PMS/ACET composites. The optimal reflection loss value of Ti‐LES with 10% ACET addition reaches −55.49 dB and the effective absorption bandwidth reaches 6.73 GHz. The 17.5% ACET‐conditioned Ti‐HES achieves a reflection loss of −37.2 dB at a low frequency of 4.8 GHz. This study not only provides a novel strategy for the development of new broadband MA materials but also validates a new idea for the multi‐scale synergistic optimization of MA materials.

Surface engineering strategy for MXene to tailor electromagnetic wave absorption performance

The emerging two-dimensional material, Ti3C2Tx MXene, has attracted significant attention in the realm of electromagnetic wave absorption owing to its exceptional inherent conductivity and distinctive microstructure. However, similar to other conductive materials, MXene encounters the challenge of impedance mismatch, thereby impeding the electromagnetic wave absorption capability in single-component MXene materials. In this study, a molten chlorine-salt method was employed to gain MXene samples with varying surface-chlorine/oxygen (Cl/O) ratios by surface engineering. Notably, among these samples, Cl/Ni-MX-6 exhibited an impressive minimum reflection loss value of −45.72 dB (1.6 mm) and an effective absorption bandwidth of 3.44 GHz (1.3 mm). This study revealed that increasing the etchant content enhances the delamination effect of MXene and leads to adjust Cl/O ratio. Importantly, the modulation of −Cl/O surface functional groups can limit the electronic conductivity, while the number and species of different kinds of surface dipoles will control the polarization effect, ultimately optimizing the electromagnetic wave absorption performance of pure MXene. These insights contribute to ongoing efforts aimed at enhancing the performance of MXene-based materials in the field of electromagnetic wave absorption as well as get a better understanding of the electromagnetic loss mechanism.

Design of CuS composite carbon-based Ni Al-LDH multifunctional phase change composite with electromagnetic shielding performance and heat storage capacity

CuS-based composites are widely used in the fields related to photothermal energy storage and electromagnetic shielding and are excellent candidates for composites with phase change materials. To meet the requirements of micro-integration and electromagnetic resistance of electronic products and optimize the thermal management of electronic products, it is necessary to prepare new flexible composite phase change materials. In this paper, through the design of MPC@Ni Al-LDH/CuS double-layer structure, two-step vacuum filtration method is used, and the highly conductive materials CuS and MPC are introduced into the manufacture of PCM films. With the help of Ni Al-LDH, flame retardancy is introduced. The electromagnetic wave absorption performance is enhanced, and the existence of nano-cellulose (CNF) makes the film have excellent mechanical properties. Ni Al-LDH/MPC and CuS substrates with stable and high mechanical properties are prepared by ultrasonic treatment. According to scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform-infrared spectroscopy (FT-IR), X-ray photoelectron spectroscopy (XPS), differential scanning calorimetry (DSC) and thermogravimetry (TG) characterizations, PEG successfully entered the MPC/CuS skeleton by vacuum filtration, and flexible phase change composite bilayers (MLPC) were obtained. Due to the synergistic effect of structure and components, the obtained composite film has many different excellent functions. Specifically, when MPC@Ni Al-LDH is 15 wt%, the phase transition enthalpy, thermal conductivity, electromagnetic shielding, and electrical conductivity are 146.8 J/g, 1.07 W/m·K, 38.8 dB and 126.4 S/m, respectively. The 3600 s infrared temperature measurement results show that the sample has stable thermal properties. Due to the presence of CuS, when MPC@Ni Al-LDH is 5 wt%, its absorbance can be kept at 1.51 L/(g·cm), and its photothermal conversion efficiency can reach 90.6 %. The MPC/CuS structure in the composite film provides many heat transfer channels, which reduces the phonon scattering in the heat transfer process and significantly increases thermal conductivity. Therefore, this multifunctional flexible phase change film can be used in photothermal conversion devices and for thermal management of electronic equipment, and it has broad application prospects in wearable equipment design due to its excellent electromagnetic shielding ability and infrared thermal stealth ability.

