Cerasmart Research Articles

The effect of whitening toothpastes on the surface properties and color stability of different ceramic materials

ObjectivesThis study aimed to evaluate the effect of whitening toothpastes on the surface roughness and colour change of CAD-CAM materials.Materials and methodsA total of 96 samples (2 × 10 × 12 mm3) were prepared from Cerasmart (CS) and Celtra Duo blocks. Celtra Duo samples were divided into two groups. One group was fired with glaze paste (CDG) and the other was not treated (CD). All groups were then divided into 4 subgroups (n = 8). The groups were brushed with conventional (Colgate™ Max Fresh), silica (Opalescence™), charcoal (Curaprox™ Black in White) and blue covarine (Signal™ White Now) toothpastes for 30,000 brushing cycles. The initial and final surface roughness values were measured with contact profilometer and a dental spectrophotometer used for obtaining colour values. One sample from each brushed group was analyzed using a scanning electron microscope. Data was analyzed with Kruskal-Wallis and Mann-Whitney tests (p = 0.05).ResultsThe surface roughness of CS samples brushed with Opalescence™ and Curaprox™ was significantly higher than CD and CDG. Surface roughness change values of CS samples brushed with Curaprox™ were significantly higher than the CD and CDG. Curaprox™ brushed samples showed significant difference in colour change values for all materials.ConclusionsBrushing increases the surface roughness of CAD-CAM ceramic materials. The roughness of resin-based materials is higher than zirconia-reinforced lithium silicates. Silica-contained toothpastes may cause discoloration of nanoceramic and zirconia-reinforced glass ceramic restorations.Clinical relevanceIt should be clinically considered that whitening toothpastes may cause roughness in ceramic materials and change the desired color.

Effects of two dentifrices on the surface properties and staining susceptibility of polymer-based materials.

This study examined the effect of whitening and abrasive regular dentifrices on the surface characteristics and stain susceptibility of polymer-based CAD-CAM blocks subjected to artificial toothbrushing abrasion (TB). Two resin composite blocks [CeraSmart (CS) and Grandio Blocs (GB)], one polymer-infiltrated ceramic [Vita Enamic (VE)], and one direct resin composite [GrandioSO (RC)] were used to produce 60 specimens. The baseline mass, gloss, roughness, Vickers hardness (Hv), and color were measured after 7 days of water storage. The specimens were then separated into three TB treatment groups (n = 5): water control (C), regular daily dentifrice (R), and whitening dentifrice (W). Measurements were repeated post-TB (20,000 cycles). All specimens were immersed in coffee, and the CIE ΔE00 was measured after 1, 7, and 14 days. Two-way, one-way ANOVA, and Tukey's post hoc tests were performed to determine any significant differences between the materials and TB groups. To determine the stain resistance, repeated measures of ANOVA, one-way ANOVA, and Tukey's post hoc tests were used (α = 0.05). The R and W mass changes were minimal (-3.77 to 3.16g%). W reduced the gloss of all the materials by 12.6%-65%. All materials in W were slightly rougher (Ra, 0.107-0.144 μm) than those in R (Ra, 0.049-0.072 μm). The ΔE00 ranged from 0.6 to 1.6 in W and 0.4 to 1.4 in R. VE was the hardest material at baseline (Hv = 362), whereas brushing and staining lowered Hv in all TB groups (282.8-300.6). After brushing in W, VE, and RC were more susceptible to coffee stains than were CS and GB. The whitening dentifrice roughened CAD-CAM specimens, reducing gloss, yet lightened some materials. Polymer-infiltrated ceramic and direct resin composite specimens brushed with abrasive regular or whitening dentifrice resulted in more intense staining than the CAD-CAM resin composites.

Repair bond strength of a new self-adhesive composite resin to three different resin-matrix ceramic CAD-CAM materials.

