Abstract
Mullite-based ceramics added with 0–20 vol % stabilized zirconia have been prepared by alumina/zirconia particles coated with an amorphous silica layer. All samples can be densified through the viscous flow of the amorphous silica layer in the typical temperature range of 1100–1310 °C. For the ZrO2-free mullite ceramics, the viscous densification kinetics is inhibited by increasing the content of the alumina inclusion particles and by crystallization of the amorphous silica layer. However, for the zirconia-mullite ceramics, the addition of the zirconia inclusion particles accelerates the viscous densifcation kinetics. Mullitization kinetics is also enhanced by the addition of zirconia. As the sintering temeperature is high, a porous, duplex microstructure is observed in samples with or without zirconia. Zirconia addition enhances the development of this microstructure. As the sintering temperature and/or zirconia content is increased, ZrO2 particles tend to coarsen, resulting in a decreased tetragonal to monoclinic ratio. Fracture toughness KlC increases with the zirconia content. Mullite-20 vol % ZrO2 composite sintered at 1600 °C has a KlC of 3.8 MPa · m1/2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.