MOFs-derived 3D flower-like Y2O3/C microspheres with efficient electromagnetic wave absorption properties

Y2O3 has emerged as a promising material for electromagnetic wave (EMW) absorption due to its excellent dielectric properties. However, the inherent insulating nature and single loss mechanism limit its absorption performance. Research on the microstructure modulation and component regulation of Y2O3-based absorbers remains relatively unexplored. In this work, Y2O3/C composites with flower-like architectures were synthesized for the first time via a metal-organic framework (MOFs) templating method. The effects of pyrolysis temperature on the microstructure, phase composition, and EMW absorption performance of the Y2O3/C composites were systematically investigated. At a pyrolysis temperature of 800 °C, the flower-like Y2O3/C microsphere exhibited optimal EMW absorption performance. The minimum reflection loss (RL) of pristine Y2O3 was only −4.75 dB, while the Y2O3/C composite achieved a minimum RL of −51.77 dB and a maximum effective absorption bandwidth of 4.32 GHz. Moreover, by simply adjusting the matching thickness, the optimal sample exhibited strong absorption (RL < −30 dB) over a wide frequency range of 4–18 GHz. The incorporation of carbon effectively neutralized the insulating nature of Y2O3, thereby optimizing the impedance matching. The synergistic effects of multiple loss mechanisms, including polarization loss, resistance loss, and interfacial polarization, facilitated substantial EMW attenuation. This study provides a promising strategy for the design and fabrication of high-performance rare-earth oxide EMW absorbers with tunable morphologies and properties.

Broadband electromagnetic wave absorption properties of RGO cement-based composite

In this study, a cement-based composite was prepared using reduced graphene oxide (RGO) as a raw material via an ethanol liquid-phase mixing pre-dispersion process. The microstructure of cement-based composites with varying RGO contents was discussed, and a systematic investigation was conducted into the electromagnetic wave absorption (EWA) performance of RGO-cement composites within the frequency range of 2–18 GHz. The results indicate that the RGO content significantly impacts its wave absorption performance. Notably, at an RGO content of 3.0 wt%, the wave absorption performance experiences substantial enhancement. For instance, the minimum reflection loss (RLmin) of −48.33 dB at 8.9 GHz with a coating thickness of 2.6 mm is achieved, while an effective absorption bandwidth (EAB) of 5.02 GHz is attained with a thickness of only 1.6 mm, covering nearly the entire Ku-band. The incorporation of high specific surface area RGO into cement materials results in abundant interface polarization losses and additional electromagnetic wave transmission paths, effectively boosting the EWA performance. Consequently, these materials exhibit significant potential for applications in the field of electromagnetic wave shielding.

Ultra-wideband electromagnetic wave absorption property with bimetallic Co6W6C/carbon

Binary dielectric materials, particularly carbide/carbon composites, have garnered considerable attention for their promising electromagnetic wave (EMW) absorption property. In this work, bimetallic carbide and carbon composite (Co6W6C/C) was successfully prepared through hydrothermal method and pyrolysis process. Characterization results reveal the growth of Co6W6C nanoparticles on two-dimensional carbon nanosheets. The mass ratio of glucose (C6H12O6) to Co6W6C was found to significantly impact the EMW absorption performance. When 150 mg C6H12O6 and 100 mg CoWO4 were added, the CWCC-2 composite exhibited an ultra-high effective absorption bandwidth of 7.49 GHz (10.51–18 GHz). In the far-domain circumstance, the highest radar cross-section acreage reached 21.24 dB m2. The exceptional EMW absorption performance can be attributed to the synergistic effects of impedance matching, electrical losses, and magnetic losses. The Co6W6C/carbon composite, synthesized through a facile approach, showcases a broad electromagnetic wave absorption bandwidth, paving the way for a breakthrough in materials science with wide-band and high-efficiency absorption capabilities.