This study aimed to evaluate the shear bond strength of two flowable composite resins to resin-matrix ceramic CAD-CAM materials.Fifty-four plates obtained from Lava Ultimate (LU), Cerasmart (CS), and Vita Enamic (VE) CAD-CAM blocks were assigned to nine groups: N0: Nova Compo SF (NCSF), N1: Silane/Single Bond Universal (SBU)/NCSF, N2: SBU/NCSF, N3: Silane/G-Premio Bond (GPB)/NCSF, N4: GPB/NCSF, G1: Silane/SBU/G-aenial Universal Injectable Composite (GUIC), G2: SBU/GUIC, G3: Silane/GPB/GUIC, G4: GPB/GUIC. After the repair procedures, shear bond strength values were analyzed. Silane pre-application decreased bond strength in most LU and CS groups but increased it in VE. NCSF performed better than GUIC in all CAD-CAM's with similar adhesive protocols. SBU in combination with NSCF had the highest bond strength among all repair procedures in LU and CS. Silane-containing universal adhesives in combination with self-adhesive resin composites should be used to repair resin-matrix ceramic materials.

Microhardness and Gloss of a New CAD/CAM Hybrid Material Following Accelerated Aging and Coffee Immersion.

To evaluate and compare the effect of accelerated aging and coffee immersion on the microhardness and gloss of a new computer-aided design and computer-aided manufacturing (CAD/CAM) hybrid material (Crystal Ultra) to those of contemporary restorative materials. A total of 160 specimens (12 × 14 × 1 mm ± 0.05 mm) were obtained from IPS e.max (IPS), VITA Enamic (VE), Crystal Ultra (CU), Lava Ultimate (LU), and CeraSmart (CS) high-translucency CAD/CAM blocks. The Vickers microhardness and gloss of the specimens were determined after thermocycling and coffee immersion. Data analysis was performed using SPSS (α = .05). IPS and CS specimens exhibited the highest (572.66 ± 11.30) and lowest (61.92 ± 3.91) microhardness, respectively. The highest gloss was observed with IPS specimens (3.31 ± 0.32), and LU specimens showed the lowest gloss (2.33 ± 0.06). A significant difference in gloss was observed between the materials at all measurement intervals (P < .01), except at T0 (P = .43). IPS specimens showed no significant changes in either group at any measurement interval. The microhardness and gloss of the new CU material were comparable to those of the tested contemporary hybrid restorative materials. Glass-ceramic showed superior hardness and gloss compared to hybrid restorative materials. Accelerated aging with thermocycling and staining significantly affected the microhardness and gloss of all tested CAD/CAM materials.

Translucency of CAD/CAM and 3D Printable Composite Materials for Permanent Dental Restorations

The aim of the study was to compare the translucency of CAD/CAM and printable composite materials for fixed dental prostheses (FDP). Eight A3 composite materials (7 CAD/CAM and 1 printable) for FPD were used to prepare a total of 150 specimens. CAD/CAM materials, all characterized by two different opacity levels, were: Tetric CAD (TEC) HT/MT; Shofu Block HC (SB) HT/LT; Cerasmart (CS) HT/LT; Brilliant Crios (BC) HT/LT; Grandio Bloc (GB) HT/LT; Lava Ultimate (LU) HT/LT, Katana Avencia (KAT) LT/OP. The printable system was Permanent Crown Resin. 1.0 mm-thick specimens were cut from commercial CAD/CAM blocks using a water-cooled diamond saw, or 3D printed. Measurements were performed using a benchtop spectrophotometer with an integrating sphere. Contrast Ratio (CR), Translucency Parameter (TP), and Translucency Parameter 00 (TP00) were calculated. One Way ANOVA followed by Tukey test for post hoc were performed for each of the translucency system. The tested materials exhibited a wide range of translucency values. CR ranged from 59 to 84, TP from 15.75 to 8.96, TP00 from 12.47 to 6.31. KAT(OP) and CS(HT) showed, respectively, the lowest and highest translucency for CR, TP and TP00. Due to the significant range of reported translucency values, clinicians should exercise caution when choosing the most appropriate material, especially considering factors such as substrate masking, and the necessary clinical thickness.

