Displacement Ductility Research Articles

Experimental Investigations of Seismic Performance of Girder–Integral Abutment–Reinforced-Concrete Pile–Soil Systems

Integral abutment bridges (IABs) have been widely applied in bridge engineering because of their excellent seismic performance, long service life, and low maintenance cost. The superstructure and substructure of an IAB are integrally connected to reduce the possibility of collapse or girders falling during an earthquake. The soil behind the abutment can provide a damping effect to reduce the deformation of the structure under a seismic load. Girders have not been considered in some of the existing published experimental tests on integral abutment–reinforced-concrete (RC) pile (IAP)–soil systems, which may not accurately represent real conditions. A pseudo-static low-cycle test on a girder–integral abutment–RC pile (GIAP)–soil system was conducted for an IAB in China. The experiment’s results for the GIAP specimen were compared with those of the IAP specimen, including the failure mode, hysteretic curve, energy dissipation capacity, skeleton curve, stiffness degradation, and displacement ductility. The test results indicate that the failure modes of both specimens were different. For the IAP specimen, the pile cracked at a displacement of +2 mm, while the abutment did not crack during the test. For the GIAP specimen, the pile cracked at a displacement of −8 mm, and the abutment cracked at a displacement of 50 mm. The failure mode of the specimen changed from severe damage to the pile top under a small displacement to damage to both the abutment and pile top under a large displacement. Compared with the IAP specimen, the initial stiffness under positive horizontal displacement (39.2%), residual force accumulation (22.6%), residual deformation (12.6%), range of the elastoplastic stage in the skeleton curve, and stiffness degradation of the GIAP specimen were smaller; however, the initial stiffness under negative horizontal displacement (112.6%), displacement ductility coefficient (67.2%), average equivalent viscous damping ratio (30.8%), yield load (20.4%), ultimate load (7.8%), and range of the elastic stage in the skeleton curve of the GIAP specimen were larger. In summary, the seismic performance of the GIAP–soil system was better than that of the IAP–soil system. Therefore, to accurately reflect the seismic performance of GIAP–soil systems in IABs, it is suggested to consider the influence of the girder.

Seismic performance of mortise-tenon joint in prefabricated platform canopy

To optimize the prefabricated canopy joints, improve the construction efficiency, and enhance the seismic performance of assembly joints, a novel mortise-tenon joint (MTJ) was proposed. To evaluate the seismic performance along the vertical and track directions, two 1:1.5 scaled specimens were tested under low-cycle reciprocated loading. The test results find the hysteretic curves in both directions exhibit the “pinch” effect especially in the vertical direction, indicating the feature of shear slippage. The displacement ductility coefficients were all above 5.0, and the ultimate drift ratios were 4.54% and 5.88% respectively, showing excellent deformation ability and ductility. The parameters, such as the sectional strength ratio, the stirrup ratio of the prefabricated beam, the reinforcement ratio and the cross-sectional area of the enlarged section, were analyzed by the validated finite element (FE) models. The analysis shows as the section strength ratio decreases and the stirrup ratio increased, the seismic bearing capacity improved, while the plastic hinge located on the prefabricated column varied to the prefabricated beam ends. Based on the results, it is recommended the number of longitudinal rebars through the prefabricated beam is 4, the stirrup diameter in the prefabricated beam is 10mm and the the column cap is no less than 400mm. Finally, based on the truss-diagonal strut model, a method for calculating the shear strength capacity of the novel joint was proposed. Compared with the test and FE results, the theoretical equations exhibit good computational accuracy.

Flexural behavior of reinforced concrete arch ribs

For many years, arch bridges have been celebrated for their striking appearance and structural effectiveness. However, the response of arch bridges to dynamic loadings, particularly during earthquakes, remains poorly understood, and reliable seismic design guidelines are lacking. Previous research has suggested that reinforced concrete (RC) arch ribs may experience flexural yielding at their springings due to the interaction of axial force and bending moment under earthquake loading. To assess the ductile behavior and ensure the adequate performance of RC arch ribs, a comprehensive investigation combining experimental and analytical approaches was conducted in this study, taking into account the influence of high axial load and the hollow section configuration present in RC arch ribs. The test results revealed that all RC arch ribs exhibited a typical flexural failure mode. As the axial load increased, the lateral load bearing capacity also increased, but the displacement ductility decreased significantly. Comparing different section configurations, the RC arch rib specimen with a double-cell boxed section demonstrated higher lateral load bearing capacity but lower displacement ductility compared to the single-cell boxed section, while the energy dissipation capacity was approximately similar for both section configurations.

