Abstract
Semiconductor alloy nanowires (NWs) have recently attracted considerable attention for applications in optoelectronic nanodevices because of many notable properties, including band gap tunability. Zinc phosphide (Zn3P2) and zinc arsenide (Zn3As2) belong to a unique pseudocubic tetragonal system, but their solid solution has rarely been studied. Here In this study, we synthesized composition-tuned Zn3(P1-xAsx)2 NWs with different crystal structures by controlling the growth conditions during chemical vapor deposition. A first type of synthesized NWs were single-crystalline and grew uniformly along the [110] direction (in a cubic unit cell) over the entire compositional range (0 ≤ x ≤ 1) explored. The use of an indium source enabled the growth of a second type of NWs, with remarkable cubic-hexagonal polytypic twinned superlattice and bicrystalline structures. The growth direction of the Zn3P2 and Zn3As2 NWs was also switched to [111] and [112], respectively. These structural changes are attributable to the Zn-depleted indium catalytic nanoparticles which favor the growth of hexagonal phases. The formation of a solid solution at all compositions allowed the continuous tuning of the band gap (1.0-1.5 eV). Photocurrent measurements were performed on individual NWs by fabricating photodetector devices; the single-crystalline NWs with [110] growth direction exhibit a higher photoconversion efficiency compared to the twinned crystalline NWs with [111] or [112] growth direction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.