Abstract
High-temperature coating was deposited on the carbon-carbon composite material pre-coated with the ZrN barrier layer and NiCoCrAlY substrate. The barrier layer and substrate have been ion-plasma deposited, and the high-temperature coating was created by means of atmospheric-plasma spray under argon. The specimens possessed four compositions: 1 ― ZrO 2 + 8 % Y 2 O 3 , 2 ― (ZrO 2 + 8 % Y2O3) 20 % + MoSi 2 80 %, 3 ― (ZrO 2 + 8 % Y 2 O 3 ) 10 % + MoSi 2 90 %, 4 ― Al 2 O 3 + TiO 2 + modifying agent. The specimens were tested for heat resistance under the oxyacetylene flame torch at 2100 °C during 20 c. The specimen with the coating of composition 1 failed the test, the specimens with the coating of the compositions 2‒4 showed excellent results even after several test cycles. Ill. 9. Ref. 13. Tab. 1.
Highlights
Проведено осаждение жаростойких покрытий на углерод-углеродный композиционный материал с предварительно нанесенным барьерным слоем ZrN и подслоем NiCoCrAlY
В настоящее время уделяется большое внимание созданию защиты высоконагруженных деталей летательных и космических аппаратов, которые подвергаются нагреву и механическим нагрузкам в атмосфере при скорости полета более 5 Махов
Improved oxidation resistance for thermal barrier ceramic coating project / I
Summary
Для изучения образцов последовательно электронном микроскопе EOL JSM 7600F при ускоряющем напряжении 20 кВ, построение карт распределения элементов по поверхности также проводили в EOL JSM 7600F с использованием рентгеновского энергодисперсионного микроанализатора «Noran System SIX». Фазовый анализ был проведен при Cr Kα-излучении на рентгеновском дифрактометре «Дифей. 401», элементный анализ ― на рентгеновском аналитическом микрозонд-микроскопе PAM 30-μ
Sign-in/Register to view highlights & summary Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.