Abstract
The Young's modulus of hot-rolled Al alloy reinforced with Al2O3 particulates, (Al2O3)p-Al composite, is measured using the dynamic sonic resonance test method. The variation in the moduli of cold- and hot-rolled composites, as a function of the reduction ratio, is compared. Although both cold and hot rolling result in more uniform distribution of the particulates, hot rolling causes less damage to the reinforcements, resulting in more isotropic composites possessing a higher Young's modulus. These observed variations in the Young's modulus with respect to reduction ratio are analysed on the basis of the microstructural changes due to the rolling and T6 heat-treating operations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.