Size effect modellings of axial compressive failure of RC columns at low temperatures

This paper applied a thermal-mechanical sequential coupled mesoscopic simulation method to explore the axial compression performance and the corresponding size effect of Reinforced Concrete Columns confined by Stirrups (i.e., RCCS) at low temperatures, with considering the interaction between concrete meso-components and steel bars as well as the low-temperature effect of mechanical parameters. Based on the heat conduction analysis, the axial compression mechanical failure behavior of RCCS with four structural sizes (i.e., 267 × 267 × 801, 400 × 400 × 1200, 600 × 600 × 1800 and 800 × 800 × 2400 mm) and two stirrup ratios (i.e., 1.26% and 2.89%) at different temperatures (i.e., T = 20, −30, −60 and −90°C) was subsequently simulated. The effects of temperature, structural size and volume stirrup ratio on axial compression properties were quantitatively discussed. The results showed that the peak strength of RCCS increased with the decreasing temperature, and the smaller-sized RCCS showed a stronger effect of low-temperature enhancement. Both the residual strength and displacement ductility coefficient decreased with the decreasing temperature. The peak strength, residual strength and displacement ductility coefficient of RCCS decreased with the increasing structural size, showing obvious size effects. The size effect on peak strength increased with the decreasing temperature, (the maximum increase was nearly 140%), but the size effect on displacement ductility coefficient decreased (the maximum decrease was nearly 70%). The peak strength, residual strength and ductility were enhanced with the increasing volume stirrup ratio, which was helpful to reduce the influence of size effect. Finally, an improved size effect theoretical model was proposed, which can effectively predict the axial compressive strength of RCCS with different structural sizes and stirrup ratios at room and low temperatures. The present research results can provide reference for the large-scale engineering application of RCCS in low-temperature environments.

Ductility and cracking behavior of UHPC-RC composite beam under bending test based on acoustic emission parameters

Ultrahigh-performance concrete (UHPC) possesses improved mechanical properties due to its high strength, durability, and toughness. Currently, there is a single method for detecting the cracking behavior and evaluating the ductility of the UHPC-reinforced concrete (RC) composite beam. As an important part of structural non-destructive monitoring techniques, the acoustic emission (AE) technique can be used to analyze the damage pattern of the structure by the variation characteristics of its individual parameters. On this basis, four-point bending tests were carried out on the RC beam and UHPC-RC composite beam, and the AE technique was used for ductility analysis and cracking behavior monitoring. The results showed that the UHPC material enhanced the flexural capacity of the UHPC-RC composite beam. The AE ring counts and energy parameters could be used to analyze the cracking process of the UHPC-RC composite beam during flexural damage. The proposed new ductility indices, AE ring counts ductility index (ARD) and AE energy ductility index (AED), differed from the displacement ductility indices within the range of 2 %, providing a new method for calculating ductility indices of concrete structures. During the failure stage, the UHPC-RC composite beam produced more tensile cracks at the early stage of cracking and the stage of damage compared to the RC beam. In addition, the b value of the RC beam had a large range of fluctuations during the failure stage, indicating that the RC beam produced more micro-cracks and macro-cracks and more damage compared to the UHPC-RC composite beam.