The Biological Activity of Fragmented Computer-Aided Design/Manufacturing Dental Materials before and after Exposure to Acidic Environment

Three ceramic and composite computer-aided design/computer-aided manufacturing (CAD/CAM) materials from different manufacturers (Cerasmart (CS)-nanoceramic resin; Straumann Nice (SN)-glass ceramic and Tetric CAD (TC)-composite resin) were tested to investigate the biocompatibility and sustainability on human fibroblasts and keratinocytes cells. Each type of CAD/CAM blocks restorative materials with fine and rough surfaces was exposed to an acidic environment for one month. After that, various powders were obtained by milling. In parallel, powders were also prepared from each restorative material, which were not exposed to the acidic environment. The cytotoxic effects were investigated by means of MTT and LDH assays, as well as nitric oxide production on two human normal cell lines, namely, fibroblasts (BJ) and keratinocytes (HaCaT). In addition, the degree of adhesion of fibroblast cells to each CAD/CAM material was evaluated by scanning electron microscopy (SEM). The results showed that the two samples that were exposed to an acidic environment (CS and SN) induced a reduction of mitochondrial activity and plasma membrane damage as regards the fibroblast cells. A similar effect was observed in TC_fine-exposed material, which seemed to induce necrosis at the tested concentration of 1 mg/mL. No oxidative stress was observed in fibroblasts and keratinocytes treated with the CAD/CAM materials. Regarding the adhesion degree, it was found that the fibroblasts adhere to all the occlusal veneers tested, with the mention that the CS and SN materials have a weaker adhesion with fewer cytoplasmic extensions than TC material. With all of this considered, the CAD/CAM restorative materials tested are biocompatible and represent support for the attachment and dispersion of cells.

Effect of Different Surface Treatments on the Surface Roughness and Gloss of Resin-Modified CAD/CAM Ceramics

The purpose of this in vitro study is to compare the roughness and gloss of four resin-modified CAD/CAM ceramics after different surface treatments. Forty-eight specimens (1.20 × 12 mm2) were prepared from Lava Ultimate (LU), Vita Enamic (VE), Cerasmart (CS), and Crystal Ultra (CU) CAD/CAM ceramics. The prepared specimens were polished with silicon carbide paper before being roughened with a 30 µm grit diamond bur. Each material was allocated into four groups: control (no treatment), Luster Meisinger polishing (MP), Optiglaze (OG), or Meisinger polishing, followed by a final polishing with Shofu Direct Dia Paste (MP+PP). The roughness and gloss were measured after the surface treatment using a profilometer and gloss meter, respectively. Scanning electron microscopy micrographs were obtained to analyze the surface characteristics. Statistical analysis was performed using a multivariate analysis of variance (MANOVA), one-way ANOVA, and Dunnett’s post hoc test (α = 0.05). The surface treatments significantly affected the surface roughness and gloss of the tested materials (p &lt; 0.05). All the tested resin-modified CAD/CAM ceramics demonstrated a lower surface roughness and higher gloss after glazing using OG, followed by MP+PP and MP. The highest and lowest Ra were presented by the control VE (0.63 ± 0.23 µm) and glazed LU specimens (0.04 ± 0.01 µm), respectively. The highest and lowest GU were presented by the glazed LU (90.48 ± 4.69 GU) and the control VE specimens (23.32 ± 2.41 GU), respectively. After clinical adjustment, finishing, and polishing, the restoration is essential to obtain a restorative surface with lower roughness and the highest gloss. Surface glazing using Optiglaze exhibited the smoothest and glossiest surface of all the tested resin-modified ceramics.

Influence of Acidic Environment on the Hardness, Surface Roughness and Wear Ability of CAD/CAM Resin-Matrix Ceramics.

This study aimed to measure the effect of storage environment on the hardness, surface roughness and wear ability of CAD/CAM resin-matrix ceramics. A total of 200 rectangular-shaped specimens were obtained by sectioning 5 CAD/CAM blocks; Crystal Ultra (CU), Vita Enamic (VE), Lava Ultimate (LU), Cerasmart (CS) and Vita blocks Mark II (MII). Microhardness and surface roughness were measured at baseline and after 7 days of immersion either in saliva or cola (n = 10). The wear ability of the CAD/CAM materials against steatite-ceramics antagonist was determined using a chewing simulator. The data were statistically analyzed using factorial ANOVA followed by post hoc Bonferroni multiple comparison tests (p < 0.05). The independent factors significantly influenced the microhardness and surface roughness (p < 0.05). The highest VHN was observed in MII at baseline (586.97 ± 13.95), while CU showed the lowest VHN after 7 days of immersion in cola (68.3 ± 1.89). On the contrary, the highest Ra was observed after 120,000 chewing cycles for the VE specimens (1.09 ± 0.43 µm) immersed in cola, while LU showed the lowest Ra at baseline (0.07 ± 0.01 µm). The highest % mass loss of the antagonist was observed with MII immersed in cola (1.801%), while CS demonstrated the lowest % mass loss of 0.004% and 0.007% in AS and cola, respectively. This study confirms that the surface properties of tested CAD/CAM materials are susceptible to degradation in an acidic environment except for hardness and wear of CS material.