Screw dislocation growth defects enhancing electromagnetic wave absorption performance of GdB6

In this study, a purity of up to 98.36 wt. % GdB6 with screw dislocation growth morphology were successfully fabricated using an in-situ reaction approach. The terraced-like structure of the GdB6 enhanced the interfacial polarization and multiple interface scattering of the electromagnetic waves. As a result, the as-obtained high purity GdB6 powder presented superior electromagnetic wave absorption performance. The minimum reflection loss value can be −49.24 dB at the frequency of 13.12 GHz with a thin matching thickness of 1.44 mm. In addition, the widest effective absorption bandwidth can be up to ∼4 GHz (14–18 GHz) with a thin matching thickness of 1.25 mm. The remarkable electromagnetic wave absorption performance of GdB6 ceramics could be attributed to conductance loss and polarization loss enhanced by the screw dislocation growth defects, as well as synergistic effects with magnetic loss. The as-obtained GdB6 with synergistic dielectric loss and magnetic loss is to be a novel single-phase with excellent electromagnetic wave absorbing material, which will pave the way on the investigation of rare earth hexaborides for the ultra-high temperature environment applications.

Thermal insulated C/SiC nanofiber aerogel with high thermal stability and superior electromagnetic wave absorption performance

Integration of thermal insulation and electromagnetic wave absorption was crucial in stealth technology and hypersonic vehicles but challenging. Herein, silicon carbide nanofibers were synthesized by in situ chemical vapor deposition within a carbon foam skeleton to form a wave absorbing and heat insulating integrated composite aerogel with a hierarchical porous structure. The unique hierarchical porous structure provided an excellent platform for the absorption of electromagnetic waves, achieving a minimum reflection loss (RLmin) of −51.46 dB at 17.20 GHz. Meanwhile, the C/SiC nanofiber aerogel maintained a low density of 0.013 g/cm3, an ultra-low thermal conductivity of 0.030 W/(m⋅K) and a high thermal stability up to 1000 °C. Furthermore, to enhance the electromagnetic wave (EMW) absorption property of the aerogel, polypyrrole (PPy) was coated on the surface of C/SiC nanofiber aerogel by facile impregnation and chemical polymerization. The multiple conductor-semiconductor-conductor structure of C/SiC-PPy composite aerogel leads to various EMW loss mechanisms and excellent impedance match, resulting in an outstanding EMW absorption performance, with a RLmin of −60.31 dB at 2.96 GHz.

Constructing multiple heterogeneous interfaces in one-dimensional carbon fiber materials for superior electromagnetic wave absorption

Due to impedance mismatch and a single loss mechanism, carbon fiber fails to meet the requirements for efficient absorbers in terms of lightweight construction and broad absorption band. In this study, we have successfully prepared one-dimensional beaded SiO2@SiC@C nanofiber (SSCF) composites with multiple heterogeneous interfaces by employing the electrospinning-carbothermal reduction method. The beaded SSCF composites effectively address the impedance mismatch issue by controlling silicon dioxide and silicon carbide through carbothermal reduction. This optimization enriches the defects and interfaces of carbon fibers composites, consequently enhancing the electromagnetic wave absorption performance. The SSCF composites demonstrate remarkable performance, with a minimum reflection loss of −59.53 dB at a matched thickness of 2.21 mm and a maximum absorption bandwidth of 6 GHz. This outstanding performance is attributed to the synergistic effects of the multi-phase composition, bead structure, and one-dimensional network structure. These features not only optimize impedance matching but also enhance defect loss, interface polarization loss (SiC/SiO2, C/SiO2, SiC/C, C/Air), conduction loss, and relaxation loss of the SSCF composites. Furthermore, radar cross-section analysis utilizing computer simulation technology confirms the excellent attenuation of microwave energy by the SSCF composites under realistic far-field conditions. This study provides valuable insights for designing efficient one-dimensional carbon-based electromagnetic wave absorbers.