End anchorage‐reinforcement CFRP systems for heat‐damaged beams with side NSM CFRP rope

AbstractThe efficiency of retrofitting systems with side near surface mounted (SNSM) CFRP ropes in boosting the flexural performance of intact/heat‐damaged reinforced concrete (RC) beams was investigated using a total of 14 RC beams (250 × 150 × 1450 mm) in two groups. In the first group, the beams were strengthened using SNSM CFRP ropes of a parabolic profile without and with end fan or hock anchorages, coupled with the implantation of lateral and/or vertical CFRP dowels in the high‐shear zone. The beams of the second group were repaired using similar configurations after being heated to 400°C in an electrical furnace for 2 h. A control beam in each group was designated as a reference. The mechanical performance and cracking sequence in all beams was evaluated under four‐point loading test setup. Heat‐damage resulted in reductions in load capacity and stiffness at 11% and 10%, yet an increase in toughness and displacement ductility by 18% and 20%, respectively. Implementing end hocks with end vertical and lateral dowels prevented concrete‐cover separation; imparting the best enhancement in structural performance for the repaired and post‐heated beams. All beams experienced flexural failure mode except for the heat‐damaged one, repaired with end‐hock anchorage without lateral doweling.

Constant-ductility inelastic displacement ratio spectra for design of superstructures in seismically isolated buildings

Constant-ductility inelastic displacement ratio (Cμ) spectra can be utilized for the estimation of peak inelastic structural displacements in the seismic design procedure. Currently, suitable analytical estimates of Cμ are lacking for base-isolated buildings with inelastic behavior of superstructures in a beyond design basis earthquake. This paper attempts to fill this research gap and hence conducts parametric studies on the Cμ spectra of base-isolated inelastic superstructures with lead-rubber bearings (LRBs). For that purpose, the inelastic model and equations of motion, boundary conditions of the analytical formulation of Cμ, and controlling parameters for the two-degree-of-freedom (2DF) superstructure-isolator system with LRBs are presented first. Subsequently, by analyzing the parameterized 2DF systems using an ensemble of strong earthquake records representative of a site with stiff soil conditions, the influence of controlling parameters, namely, displacement ductility ratios, superstructure periods, post-yielding stiffness ratios of superstructures, mass ratios, isolation periods and normalized isolator strength, on the mean and dispersion of Cμ are discussed, and the boundary conditions of Cμ are validated based on the calculated data. Comparisons of how the controlling parameters influence the Cμ and earlier investigated CR (i.e. constant-strength inelastic displacement ratio) spectra are also presented. Lastly, a predicting equation with reasonable accuracy is proposed for the mean Cμ using the nonlinear multivariable regression analysis method. The outcome of this study allows the application of displacement-based design via inelastic displacement ratio for new base-isolated structures under beyond design basis earthquakes.

Tests on seismic and shear performance of RC shear walls under alternating axial tensile and compressive loads

Under strong earthquakes, reinforced concrete (RC) shear walls at the bottom of high-rise buildings may experience an internal force state of alternating tension-shear (-bending) and compression-shear (-bending). In order to clarify the seismic and shear performance of shear walls under alternating axial tensile and compressive loads (referred to as alternating axial loads), cyclic tests on five shear-controlled large-scale RC shear walls were conducted in this study. The tests were conducted with synchronized axial loads and horizontal displacements, and a quantitative analysis of the influence of the alternating axial loads was achieved by setting two control specimens. The crack development, failure modes, load-carrying capacity, deformation capacity, and energy dissipation of the specimens were measured and analyzed. The test results indicate that different axial load cases altered the crack pattern and failure mode. With an increase in the target axial tensile load, both tension- and compression-shear capacities of the specimens under alternating axial loads decreased, with the former experiencing a more significant reduction. In comparison to the tension-shear control specimen, it was observed that the alternating axial loads significantly reduced the displacement ductility of shear walls in the tension-shear state, resulting in substantially lower energy dissipation capacity. In addition, based on the tests in this study and the collected shear wall tests, the shear strength formulas in the current codes ACI 318-19 and JGJ 3–2010, as well as a shear model previously proposed by the authors, were evaluated. Based on the test results, a reduction factor was fitted to account for the effect of alternating axial loads on the compressive-shear capacity of RC walls.