Digital Volumetric Analysis of CAD/CAM Polymeric Materials after Tooth Brushing.

The objective of the study was to evaluate the volumetric wear of four composite materials for CAD/CAM (computer-aided design/computer-aided manufacturing) systems. The materials evaluated were: Cerasmart (CER), Shofu Block HC (SBH), Tetric CAD (TEC) and Brava (BRA). All the samples (n = 40) were subjected to simulated brushing (100,000 cycles). Wear was evaluated by superimposing pre-and post-brushing scans obtained with an intraoral optical scanner (CEREC Primescan; Dentsply Sirona, Germany), which were subsequently imported into the OraCheck software 5.0 (Dentsply Sirona, Germany). The data were analyzed by ANOVA test and Tukey’s HSD test was used for multiple comparisons. Cerasmart showed the least wear after brushing. All the tested materials exhibited mass loss.

Effects of background color and thickness on the optical properties of CAD-CAM resin-matrix ceramics

Statement of problemInformation regarding the masking ability of computer-aided design and computer-aided manufacture (CAD-CAM) resin-matrix ceramic materials with different compositions is scarce. PurposeThe purpose of this in vitro study was to evaluate the effects of background color and thickness on the optical properties (color and translucency) of CAD-CAM resin-matrix ceramics. Material and methodsTwelve rectangular specimens were fabricated at a different thickness (1, 1.5, and 2 mm) (n=12) from each of the resin-matrix ceramic materials: Shofu block (SB), Lava Ultimate (LU), CERASMART (CS), VITA ENAMIC (VE), Crystal Ultra (CU), and the VITABLOCS Mark II feldspathic ceramic (VB). The color of the specimens over amalgam, titanium, enamel, and dentin backgrounds was measured with a spectrophotometer, and the color differences (ΔE∗ab) were calculated by using the Commission Internationale de l’Eclairage (CIE) 76 formula. The difference in color of the specimen over the black and white backgrounds was used to calculate the translucency parameter (TP). ANOVA was used to statistically test whether material, background, and thicknesses influenced ΔE∗ab and TP values. Post hoc comparisons were performed to determine the significant difference among the groups (α=.05). ResultsThe interaction with 2 between factors demonstrated that the material was a factor that significantly influenced ΔE∗ab (P<.001). The highest mean ±standard deviation of ΔE∗ab was recorded in the combination of VB material and 2-mm thickness (1.84 ±0.37), and the lowest with CS material with 1.5-mm thickness (0.47 ±0.24). The type of material and specimen thickness significantly influenced TP (P<.001). The highest and lowest mean ±standard deviation of TP were recorded for the 1-mm-thick CS (14.20 ±0.90) and 2-mm-thick SB (4.91 ±0.42) specimens, respectively. ConclusionsCERASMART resin-matrix ceramic and VITABLOCS Mark II feldspathic ceramic exhibited high and low masking abilities over the investigated background substrates, respectively. However, irrespective of the thickness, all study materials exhibited acceptable masking abilities.

Is the radiopacity of CAD/CAM aesthetic materials sufficient?