Polypyrrole/Fe3O4 nanocomposites anchored on graphene toward efficient electromagnetic wave absorption performance

The ternary nanocomposites of polypyrrole/Fe3O4/graphene (PPy/Fe3O4/RGO) have been prepared via a two-step method. PPy/Fe3O4 composites have been initially anchored on GO surface by chemical one-step method following by reducing GO. The electromagnetic wave absorption (EMWA) performance of composites can be tuned by adjusting the amount of pyrrole monomers. The maximum reflection loss of the PPy/Fe3O4/RGO-0.5 (pyrrole:0.5 mL) composite is up to −66.0 dB at 14.88 GHz and the absorption bandwidths exceeding −10 dB were 5.76 GHz with absorber thickness of 2.5 mm. The investigation of the electromagnetic absorb-ability reveals that PPy/Fe3O4/RGO exhibits enhanced electromagnetic absorption properties compared to Fe3O4/RGO, which is mainly ascribed to the improved impedance matching, the enhanced interfacial effects and geometric effect. Furthermore, this strategy expands the scope of the electromagnetic wave absorption materials. It confirms that modification of graphene with PPy and Fe3O4 makes the ternary nanocomposites have a promising future in electromagnetic wave absorption materials.

Optimization of three dimensional rGO@MWCNTs/Fe3O4-PVA composite film through regulated structure for convenient and replaceable electromagnetic wave absorption material

Optimizing the composition and structure of polymers and carbon nanomaterials to obtain composite films with excellent mechanical and electromagnetic wave (EMW) properties is an excellent solution for exploring EMW absorbing materials. In this work, a flexible composite film with a regular three-dimensional network structure was designed and prepared. The modified rGO@MWCNTs/Fe3O4-PVA composite nanofilm with optimized composition and structure has a multi-component heterogeneous interface, three-dimensional network structure. The composite film has high EMW absorption performance, excellent flexibility, mechanical strength and stability, and can be used in a wide range of application scenarios. At a thickness of 2.8 mm, the effective absorption bandwidth (fE) reaches 3.72 GHz, the minimum reflection loss (RLmin) is -48.99 dB, and the tensile stress reaches 32 MPa. This work realizes the regulation of the mechanical properties and EMW absorbing properties of the composite film, and provides an efficient and stable flexible composite EMW absorbing material.

Improved broadband design of SiC/MWCNT absorbing materials through synergistic regulation of heterointerface structure and triple periodic minimal surface meta-structure

SiC/multi-walled carbon nanotube (MWCNT) composites are considered to be promising materials for high-temperature electromagnetic wave (EMW) absorption due to their strong thermal stability and tunable dielectric properties. However, the EMW absorption performance of these composites is limited by poor impedance matching. This study proposes a novel multiscale structure synergistic regulation approach to enhance EMW absorption performance, which involves constructing a heterointerface structure and a triple periodic minimal surface (TPMS) meta-structure. The addition of a SiO2 shell as an impedance layer to the SiC/MWCNT core to improve the intrinsic impedance. Meanwhile, the heterointerface between the core-shell structure leads to multiple interface polarization, significantly enhancing EMW energy dissipation. Consequently, the effective absorption bandwidth (EAB) of SiO2–SiC/MWCNT composites increased from 0.88 to 4.56 GHz. Furthermore, a TPMS meta-structure, fabricated by three-dimensional (3D) printing and sol infiltration technology, is developed to further improve impedance matching with the equivalent electromagnetic effect. Simulation and experimental results demonstrate that the SiO2–SiC/MWCNT TPMS meta-structure exhibits broadband EMW absorption performance, with the EAB reaching 7.2 GHz. This improvement is attributed to the synergistic regulation of the heterointerface structure and TPMS meta-structure, which provides a good balance between the requirements of electromagnetic loss and impedance matching. Additionally, the composites exhibit excellent oxidation resistance, as their EAB remains almost unchanged after exposure to 1000 °C for 6 h. This research offers a new design paradigm for ultrabroadband design of the nonmagnetic high-temperature absorbing materials.