Rubberized reinforced concrete columns under axial and cyclic loading

The experimental study presented in this research was conducted to understand the performance of rubberized concrete columns under axial loads and numerically analyze the conduct of rubberized reinforced concrete (RRC) columns under cyclic loads. Twelve large-scale columns with square and circular cross sections were utilized to carry out experimental testing. Under axial loading, fine aggregate was replaced in percentages of 0%, 10%, and 15% with crumb rubber (CR). Square RRC columns were examined by a finite element program (ABAQUS) under cyclic loading. The experimental results indicated that the columns with crumb rubber had a lower load capacity than those without crumb rubber when exposed to axial loads. The numerical results were in good alignment with the experimental results, indicating that the simulated model may simulate the behavior of rubberized concrete columns under both axial and cyclic loads. According to the numerical analyses, the lateral displacement was significantly improved for rubberized reinforced concrete columns with 10% and 15% replacement of fine aggregates compared to columns without CR. Adding 10% and 15% of crump rubber to the fine aggregate in reinforced concrete columns increased the displacement ductility. The equivalent viscous damping ratio was enhanced by 33.67% when increasing crumb rubber (CR) from 0% to 10%, and when crumb rubber (CR) replacement became 15%, the damping ratio increased to 44.02%.The rubberized reinforced concrete columns showed a more ductile reaction than the traditional reinforced concrete columns, as evidenced by their softer post-peak response.

Retrofit of damaged reinforced concrete frame by autoclaved aerated concrete blocks infill wall: Experimental validation and strength estimation

This study introduces a novel approach for the global retrofitting of seismic performance in destructively damaged reinforced concrete (RC) frames through the application of autoclaved aerated concrete (AAC) blocks infill walls to enhance both structural strength and stiffness. Three full-scale RC frames are designed and fabricated, comprising an intact bare frame, a damaged frame strengthened by carbon fiber-reinforced polymer (CFRP), and a damaged frame retrofitted with the same CFRP and AAC blocks infill walls. To verify the cyclic behaviors and working principle of the retrofitted system, the two frames undergo a pre-damage scenario with a maximum inter-story drift ratio (MIDR) of 2.52%, and then both specimens are retrofitted. Afterward, a pseudo-static cyclic test is conducted on three specimens, with a MIDR of 3.36%. The test data is analyzed and discussed in terms of hysteretic responses, secant stiffness, displacement ductility, and energy dissipation capacity. The findings indicate a significant improvement in the lateral strength and stiffness of the seismic-damaged frame through the implementation of AAC blocks infill walls, demonstrating performance comparable to the intact RC frame. Also, the slight local crushing of AAC blocks and their interaction with mortar joints effectively dissipates a considerable amount of input energy, thereby reducing the energy dissipation demands on retrofitted structural components. Moreover, the theoretical deduction of the lateral strength of the retrofitted RC frames is presented. The errors between the predicted and test results fall within 5%, suggesting that the analytical outcomes can reasonably predict the lateral strength of the specimens.

Experimental and numerical investigation of the cyclic behaviour of coupled balloon-type CLT shear walls with high-capacity base connections

Mass timber buildings have gained global popularity due to the increasing availability and affordability of mass timber products and an increasing awareness of the sustainability of timber construction. This paper presents an experimental and numerical study on coupled balloon-type cross-laminated timber (CLT) shear walls with the aim of overcoming the capacity limitations of platform CLT shear walls. Using self-tapping screws to create innovative hold-down solutions, three two-storey coupled CLT shear walls were cyclically tested and the results demonstrated that the proposed coupled wall systems could achieve significantly higher lateral strength (over 400 kN) and initial stiffness (up to 14 kN/mm) compared to platform CLT shear walls in literature. The cyclic test results were used to validate a finite element CLT shear wall model in CLTWALL2D. The calibrated model was then used to run a parametric study of a series of balloon-type CLT shear walls up to twelve storeys (42 m) in height. This study provided evidence that coupled balloon-type CLT shear walls with high-capacity screwed connections have the potential of reaching high strength and stiffness with the displacement ductility factor μ = 2–4.

