Ash-based Geopolymer Research Articles

Novel electromagnetic induction heat curing process of fly ash geopolymer using waste iron powder as a conductive material

Geopolymer (GP) was invented to replace concrete, but its heat curing requirement hinders extensive use in real-world construction. Past studies have tested several methods of heat curing. However, the conventional heat curing process (using an oven) is still required for GP to develop good strength on the laboratory scale. This study introduces a new heat curing method for GP based on an electromagnetic field (EMF)generator and a ferromagnetic material. Waste iron powder (WIP) was used as the ferromagnetic material mixed with the fly ash-based GP to generate heat through induction. The sample was cured at 1.18 kW with 150–200 kHz of EMF generator for 15 min. The results showed that 5% of the WIP mixed sample gained compressive and flexural strength at 28 days more than the control (oven-cured). Compressive and flexural strengths of 76.8 MPa and 11.3 MPa were obtained, respectively. In addition, heat induction enhanced the densification and geopolymerization in the GP matrix following SEM and XRD results. This alternative method of heat curing accelerated the formation of the GP matrix, reduced curing time, and increased strength. Moreover, this EMF curing method can save 99.70% of the energy consumed compared to the conventional heat curing method.

Effect of Naoh Molar Concentration on Microstructure and Compressive Strength of Dolomite/Fly Ash-Based Geopolymers

Effect of Naoh Molar Concentration on Microstructure and Compressive Strength of Dolomite/Fly Ash-Based Geopolymers

Control of the setting reaction and strength development of slag-blended volcanic ash-based phosphate geopolymer with the addition of boric acid

This work aimed to evaluate the role of the addition of blast furnace slag for the formation of reaction products and the strength development of volcanic ash-based phosphate geopolymer. Volcanic ash was replaced by 4 and 6 wt% of ground granulated blast furnace slag to accelerate the reaction kinetics. Then, the influence of boric acid for controlling the setting and kinetics reactions was also evaluated. The results demonstrated that the competition between the dissolution of boric acid and volcanic ash-slag particles is the main process controlling the setting and kinetics reaction. The addition of slag has significantly accelerated the initial and final setting times, whereas the addition of boric acid was beneficial for delaying the setting times. Consequently, it also enhanced the flowability of the paste. The compressive strength increased significantly with the addition of slag, and the optimum replaced rate was 4 wt% which resulted in 28 d strength of 27 MPa. Beyond that percentage, the strength was reduced because of the flash setting of the binder which does not allow a subsequent dissolution of the particles and their precipitation. The binders formed with the addition of slag and/or boric acid are beneficial for the improvement of the water stability of the volcanic ash-based phosphate geopolymer.

Microstructure Stability and Thermal Resistance of Ash-Based Geopolymer with Sodium Silicate Solution at High Temperature

Current cement-based building materials have a huge disadvantage that they are easily broken due to thermal decomposition at high temperature (over 500°C) of structures of hydrated cement. This is easily observed at construction works when burned, the cement-based mortar and concrete materials and plaster are susceptible to collapse causing damage to buildings or structures. More seriously, these accidents easily cause injuries or loss of life for residents and people working there. Therefore, research on fire resistance and structural stability at high temperatures of building materials is always an interested topic of many scientists. This study utilized resources of highly active alumino silicate materials such as coal bottom ash and rice husk ash to produce geopolymer using sodium silicate solution as an alkaline activator. The ash-based geopolymer has good engineering properties responding to requirements of ASTM C55 and C90 for lightweight concrete brick. It is interesting to note that the geopolymer product was tested for thermal properties at 1000°C such as heat resistance, volumetric shrinkage, mass loss. The experimental results show that the ash-based geopolymer material has high thermal stability with increasing significantly of compressive strength after heated at 1000°C. Moreover, the geopolymer was also carried out to characterize microstructure before and after exposed at high temperature using methods of X-ray diffraction (XRD), scanning electron microscope (SEM). Thermal analysis methods such as thermogravimetric (TG), differential thermal analysis (DTA), and dilatometry-thermal expansion (CTE) were used to evaluate microstructural stability of the geopolymer-based materials.

Utilization of Industrial By-Products/Waste to Manufacture Geopolymer Cement/Concrete

There has been a significant movement in the past decades to develop alternative sustainable building material such as geopolymer cement/concrete to control CO2 emission. Industrial waste contains pozzolanic minerals that fulfil requirements to develop the sustainable material such as alumino-silicate based geopolymer. For example, industrial waste such as red mud, fly ash, GBFS/GGBS (granulated blast furnace slag/ground granulated blast furnace slag), rice husk ash (RHA), and bagasse ash consist of minerals that contribute to the manufacturing of geopolymer cement/concrete. A literature review was carried out to study the different industrial waste/by-products and their chemical composition, which is vital for producing geopolymer cement, and to discuss the mechanical properties of geopolymer cement/concrete manufactured using different industrial waste/by-products. The durability, financial benefits and sustainability aspects of geopolymer cement/concrete have been highlighted. As per the experimental results from the literature, the cited industrial waste has been successfully utilized for the synthesis of dry or wet geopolymers. The review revealed that that the use of fly ash, GBFS/GGBS and RHA in geopolymer concrete resulted high compressive strength (i.e., 50 MPa–70 MPa). For high strength (>70 MPa) achievement, most of the slag and ash-based geopolymer cement/concrete in synergy with nano processed waste have shown good mechanical properties and environmental resistant. The alkali-activated geopolymer slag, red mud and fly ash based geopolymer binders give a better durability performance compared with other industrial waste. Based on the sustainability indicators, most of the geopolymers developed using the industrial waste have a positive impact on the environment, society and economy.

