Abstract
ZrB 2–Nb (ZN) composites were prepared through hot-pressing at a temperature of 1800 °C. A contribution of Nb was believed a significant influence on the sinterability, microstructure and mechanical properties of ZN composites. The values of flexural strength of ZN composites rang from 395 to 773 MPa, who are dependent on Nb contents. The highest strength obtained for the ZN composite containing 25 vol.% Nb (773 MPa). A fracture toughness of 7.1 MPa m 1/2 of ZN was revealed, which was much higher than that of monolithic ZrB 2. The improvement in fracture toughness strongly depended on an introduction of Nb–ZrB 2 matrix. Crack deflection and branching were believed to be the toughening mechanism of ZN.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.