Comparative analysis of the seismic performance of ECC jacket reinforced columns with different cross-sectional forms subject to different load modes

Based on the high tensile strength and tensile strain of (engineered cementitious composites) ECC, it is applied to the weak link central columns of subway stations to enhance their seismic resilience. In this study, the effects of the column's cross-sectional shape, ECC jacket form, and the vertical gravity load and vertical dynamic load during seismic action on the hysteretic performance of the column were thoroughly analyzed. A constrained constitutive model for cementitious materials, a reinforced hysteresis constitute model, and a calculated damage factor for concrete were adopted to establish a three-dimensional refined column model with an experimentally verified error of less than 10 %. After that, the damage distribution and damage degree of the columns, as well as the changes in hysteretic performance such as hysteretic curve, skeleton curve, energy dissipation, and stiffness degradation were analyzed by the static model analysis. The results showed that the columns had higher damage levels under high frequency and high amplitude of dynamic axial compression ratio in the vertical direction compared to the constant high axial compression ratio, and the ECC jacket could effectively reduce the damage levels of the columns, but the use of the in-built ECC (IB-ECC) jacket was better than the out-sourced ECC (OS-ECC) jacket. In addition, the IB-ECC jacket did not significantly improve the peak bearing capacity of the columns, but significantly improved the ultimate bearing capacity and displacement ductility of the columns, while the OS-ECC jacket significantly improved the peak bearing capacity of the columns. The ECC jacket was also effective in slowing down the stiffness degradation of the columns. This study significantly contributes to the design strategies for enhancing the resilience of columns in subway stations.

Experimental study on seismic performance of two-story two-bay. Precast concrete frame with UHPC-based connections

The UHPC-based connections, utilizing Ultra-high performance concrete (UHPC) to connect rebars within precast concrete structures, present the advantages of short splice length, simplified construction, and low cost due to the excellent bond property between UHPC and rebars. This investigation focuses on seismic performance of precast concrete frame (PCF) with UHPC-based connections. The UHPC-based connections were arranged strategically to the beam-column joints and column bases in PCF to connect longitudinal rebars of beams and columns, respectively. Two half-scale, two-story, two-bay reinforced concrete frames, including PCF and a monolithic concrete frame (MCF) for reference, were tested under cycle loading with axial compression ratios of 0.33 in the middle columns and 0.22 in the side columns. The results revealed that PCF exhibited a beam sway mechanism, with all beam hinges developed prior to column hinges, while MCF displayed a mixed sway mechanism, with part of beam hinges developed prior to column hinges. The hysteresis curves of the two frames were globally stable with minimal pinching, and PCF displayed greater energy dissipation compared to MCF. The load-carrying capacity of PCF was 9 % higher than that of MCF. The displacement ductility of PCF was 4.14, exceeding that of MCF by 10 %. The two frames showed similar laws of stiffness degradation. Overall, the precast concrete frame with the UHPC-based connections exhibited better seismic performance in comparison with the monolithic counterpart.

Seismic rehabilitation of RC frames with innovative precast U-shaped UHPC jackets: Experimental evaluation and computational simulation

The rehabilitation of post-earthquake reinforced concrete (RC) frames is crucial for both restoring structural integrity and enhancing seismic resilience against future seismic events. Ultra-high-performance concrete (UHPC) is distinguished by its exceptional strength, crack-control capabilities, ductility, and durability. Despite numerous studies on its use for structural retrofitting, its application in rehabilitating damaged RC frames remains limited. This study introduced a novel precast U-shaped UHPC jacket designed for the post-earthquake rehabilitation of RC frames. The jacketing method promotes composite action in rehabilitated members through lap splicing and dowel bars, complemented by cast-in-place connections using UHPC to minimize splice length and strengthen potential weak areas under external loads. The efficacy of this jacketing approach was rigorously evaluated through cyclic loading experiments on two RC frame specimens. Results indicated that the UHPC rehabilitation method not only recovered but significantly enhanced the seismic performance of the previously damaged frame, improving initial stiffness, yield strength, peak strength, displacement ductility, and energy dissipation capacity. However, the rehabilitated frame showed a reduced yield drift and increased residual displacement compared to the as-built frame. The experimental results also revealed the necessity of accounting for bond slip in structural rehabilitation analysis and design to prevent overestimating lateral stiffness. Furthermore, the study developed a computational model that incorporates flexure, bond slip, and shear responses, aiming to effectively simulate the load-displacement behavior of rehabilitated RC frames with reasonable accuracy.