Enhancing mortar strengths by ternary geopolymer binder of metakaolin, slag, and palm ash

PurposeThe purpose of this paper is to develop an alternative new ternary geopolymer mortar (MKSP) to resolve a traditional mortar problem which exhibits several disadvantages, including poor strengths and surface microcracks and the CO2 air pollution.Design/methodology/approachThe MKSP ternary binder was produced using metakaolin (MK), slag (S), and palm oil fuel ash (POFA) activated with an alkaline mixture of sodium silicate (Na2SiO3) and 10 M NaOH in a mass ratio of 2.5. Seven different mix proportions of MK, slag, and POFA were used to fabricate MKSP mortars. The water-to-binder ratio was varied between 0.4 and 0.5. The mortars were heat cured for 2 h at 80°C and then aged in air. Flexural stress and strain, mortars flow and compressive strength were tested. Furthermore, the mortars were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) analyses.FindingsThe results showed that the sample MKSP6, which contained 40 percent MK, 40 percent slag, and 20 percent POFA, exhibited high compressive strength (52 MPa) without any cracks and flexural strength (6.9 MPa) at 28 days after being cured for 2 h at 80°C; however, the MKSP7 mortar with optimal strength of 55 MPa showed some surface cracks . Further, the results of the XRD, SEM, and FTIR analyses indicated that the MKSP mortars primarily consisted of a crystalline (Si+Al) phase (70 percent) and a smaller amorphous (Si+Ca) phase (30 percent).Research limitations/implicationsThe MKSP ternary geopolymer mix has three limitations as an importance of heat curing for development early strength, POFA content less than 20 percent to gain high normal strength and delaying the sitting time by controlling the slag content or the alkali activator type.Practical implicationsThe use of geopolymer materials binder in a real building is limited and it still under research, Thus, the first model of real applied geopolymer cement in 2008 was the E-Crete model that formed by Zeobond company Australia to take the technology of geopolymer concrete to reality. Zeobond Pty Ltd was founded by Professor Jannie S.J. van (van Deventer et al., 2013), it was used to product precast concrete for the building structure. The second model was PYRAMENT model in 2002 by American cement manufacturer Lone Star Industries which was produced from the development carried out on inorganic alumino-silicate polymers called geopolymer (Palomo et al., 1999). In 2013 the third model was Queensland’s University GCI building with three suspended floors made from structural geopolymer concrete containing slag/fly ash-based geopolymer (Pathak, 2016). In Australia, 2014, the newly completed Brisbane West Wellcamp airport becomes the greenest airport in the world. Cement-free geopolymer concrete was used to save more than 6,600 tons of carbon emissions in the construction of the airport. Therefore, the next century will see cement companies developing alternative binders that are more environmentally friendly from a sustainable development point of view.Originality/valueProduction of new geopolymer binder of mortar as alternative to traditional cement binder with high early and normal strength from low cost waste materials, less potential of cracking, less energy consumption need and low carbon dioxide emission.

Influence of Foaming Agent/Water Ratio and Foam/Geopolymer Paste Ratio to the Properties of Fly Ash-based Lightweight Geopolymer for Brick Application

Nowadays, the demand for lightweight building materials has been growing worldwide. This paper presents an investigation on the use of waste materials of fly ash as a source materials for the production of lightweight geopolymer by using foaming agents. The key properties for the foamed geopolymer namely density, compressive strength, and water absorption were investigated. The chemical composition of materials and morphology analysis were studied to find the microstructure properties of foamed geopolymer. The foamed geopolymer were prepared by combination of 12 M Sodium Hydroxide (NaOH) solution and Sodium Silicate (Na2SiO3) solution. The ratio of Na2SiO3/NaOH and ratio of fly ash/alkaline activator were kept constant at 2.5 and 2.0, by mass respectively. The effect of different ratio of foaming agent/water and foam/geopolymer paste were investigated at 7 days of ageing and cured at 80�C for 24 hours. In general, the results showed that the fly ash-based lightweight geopolymer has good potential as brick application.

Recycling by-products from coal-fired power stations into different construction materials

The present investigation aims to analyse alternative uses of bottom ash and fly ash as part of con- struction materials for different applications: bottom ash- based ceramic bricks, pozzolanic material in the cement production, waste stabilisation/solidification of an electric arc furnace dust using ash-based geopolymers, and ash- based geopolymers used as hydraulic road binders. Dif- ferent replacements of natural materials by different fly and/or bottom ashes have been studied in all the cases. This study has analysed various parameters influencing the manufacturing process, with the aim of reducing the energy consumption of these processes, as they have been, for example, the firing temperature of bricks and grind size of bottom ashes in cements. All materials are manufactured in a simple and economical way, in order not to increase the cost of the products, and the final products have been evaluated according to different European standards used in these applications, in order to assess their possible, actual technical feasibility. The results obtained in this study show that even higher ratios of replacement ((40 %) of ashes have properties similar to those commonly used.