Multifunctional carbon aerogels loaded with pea-pod-like carbon nanotubes for outstanding electromagnetic wave absorption performance

Although ordered porous carbon materials (PCMs) have shown promising potential in the field of electromagnetic wave absorption (EWA), creating multifunctional PCMs with outstanding microwave absorption performance remains a significant challenge. Herein, ordered porous carbon aerogels loaded with pea-pod-like nitrogen-doped carbon nanotubes (CNTs) were fabricated via orientation freeze-drying followed by high-temperature pyrolysis. The optimized aerogel exhibits extraordinary EWA performance with a broad effective absorption bandwidth of 7.68 GHz and exceptionally strong absorption of −91.58 dB at a low filling ratio of only 3 wt%, which is the largest absorption strength among all known aerogels to date. The exceptional EWA performance is attributed to the synergistic effect of abundant loss mechanisms resulting from a unique pod-like structure in ordered porous carbon aerogel, where nitrogen-doped CNTs encapsulate magnetic alloy nanoparticles. Optimized aerogel exhibits superior compressive elasticity, thermal insulation, and light weight, laying the groundwork for designing practical next-generation EWA materials.

In-situ synthesis of Co/Co3O4 nanoparticles decorated carbon nanofiber aerogels for lightweight electromagnetic wave absorption rubber composites with multiple loss effects

Carbon-based magnetic absorbents are widely used for electromagnetic wave absorption (EMWA) rubber composites due to the dual electromagnetic wave loss effects of dielectric loss and magnetic loss. Co/Co3O4 nanoparticles decorated carbon nanofiber aerogels (C/Co/Co3O4 aerogels) are prepared by carbonization of nanofiber network structure agarose/cobalt acetate. The in-situ synthetic C/Co/Co3O4 aerogels with carbon nanofiber network structure and controllable particle size of Co/Co3O4 nanoparticles that have the good conductivity and tunable magnetic property increasing both of the dielectric loss and magnetic loss capabilities, which can improve the EMWA performance. Lightweight EMWA rubber composites with 3.75 wt% C/Co/Co3O4 aerogels have the same density as that of silicone rubber (PDMS), the effective absorption band (EAB, frequency for reflection loss<−10 dB) of PDMS/Co-1.25 is aways above 3 GHz when the thickness is bigger than 2.5 mm, the max EAB is 4.24 GHz at the thickness of 2.74 mm. The radar cross section (RCS) reduction can achieve 14 dBm2 when the perfectly electrically conductive (PEC) is covered by a 4.5 mm thick PDMS/Co-1.25. The intensity distributions of electric field, magnetic field and power loss density of EMWA rubber composites are exhibited based on the electromagnetic parameters. The rubber composites based on C/Co/Co3O4 aerogels can be used as lightweight flexible EMWA materials.

Fabrication of MOF-rGO aerogels to enhance electromagnetic wave absorption by adjusting the morphology and structure of MOFs by electron transfer

Graphene and its derivatives have become the star materials in the field of electromagnetic wave (EMW) absorption, and have been widely studied because of their unique structure and excellent properties. However, the high electrical conductivity of graphene-based material leads to poor impedance matching performances, so it often needs to be annealed at high temperatures, which is a intricate procedure and cause the waste of energy. Herein, we develop a convenient strategy to synthesize metal organic framework-reduced graphene oxide (MOF-rGO) aerogels through facile hydrothermal and freeze drying procedure. Firstly, the excessive electrons on graphene can be transferred to MOF, in this way, no annealing is needed. Secondly, the morphology and structure of MOF can be regulated electronically to endow the material with rich heterojunction interfaces and enhance its interfacial polarization. Thirdly, the synthesized aerogels satisfy the requirements of thin thickness, low density and light weight. The fabricated Ni-MOF-rGO and FeNi-MOF-rGO aerogels exhibit remarkable EMW absorption performances with strong reflection loss (RL) and broad effective absorption band (EAB) at the thickness of 2.4 (−47.8 dB and 7.84 GHz) and 2.9 mm (−48.3 dB and 8.32 GHz) whereas the filling contents are just 5 %. Moreover, the attenuation capacity of the fabricated aerogels are verified through the radar-section simulation and the interfacial polarization loss are confirmed by the COMSOL analogue simulation. In a word, this work provides a new afflatus and inspiration for the design of graphene-based EMW absorption materials.