Abstract
C/SiC composites are raising great interest as a thermal shielding for aerospace applications, provided that they are protected from oxidation by suitable coatings. Conversely, ultra high temperature ceramics, and in particular ZrB2, is among the best oxidation resistant materials as known. A new type of oxidation protective coating (ZrB2/SiC coating) was produced on C/SiC composites. The composites were produced by precursor infiltration and pyrolysis (PIP), which is a simple and low cost method; the coating was ZrB2 mixed with SiC, which was fabricated by painting slurry on the surface of the composite followed by chemical vapor deposition (CVD) SiC on the top. Mechanical tests were conducted before and after oxidation test. Anti-ablation property was tested under oxy-acetylene torch. Oxidation test shows that the uncoated samples are oxidized quickly and the weight loss reaches 29.2% and the reservation of original flexural strength is only 6.74%, while the weight loss of ZrB2/SiC coated samples is only 5.19%, and the reservation of original flexural strength is 37.4%. ZrB2/SiC coating can provide longtime protection for C/SiC composites at 1973K. Compared with the uncoated composites, the linear and mass ablation rates of the coated composites decreased by 62.1% and 46.1%, respectively, after ablation for 30s. The formation of zirconia and silicon dioxide from the oxidation of ZrB2/SiC improved the ablation resistance of the composites, because of the evaporation at elevated temperature, which absorbed heat from the flame and reduced the erosive attack to carbon fibers and SiC matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.