ObjectivesThis study was designed to investigate CAD/CAM restorative blocks and other resin-based materials by (i) determining their chemical composition, (ii) comparing their radiopacity and (iii) correlating their radiopacity with specimen thickness. MethodsDisk specimens, of 1and 2 mm thickness (n = 3), were prepared from five CAD/CAM and six resin-based composites (RBCs). The CAD/CAM resin-composites included aesthetic types: CeraSmart (CS), Grandio Blocs (GB), Lava Ultimate (LU), plus a polymer infiltrated ceramic Vita Enamic (VE), and a feldspathic ceramic Vita Mark II (VM II). The six RBCs were for different clinical applications: direct filling, flowable, bulk fill, base and two luting cements. The specimens were radiographed alongside an aluminium step wedge and a tooth section. Digital images were analysed, and the radiopacity of each specimen was determined according to ISO 1311/2014. Statistical analyses of radiopacity, expressed as mm Al (n = 15), were carried out using the Kruskal-Wallis test followed by pairwise comparisons (α = 0.05). ResultsRadiopacities of CAD/CAM materials were, in ascending order, VE, VM II, CS, LU, and GB. At 1 mm thickness, the radiopacities of all CAD/CAM specimens were matching or slightly lower than enamel. At 2-mm thickness, the resin composite blocks were significantly more radiopaque than the ceramics VE and VM II (p < 0.0001). No statistically significant differences in radiopacity were detected between the 1-mm thick infiltrated ceramic, enamel, dentin and various resin composites except for filling and bulk fill types. The radiopacity of polymer-infiltrated ceramics was low despite the presence of radiopacifying elements and high filler content. SignificanceIdentifying thin restorations in standard radiographs is necessary with the development and expanded application of ‘digital’ dental materials in restorative treatment. This study confirmed the joint influence of composition and thickness on radiopacity. CAD/CAM restorative materials showed thickness-dependant radiopacity. But polymer-infiltrated ceramics were fairly radiolucent. There is a need to revisit radiopacity requirements for CAD/CAM restorative materials.

Quantitative nano-mechanical mapping AFM-based method for elastic modulus and surface roughness measurements of model polymer infiltrated ceramics

ObjectivesThe aim of this in vitro investigation was to assess and compare surface characteristics and nanomechanics of model polymer infiltrated ceramic network (PICN) materials compared to CAD/CAM resin composite blocks. Material and methodsFour model PICN materials sintered at different temperatures (Exp.125, Exp.130, Exp.135 and Exp.155) were investigated along with three CAD/CAM resin composites; Lava Ultimate (LU), Cerasmart (CS) and Grandio Bloc (GB), and one commercial PICN block - Vita Enamic (VE). Forty samples were prepared with dimensions of 14 × 12 × 2 mm for resin ceramic and VE blocks and 15 × 2 mm discs for model PICN materials. All samples were scanned using atomic force microscopy (AFM) (n = 3) at multiple locations and two different scan sizes (20 ×20 µm and 3 ×3 µm). Surface optical gloss (n = 5) at 60° was also determined for all the groups. Data were analysed using one-way ANOVA, and Tukey’s post hoc test (α = 0.05). ResultsResin composite blocks showed smoother surfaces compared to the PICN materials. The average surface roughness values (Ra) ranged from 7.75 nm to 31.21 nm and the gloss value ranged from 56.43 GU to 91.81 GU. The highest surface roughness value was found for Exp.125 (31.21 nm) while LU showed the lowest roughness value (7.75 nm) (the difference being statistically significant: p = 0.001). Variation was noticed in terms of nanomechanical mapping within and between the groups. Images generated from the elastic modulus map values clearly indicated that all PICN materials had more than one phase and very different components. ConclusionsCAD/CAM resin composite blocks exhibited higher gloss and lower roughness values compared to PICN materials. However, both the commercial and model PICN materials showed more stiffness than resin composite with the presence of at least two different phases. Sintering temperature appears to have a significant effect on material topography and nanomechanical properties. The model PICN sintered at 1550 °C showed a comparable range of elastic modulus values to those of enamel.

Repair Bond Strength of Composite Resin to Aged Resin and Glass-Matrix CAD/CAM Ceramic Materials Using Two Different Repair Systems

This study evaluates the repair bond strength of resin-matrix and glass-matrix CAD/CAM ceramic materials based on two repair systems. Thirty specimens measuring 2.5 mm in thickness were prepared from Crystal Ultra (CU), Vita Enamic (EN), Lava Ultimate (LU), Cerasmart (CS), and Vitablocs Mark II (VM2) materials and aged for 5000 thermal cycles. Specimens were randomly allocated into three groups: control, Monobond-S (MS) primer, and Monobond Etch &amp; Prime (MEP). Composite resin (Tetric N Ceram) (5 mm in diameter and 2 mm thick) was packed and light-cured onto treated specimen surfaces. Subsequently, the specimens’ shear bond strength (SBS) was evaluated, and failure modes was recorded. Statistical analysis was performed using factorial ANOVA and Tukey’s post hoc tests (a = 0.05). The factorial ANOVA revealed significant interactions between the material type and repair system, which was significant (p &lt; 0.01). The highest and lowest SBS were obtained for CU (27.09 ± 1.11) and VM2 (4.30 ± 0.59) in MS and control groups, respectively. In all the groups, CU demonstrated higher SBS, whereas VM2 demonstrated lower SBS. There were no significant differences in SBS between EN and LU, and CS and CU in all the study groups (p &gt; 0.05). The Monobond-S repair system provided non-significantly higher SBS compared to the MEP systems, except for VM2 and LU materials. The new resin-matrix CAD/CAM material demonstrated the highest SBS compared to the other materials for both conventional and MEP repair systems. Both repair systems showed clinically acceptable bond strength and allowed for successful repair of the resin-matrix ceramic materials.