Local scour effects on seismic behavior of pile-group foundations in cohesionless soils: Insights from quasi-static tests

Local scour has been reported as a common phenomenon for pile-group foundations in marine, coastal, and riverine sites, while its effects on the seismic behavior of pile-group foundations are yet to be well documented. This paper reported a pair of quasi-static cyclic loading tests on 2 × 3 scoured pile-group foundation specimens, one in global scour and the other in local scour, to understand the influence of local scour on the seismic behavior, particularly in terms of soil-pile interaction features and failure mechanisms. Test results indicate a flexural failure mode for both specimens. Local scour does not change the order of limit states but postpones the occurrence of concrete cover cracking and rebar yielding due to the reduced lateral stiffness of the locally scoured piles. Moreover, local scour rarely changes the aboveground damage regions at the top of outer piles (one time the side length of squared pile section, D), but significantly aggravates and deepens the underground damage regions at outer piles (from 4 ∼ 5D for global scour to 3.7 ∼ 6D for local scour). Besides, local scour reduces the displacement ductility factor from 2.50 to 1.25 for the Easy-to-Repair limit state, resulting in adverse impacts on pile-group foundations in general.

Experimental study on seismic performance of post-tensioned precast segmental piers designed with multiple joint openings

In accelerated bridge construction (ABC), precast segmental piers (PSPs) have shown significant progress in shortening the construction period and reducing the cost. By combining multiple segments with post-tensioned (PT) tendons, the desired self-centering ability can be introduced; however, this may lead to a lower energy dissipation (ED) capacity and concentrated damage. To address this concern, the present study proposes a design concept that promotes multiple joint openings to achieve a better energy dissipation capacity and decentralized damage without compromising the self-centering ability. Two main approaches for this objective are discussed in detail. The first approach incorporates different arrangements of ED rebars at various joints, while the second introduces innovative damage control rubber joints (DCRJs) with varying stiffness beneath each segment. Four scaled specimens designed using these two approaches were quasi-statically tested. The observed damage, final failure mode, energy dissipation capacity, resilience index, and damage decentralization were further examined. The results revealed that for PSPs designed using the first approach, the joint openings were successfully decentralized only up to a certain level, after which they were still predominantly concentrated at a single joint, leading to strength degradation and damage concentration. PSPs designed using the second approach demonstrated decentralized joint openings, improved displacement ductility, and damage mitigation, resulting in both superior seismic and post-seismic performance.

Experimental study on seismic behavior of reinforced concrete exterior beam-column joints under varying axial load

The majority of low-cycle loading tests on reinforced concrete (RC) beam-column joints were currently conducted under constant axial loads. During earthquake shaking, the axial load on the joints fluctuates due to the overturning moment and vertical ground vibration. Particularly in exterior beam-column joints, where beam shear occurs on only one side, the range of axial load variation is significantly larger. To elucidate the impact of varying axial loads on the seismic performance of exterior beam-column joints, low-cycle loading tests were conducted on four groups of full-size beam-column subassemblage specimens. Two identical specimens from each group underwent low-cycle loading tests with constant and varying axial loads, respectively. Based on the experimental findings, this paper examines the differences in cyclic behaviors among comparison specimens, focusing on damage characteristics, joint shear strength, stiffness degradation, displacement ductility, and longitudinal bar slip. The study suggests that compared to specimens subjected to constant axial loads, the comparison specimens exhibit variations in load-carrying capacity corresponding to the fluctuations in axial load. Furthermore, varying axial loads accelerate post-peak stiffness and strength degradation, leading to reduced ductility. Additionally, specimens in one of the comparison groups exhibited different failure models when subjected to varying axial loads and constant axial loads, specifically beam failure and joint failure, respectively. Numerical simulations of the corresponding beam-column subassemblages were conducted on the Opensees platform to elucidate how the two axial loading methods affect the transformation of failure modes. A subsequent parametric study focusing on the axial compression ratio was performed to further explore the impact of varying axial loads on the seismic behavior of beam-column joints.

