Abstract
The microstructure of Mg-3wt%Nd-0.2wt%Zn-0.4wt%Zr (NZ30K) alloy after solution treatment was investigated and several kinds of interesting phases containing zirconium were found in this study. NZ30K was gravity cast using permanent die casting. After high tempering solution treatment at 540°C, cluster particles were observed inside the grains under optical microscopy. The detailed investigations were carried out on transmission electron microscopy (TEM). Four kinds of precipitates were visible inside grains with different shapes: block-like, globular, short rod-like, long rod-like. The block-like particle was identified as ZrH2 phase and the globular one was Zn2Zr3 phase. The other two were still Zr-containing phases, which could not be identified to any of existed compounds containing Zr. The formation of Zn-Zr compounds would probably be due to relative high ratio of Zr to Zn in the center of grains. ZrH2 would be the results of reaction of zirconium with H element during solution treatment, which probably came into the alloy during melting.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.