Impact of the Microstructure of CAD/CAM Blocks on the Bonding Strength and the Bonded Interface.

To investigate the relationship between the microstructure of CAD/CAM blocks and the quality of adhesion as function of the surface treatment and resin cement type. Two nano-ceramic composite resin CAD/CAM blocks, Lava Ultimate (LU) and Cerasmart (CS), and two Leucite-reinforced glass ceramic CAD/CAM IPS blocks, Empress® CAD (EM) and InitialTM LRF (IR), received either Hydrofluoric acid (HF) or sandblasting (SB) surface treatments. The blocks were then luted using two dual-cure resin cements, LinkForce (LF) and Multilink Automix (ML) with their corresponding silanes, resulting in 16 study groups. The luted blocks were then thermal-cycling (TC) for 5000 cycles and subjected to a microtensile bond strength (μTBS) test. Scanning electron microscopy (SEM) micrographs of the treated surfaces were analyzed using ImageJ software and XRD analyses were performed for the two ceramic blocks. The data obtained were submitted to Games-Howell post-hoc nonparametric test to compare combinations of groups or treatments and a linear mixed-effects model for the factors surface treatment, block type, and resin cement, together with their first-degree interactions (α = 0.05). The lowest mean μTBS values were obtained with LU-HF, whereas the highest mean μTBS values were obtained with CS regardless of resin cement type and surface treatment method. IR-HF mean μTBS were significantly higher than IR-SB, EM-SB, and EM-HF. Analysis using ImageJ software demonstrated significant differences in the density and pore size after HF surface treatment. The specific microstructure of each block material within the same family group impacted the micromechanical retention and the bonded interface strength.

Effect of Staining and Aging on Translucency Parameter of CAD-CAM Materials.

ObjectivesTo evaluate different intervals of exposure to staining solutions and artificial aging on translucency parameter (TP00) of CAD-CAM materials.Material and MethodsOne millimeter thick square-shaped specimens (N = 288) were cut from Cerasmart (CS), IPS e.max (IE), Lava Ultimate (LU), Shofu HC (SH), Vita Enamic (VE), and Vita Suprinity (VS) and were divided into laboratory and chairside polishing. Reflection wavelength spectra, CIE D65 standard illuminant, 2 ° standard observer, SCI, UV included, SAV aperture, 6 mm diameter, were recorded at 10 nm sensitivity against white and black calibration tiles using a benchtop spectrophotometer. Subsequently, they were converted into CIEDE 2000 TP00. After baseline measurements (T0), the specimens were divided as follows (n = 8): staining in coffee (C) and wine (W), for 60 (T1) and 120 hours (T2), and accelerated artificial aging (A). Artificial aging (ISO 4892-2 standard) was performed in two cycles of 150 KJ/m2, for T1 and T2, respectively. TP measurements were repeated at T1 and T2. Data of TP00 retention were submitted to analysis of variance and Fisher’s PLSD multiple comparison test (α=0.05).ResultsFisher’s PLSD critical differences among materials, time intervals and staining/aging were 0.16, 0.11 and 0.11, respectively. SH showed the highest TP00 followed by LU > CS > IE = VS > VE. For all time intervals, the lowest TP00 retention was observed with C. W, and A presented similar values.ConclusionsTranslucency Parameter was a time and staining/aging-dependent material. In majority of cases, it decreased upon staining/aging.

