Abstract
Organic–inorganic composite microspheres with PS as a core and CeO2 as a shell were synthesized by in situ chemical precipitation method. The size of PS core was 117, 163, 206, and 241 nm, respectively, and the shell thickness was about 10 nm. The CeO2 shell was composed of a large number of nanoparticles, of which the size was 4–6 nm. Atomic force microscopy was employed to probe the mechanical properties of core–shell structured ceria-coated polystyrene (PS/CeO2) composite microspheres. On the basis of Hertz’s theory of contact mechanics, compressive moduli were measured by the analysis of force–displacement curves captured on the microsphere samples. For a fixed CeO2 shell thickness, the Young’s modulus of composite microspheres increased with an increase of PS core size. The calculated Young’s moduli (E) values of composites for 136, 185, 242, and 261 nm in diameter were 5.78 ± 0.9, 7.23 ± 1.3, 11.46 ± 1.7, and 14.54 ± 1.4 GPa, respectively. The results revealed the effect of the CeO2 shell on the elastic deformation of the PS core. This approach will provide fundamental insights into the actual role of organic/inorganic core/shell composite abrasives in chemical mechanical polishing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.