Abstract
Lately, magnesium alloys have been extensively investigated through severe plastic deformation (SPD) methods in order to extend their application to structural components. In the present work, as-extruded ZK60 magnesium alloy samples were subjected to 4 passes of equal-channel angular pressing (ECAP) at a processing temperature of 250°C, following route Bc. The microstructural evolution of the deformed grains was analyzed using electron back-scattered diffraction (EBSD). The Orientation Imaging Microscopy (OIM) maps, together with the grain boundary misorientation distribution showed a reduction in the grain size accompanied by a large proportion of high angle grain boundaries. Calorimetric analysis showed a slight increase in the recrystallization temperature of the ECAPed magnesium samples. Mechanical tests showed an improvement in the elongation-to-failure after 4 ECAP passes, which were about 2 times higher than in the as-extruded sample. Also a brittle to ductile transition was observed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.