Effect of cavity design and material type on fracture resistance and failure pattern of molars restored by computer-aided design/computer-aided manufacturing inlays/onlays

The maximum conservation of tooth structure and the use of restorative materials with elastic modulus close to the dental structure may promote greater longevity of the tooth/restoration complex. This study was conducted to evaluate the effect of cavity design and material type on fracture resistance and failure pattern of molars restored by computer-aided design/computer-aided manufacturing (CAD/CAM) inlays/onlays. In this in vitro study, 55 human maxillary molars were embedded in resin blocks and divided into control group (CG) and five main groups: Group 1: Inlay, Group 2: Conventional onlay/mesiobuccal (MB), Group 3: Conservative onlay/MB, Group 4: Conventional onlay/MB and distobuccal (DB), and Group 5: Conservative onlay/MB and DB. Then, each group was divided into two subgroups: (A) CeraSmart (CS) and (B) Katana Zirconia (KZ). Restorations were cemented by RelyX Ultimate and then thermocycled. The universal testing machine was used to measure fracture loads. Failure was determined using a magnifying lens. Data were statistically analyzed using ANOVA followed by Tukey's post hoc test (P < 0.05). Group 5 showed the highest significant fracture load, whereas the least significant value was recorded in Group 2. KZ recorded higher significant fracture loads than CS in all tested groups. Groups 1, 2, and 3 restored by CS showed lower fracture load than CG, but the difference was insignificant with Group 1. CS restorations showed restorable failure, while unrestorable pattern was predominant in KZ restorations (P < 0.05). KZ inlays and onlays can be used safely in terms of fracture resistance as both have values exceed the physiologic requirements. CS inlays and onlays/MB and DB are of fracture resistance comparable to intact teeth. The use of conservative onlay design with more cusp coverage guarantees better resistance of CS restorations. Being force absorbing material, the predominant failure of teeth restored by CS was restorable.

Fracture origin and crack propagation of CAD/CAM composite crowns by combining of in vitro and in silico approaches

PurposeFractographic analysis has been used to investigate the fracture behavior of Computer-aided design/computer-aided manufacturing (CAD/CAM) composite crowns by subjecting them to compression tests. However, it is difficult to investigate details of the fracture, including its initiation and propagation, using in vitro tests. The aim of this study was to determine the fracture origins and the order of crack initiation of CAD/CAM composite crowns using in silico nonlinear dynamic finite element analysis (FEA). Material and methodsThe following materials were used: Cerasmart (CS), Katana Avencia Block (KA), and Shofu Block HC (HC) as CAD/CAM crowns, Panavia SA Cement Plus (SA) as a luting material, and Clearfil DC Core Plus (DC) as an abutment. The elastic moduli and fracture strain of each material were obtained from the stress–strain curve of in vitro three-point bending tests. The fracture origins and order of crack initiation of the materials were determined by in silico nonlinear dynamic compression analysis. Load-displacement curves were statistically compared with the results of the in vitro compression tests (Pearson's correlation test, α = 0.05). ResultsThe nonlinear dynamic FEA demonstrated that crack initiation was primarily observed near the lingual side of the CAD/CAM crowns and immediately propagated to the central fossa. The models were fractured following the in vitro fracture strains, showing the same order for the products tested (CS/KA/HC, SA, and DC). Load-displacement curves with the use of CS, KA, and HC were significantly correlated to the corresponding in vitro compression tests results (CS: r = 0.985, p < 0.05, KA: r = 0.987, p < 0.05, and HC: r = 0.997, p < 0.05). ConclusionsThe in silico model established in this study clarified the crack initiation of the CAD/CAM composite crowns and the order of crack initiation among the investigated products, suggesting that the present approach is useful for analyzing the fracture behavior of CAD/CAM composite crowns in detail.

In Vitro Evaluation of Translucency and Color Stability of CAD/CAM Polymer-Infiltrated Ceramic Materials after Accelerated Aging.

