The study aimed to investigate the shear bond strength (SBS) of orthodontic ceramic brackets bonded to porcelain ceramic surfaces that had undergone various conditioning methods. Materials and Methods: Forty ceramic discs were fabricated (vita vmk master®, zahnfabric, Germany) with a diameter of (4*10mm). Ceramic discs were divided into four groups (n = 10) according to ceramic surface conditioning methods, 37% phosphoric acid (PH), 9%hydrofluoric acid (HF), and surface conditioning with a fine diamond bur. Transbond XT light-cure composite was used to bond ceramic brackets. Before bonding, extra samples from each group were chosen to be examined using a scanning electron microscope (SEM) to determine the topography of the ceramic surface. The Shear Bond Strength data were evaluated using one-way analysis of variance (ANOVA) and Tukey HSD tests. Under an optical stereomicroscope, debond surfaces were examined. Results: Surface conditioning with a fine diamond bur + HF acid etching group produced the highest SBS (30.64 ± 7.28 MPa), and the lowest SBS was investigated in the PH acid etching group (14.75 ±3.32 MPa). Conclusions: Different conditioning methods affected the porcelain ceramic surface's shear bond strength (P < 0.05). The highest SBS was found in the fine diamond bur_+ HF acid etching group; however, this had a deleterious effect on the ceramic surface after debonding.