Probabilistic damage evaluation of isolated steel box-girder bridge excited by near-field earthquakes

Modern civilization regards bridges as lifelines, and their failure due to significant earthquakes in the past has raised concerns about their seismic vulnerability. The effect of near-fault earthquakes on the bridge vulnerability is a significant problem that has not been well explored. The present work utilizes fragility analysis to assess the probabilistic seismic risk evaluation of a continuous isolated steel box girder bridge exposed to near-field ground motions (NFGMs). Probabilistic seismic demand models (PSDMs) of the bridge are explored to reliably associate key demand and intensity measures to capture the seismic performance of the system. This study examines a steel box girder bridge in Guwahati, India, isolated with lead rubber (LRB) bearings and a friction pendulum system (FPS). To achieve a comparable seismic response, each bearing system is designed for a similar isolation period. The PGV/PGA ratio is a useful metric for classifying ground motion suites and estimating their frequency content by classifying the input excitations into low- and high-frequency motions. To perform probabilistic seismic risk assessments, two ensembles of forward directivity records with PGV: PGA >160 cm/s/g (high frequency) and PGV: PGA <160 cm/s/g (low frequency) are considered. Moreover, one ensembles of near-field incorporating the fling effect and far-field are also utilized. The failure probability under the seismic hazards for isolated bridges is assessed utilizing different damage measures (DM) such as maximum displacement ductility of pier (DDP), displacement of deck (MDD), drift ratio of pier (PDR), and rotational ductility (RDP). The near-field earthquake damage probability is significantly impacted by the PGV/PGA ratio, as a high PGV/PGA ratio results in a greater probability of damage than a low PGV/PGA ratio. In conclusion, guidelines are provided that will help the design engineers for designing bridges with LRB and FPS isolators for seismic isolation in the event of varying ground motion characteristics.

Residual load-carrying performance of ECC-RC composite beam after drop hammer impact

Four types of specimens with various thicknesses of ECC layer in the tensile side of RC beam are fabricated. The influence of ECC layer on the dynamic response and residual capacity of RC beams is investigated through drop hammer impact test and post-impact static loading test. The results reveal that increasing the thickness of the ECC layer in the tensile side leads to less major cracks and more tiny cracks on the beam side under impact, and the damage of concrete in the impact zone alleviates. The incorporation of the ECC layer plays an insignificant role in displacement restitution and residual load-carrying capacity. However, ECC-RC composite beams effectively mitigate displacement ductility degradation. Compared to RC beam, ECC-RC composite beams also exhibit superior energy dissipation capacity at the post-impact loading stage. The parametric analysis indicates that a thicker ECC layer in composite beams with a low tensile reinforcement ratio effectively reduces maximum impact displacement but has a negligible influence on residual load-carrying capacity. In contrast, increasing the ECC layer in beams with a high tensile reinforcement ratio offers a limited reduction in maximum impact displacement but its residual load-carrying capacity significantly improves after impact.

Comparative study on seismic behavior of corroded RC columns strengthened by ECC combined with steel cage /fiber grid/CFRP

A method for strengthening was proposed to improve the seismic behavior of corroded reinforced concrete (RC) columns by using engineered cementitious composite (ECC) combined with a steel cage/fiber grid/carbon fibre reinforced plastics(CFRP). The corroded RC columns strengthened with ECC combined with a steel cage, fiber grid, and CFRP were subjected to low cyclic compression tests at design axial pressure ratios (n) of 0.3 and compared with corroded and uncorroded columns. Experimental results showed that ECC strengthening of corroded RC columns not only significantly improved their load-carrying capacity, displacement ductility, and energy dissipation capacity but also effectively reduced the degree of damage and stiffness degradation. The ductility coefficients of ECC/steel cage composite strengthened columns and ECC/CFRP composite strengthened columns are 35.58 % and 34.13 % higher, respectively, compared to ECC fully strengthened columns, while the ductility coefficient of ECC/fiber grid composite strengthened columns decreased by 4.33 % compared to ECC fully strengthened columns. Among them, the ECC/steel cage composite-strengthened columns exhibited the highest number of hysteresis loops, the strongest energy dissipation capacity, and the best strengthening effect. Additionally, a restoring force model for ECC-strengthened corroded RC columns was established, and its validity was verified through theoretical calculations.