To investigate and compare the translucency and color stability of a newly introduced polymer-infiltrated ceramic network (PICN) material (Crystal Ultra) to those of clinically well-established restorative materials. A total of 80 specimens measuring (12 × 14 × 1 mm ± 0.05 mm) were prepared from five CAD/CAM (IPS e.max (IPS), Lava Ultimate (LU), Cerasmart (CS), Vita Enamic (VE), Crystal Ultra (CU)) high translucency (HT) blocks in A2 or equivalent shades. Specimens were randomly allocated into two groups (A and B) (n = 8), and were subjected to 5,000 thermal-cycles (TC). This was followed by one-week immersion of group A specimens in coffee (staining) solution and group B specimens in distilled water. Following immersion, the specimens from both groups were further subjected to 5,000 TC. A spectrophotometer was used to measure the translucency parameter (TP) and color change (ΔE00 ) of the samples using CIELAB color coordinates at baseline, after 5,000 TC, following immersion, and after further 5,000 TC. Color stability was evaluated using the CIEDE2000 formula. Data were analyzed by non-parametric tests (α = 0.05). The TP values of the CAD/CAM materials ranged from 18.0-22.0. Following the initial TC, the changes in TP values were significant for VE (p = 0.012). Coffee immersion and further TC significantly impacted the TP values of PICN (VE and CU) materials compared to glass- ceramics (IPS), and resin nanoceramic (CS and LU) materials (p = 0.012). The comparison between CAD/CAM materials at different intervals showed a significant difference in the TP values (p < 0.01). The materials showed perceptible color changes following the initial TC except for PICN materials which demonstrated acceptable color changes. The major color difference was noticed for the resin nanoceramic specimens immersed in coffee; LU and CS showed higher color changes (ΔE00 = 2.45 and 2.09, respectively) than VE and CU (ΔE00 < 1.8). The translucency of the newly introduced Crystal Ultra PICN material was low compared to the resin nanoceramics and lithium disilicate glass-ceramic. The Crystal Ultra material exhibited better color stability compared to resin nanoceramics, but higher color change when compared with Vita Enamic PICN and lithium disilicate glass-ceramic CAD/CAM materials.

Effect of etching with low concentration hydrofluoric acid on the bond strength of CAD/CAM resin block.

The effect of etching for 90 s with low concentrations (0.5, 1.0, 2.0, 3.0, 3.5, and 4.0%) of hydrofluoric acid (HF) on the adhesiveness of computer-aided design/computer-aided manufacturing (CAD/CAM) resin blocks [CERASMART (CS), SHOFU BLOCK HC (HC), KATANA AVENCIA Block(KA), and VITA ENAMIC (EN)] was investigated. Energy dispersive spectroscopy revealed that the silicon content of HC, KA, and EN groups remained almost constant with HF etching of ≤4%. HF etching increased the surface roughness of all blocks. The HF concentration resulting in the highest shear bond strength in each group was as follows: CS (2.0%), HC (3.0%), KA (3.5%) and EN (0.5%). Scanning electron microscopy revealed that the bonding interface of etched surfaces differed significantly from that of airborne-particle abrasion surfaces. Thus, low concentration HF etching is effective for surface treatment of CAD/CAM resin blocks. The etching effect and optimum HF concentration differ with the block composition and structure.

Do resin-based composite CAD/CAM blocks release monomers?

The present study aimed to identify and quantify the elution of monomers of five different resin-based CAD/CAM blocks (RCBs) using HPLC. Five different RCBs were used in the study: GC Cerasmart (CS), Voco Grandio blocs (GR), 3M Lava Ultimate (LU), Shofu Block (SB), and Vita Enamic (VE). Fifteen samples from each material were prepared using a low-speed precision diamond saw (ISOMET Buehler, Lake Bluff, IL, USA) at 5 × 5 × 4mm size. After the preparation of samples, an extraction solution was mixed with %75/%25 ethanol/water. The samples were stored in the amber-colored bottles during three different immersed periods as 1h, 24h, and 90days (n = 5). After immersion, 0.5ml solutions were taken from each bottle and analyzed using HPLC. A total of 16.7μg/ml of monomers from SB, 13.4μg/ml of monomers from GR, 13.2μg/ml of monomers from CS, and 6.7μg/ml of monomers from LU were found after 3-m immersion. TEGDMA after 3-m of immersion was only released from the SB group, and also BisEMA was released from the CS group. Among the specimens immersed for 1h, UDMA was released the least from the LU group and the most from the GR group (p < 0.05). Correspondingly, 24h and 3m after immersion, the highest release of monomers was found in the GR (p < 0.05). When the monomer release from RCBs was evaluated, it was shown that these materials released methacrylate-based monomers except VE, especially if they were kept in a solvent solution for a long time such as 3m. The novel resin-based CAD/CAM blocks might monomer release, which may cause cytotoxic effects. But, the detected amount of monomer release is below the estimated daily limit.