Abstract
We report the effect of the addition of BaTiO3 and WO3 nanoparticles on the pseudogap and excess conductivity of YBCO polycrystal. The excess conductivity analysis showed that the experimental data of pure and sample added with low amount of WO3 and BaTiO3 were perfectly described by the 2D Maki-Thompson (MT) and 3D Aslamazov-Larkin (AL) models. A sharp decrease in excess conductivity was obtained for samples added with high amount of nanoparticles where the analysis indicated the presence of the AL contribution and Lawrence-Doniach (LD) models. The pseudogap (PG) results showed that the value of Tpair (the temperature at which local pairs are transformed from strongly bound bosons into the fluctuating Cooper pairs) increased from around 117 K for the pure sample to around 187 K for sample co-added with low amount of nanoparticles. The pseudogap Δ*(TG) reduced from 230.9 K (for pure sample) to 223.4 K (for added sample).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.